• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.4
• /
• pp.738-746
• /
• 1988

Fatigue crack propagation of duplex stainless steel weldments was studied to develop further phenomenological understanding of the influences of welding heat cycle accompanying microstructural changes. Fatigue tests were carried out under constant amplitude of load in air at room temperature. The results showed that the crack propagation rate was different in base metal, heat affected zone and welding line. The crack propagation behavior in each part of duplex stainless steel was strongly dependent on phase ratio(.gamma../.alpha.) and several factors of microstructure also affected this propagation behavior. The fractographic feature in each part of steel were discussed on crack propagation behaviors.

• Journal of Welding and Joining
• /
• v.12 no.1
• /
• pp.28-37
• /
• 1994

본 소고에서는 Al-Zn-Mg 계통의 고강도 알루미늄합금의 제조과정에서 실시하는 열처리 공정을 통해 얻어지는 시효경화 효과, 합금원소 첨가에 따른 석출물의 생성과 이에 따른 석출경화 효과와 용착금속의 응고균열 발생과의 상호관계를 조사하고 용접열영향부의 용질원자 확산과 입계의 liquid film에 의한 액화(liquation) 균열의 생성을 분석하여 설명하고자 한다.

• Proceedings of the KWS Conference
• /
• 2001.10a
• /
• pp.140-142
• /
• 2001

항공기의 제트 엔진을 비롯하여 육상용 발전기, 선박용 엔진, 로켓 엔진 등에 널리 사용되는 터빈 블레이드를 포함한 고온용 가스터빈 부품은 최대 온도 120$0^{\circ}C$ 이상의 고온에 노출되어 가혹한 기계적 응력을 받는 동시에 고온에서의 표면 안정성이 요구되므로 초내열 니켈 합금(superalloy), 티타늄 합금, 내열강 등의 고온강도가 우수한 합금이 사용된다. 그런데 합금성분이 많이 첨가된 내열 합금을 용접하는 경우, 미세균열, 용접부의 기계적 성질의 저하, 용접열영향부의 내식성과 내산화성의 저하, 용접외부 결함에 의한 피로강도 저하 등의 문제가 발생하므로 이를 해결해야 한다. 본고에서는 생산성과 용접품질이 우수한 고밀도 에너지빔 용접의 적용 현황에 관하여 고찰코자 한다.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.42-42
• /
• 2009

마찰교반접합 (Friction Stir Welding)은 1991년 영국 TWI에서 개발된 접합 법으로서 회전하는 툴이 재료내부에 삽입되면 툴과 재료사이에서 발생하는 마찰열에 의하여 온도가 상승하게 되어 재료는 연화되고, 이러한 재료 내부에서 회전하는 툴이 이동하게 되면 재료 내부는 기계적 교반에 의해 소성변형이 일어남과 동시에 접합이 이루어진다. 마찰교반접합은 동적 재결정에 의한 접합부의 미세한 결정립 형성으로 인하여 기계적 특성이 향상되며 보호 가스가 필요 없어 친환경적임과 동시에 용융 용접 법에 비해 접합 시 에너지 소모가 적으며 또한 접합 후 접합부에서의 변형이 상대적으로 적다는 장점이 있다. 이러한 장점을 가진 마찰교반접합은 알루미늄 합금, 마그네슘 합금 그리고 동 합금과 같은 저 융점 비철재료에 많은 연구와 적용 사례들이 있어왔다. 하지만 최근에는 일반 탄소강, 연강, 오스테나이트계 스테인리스강, 니켈 합금, 티타늄 합금과 같은 고융점 재료에도 연구 및 적용이 진행되고 있는 추세이다. 페라이트계 스테인리스강은 가격이 비싼 Ni을 함유하지 않아 오스테나이트계 스테인리스강에 비하여 강재의 가격은 낮으면서도 고온특성 및 내식성이 우수하여 건축용, 자동차 배기계용으로 널리 사용되고 있다. 하지만 이런 장점을 가진 페라이트계 스테인리스강을 기존의 용융 용접 법으로 접합 시 용접부 및 열영향부에서의 결정립의 조대화로 인한 인성 및 연성이 저하되며, 특히 예민화된 열영향부 입계 내에 Cr 탄화물이 석출되어 입계주변에 Cr 결핍 층을 형성되어 입계부식이 발생되는 문제점이 발생된다. 본 연구에서는 마찰교반접합을 이용하여 두께 3mm의 409 스테인리스강에 대해 맞대기 접합을 실시하였다. 접합 변수를 툴의 재료 (WC-12wt%Co, $Si_3N_4$)로 하여 접합을 실시하였고 접합 후 외관상태 점검, 광학 현미경과 주사 전자 현미경을 통하여 미세조직을 관찰하였으며 황산-황산동 부식 시험을 실시하여 접합부의 부식 특성을 평가하였다.

• Proceedings of the KWS Conference
• /
• 2005.06a
• /
• pp.334-336
• /
• 2005

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.1
• /
• pp.30-41
• /
• 2006

This paper shows mechanical Properties and behaviors of macrostructures for specimens welded by F.S.W according to welding conditions and tool dimensions with $6.35mm_t$ aluminum 7075-T651 alloy plate. It apparently results in defect-free weld zone in case transition speed was changed to 15mm/min 61mm/min and 124mm/min under conditions of tool rotation speed such as 800rpm. 1250rpm and 1600rpm respectively with tool's Pin diameter 40mm and 60mm. The optimum mechanical property, ultimate stress,${\sigma}_Y=470Mpa$ is obtained at the condition of 124mm/min of travel speed with 800rpm of tool rotation speed using full screw type pin. shoulder dia. $20{\phi}mm$ pin dia. $6{\phi}mm$ and pin length 6mm. The full-screw type and the half-screw type pin shows the similar behaviors of weldability. It is found that the size of nugget is depended on tool transition speed and tool dimension by macrostructures of the cross section of weld zone.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2005.06a
• /
• pp.348-358
• /
• 2005

This paper showed mechanical properties and behaviors of macrostructures for specimens welded by F.S.W according to welding conditions and tool with 6.35$mm_t$ aluminum 7075-T651alloy plate. It resulted in defect-free weld zone in case tool rotation speed was 800rpm, 1250rpm and 1600rpm respectively that transition speed was changed to 15mm/min, 61mm/min and 124mm/min with tool's pin diameter 4${\Phi}$mm and 6${\Phi}$mm. The optimum mechanical property, ultimate stress,${\sigma}_Y$=470Mpa was obtained at the condition of 124mm/min of travel speed with 800rpm of tool rotation speed using full screw type pin, shoulder dia. 20${\Phi}$mm, pin dia.6${\Phi}$mm and pin length 6mm. The full-screw type and the half-screw type pin showed the similar behaviors of weldability. It is found that the size of nugget was depended on tool transition speed and tool dimension by macrostructures of the cross section of weld zone.

• Plant Journal
• /
• v.10 no.2
• /
• pp.48-59
• /
• 2014

Coupons which have same figure as weld joint of the forged steel valves and 1 inch nominal weld thickness were manufactured using ASTM A182 F92 material. After welding with GTAW method, the welded specimens have been post-weld heat treated at $705^{\circ}C$, $735^{\circ}C$, $750^{\circ}C$, $765^{\circ}C$, $795^{\circ}C$ and $825^{\circ}C$ for 1 hour per 1 inch nominal weld thickness each (Group 1) to evaluate characteristics of welds based on various holding temperature. Indeed, 3 welded specimens were post-weld heat treated for 30 minutes, 1 hour and 2 hour (Group 2) at $735^{\circ}C$ to evaluate characteristics of welds based on various holding time. Hardness values were measured at the weld metal, heat affected zone and base metal to observe hardness change depending on the condition. As a result of the evaluation, appropriate holding temperature for PWHT is proved as $750^{\circ}C$ and $765^{\circ}C$ for 1hour per 1 inch nominal weld thickness. Indeed, holding for 1 hour per 1 inch nominal weld thickness was insufficient for PWHT effect when the holding temperature was at $735^{\circ}C$. The microstructure of post-weld heat treated weld metal was determined as tempered-martensite structure.

• Journal of the Korean Society of Industry Convergence
• /
• v.6 no.1
• /
• pp.43-48
• /
• 2003

점용접은 자동차를 제작하는데 사용하는 가장 유용한 용접법이다. 그러나 산업현장에서 직면하고 있는 가장 큰 문제점 중의 하나는 점용접의 용접성에 관한 문제이다. 본 연구에서는 강판의 두께가 1.6mm인 경우와 1.2mm인 경우에 대해 2점 점용접을 실시하여 인장강도를 증가시키고 용접의 흔적을 남기지 않게 하기 위한 조건을 찾는 것을 목적으로 하였다. 용접성에 영향을 미치는 많은 요소들이 있다. 그중에서 용접전극의 형상이 인장강도를 증가시키는 요소로 집중을 하면서 연구를 수행하여 다음과 같은 결과를 얻었다. 인장강도는 용접전극의 형상 및 팁직경 거리와 전류가 클수록 증가하였다. 시행 착오법을 통해 최적용접조건을 찾았고 그에 따른 최적전류인 9,000A와 전극의 형상 RF형을 찾았다. 경도시험결과는 인장력이 시험편에 작용할 때 열 영향부인 HAZ부에서 왜 파괴가 일어나는지를 설명해 주었다.

• Journal of Welding and Joining
• /
• v.8 no.4
• /
• pp.27-34
• /
• 1990

Integranular corrosion behaviors of KAL (Knife Line Attack) and mechanical properties such as tensile and creep rupture were investigated for the tube material used for nearly 20 years under the condition of 463.deg. C and 28 $kg/cm^2$. Based and weld metal were austenitic stainless steel AISI 321 containing Ti, AISI 347 containing Nb, respectively. KLA is a kind of the intergranular corrosion which often occurs just near the HAZ (heat affected zone) of AISI 321 and AISI 347 stainless steel due to the grain boundary sensitization. In KLA zone, intergranular corrosion crack has propagated outwards from the inner surface and carbides of white and narrow band type assuming as (Cr, Fe) carbide were confirmed. All the delta-ferrite formed in the weld metal during weld solidification has been transformed into sigma-phase since delta-ferrte was exposed for 20 years at 463.deg. C. Elongation was very low at the range from room temperature to 600.deg. C and it was confirmed that creep-rupture properties were not consideralbly affected.