• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.12
• /
• pp.1317-1323
• /
• 2014

The aim of this paper is to investigate the effects of crack orientation on fatigue crack growth behavior in friction stir welded (FSWed) Al 7075-T651. Fatigue crack growth testing was conducted on compact tension (CT) specimens machined from the friction stir welds and the base metal under constant stress intensity factor range control. Tests were performed with the crack propagating nominally perpendicular to the weld line (termed the TL specimen) and the crack propagating in a parallel direction of the weld line (termed the LT specimen), and with three different constant stress intensity factor ranges. Both these specimen orientations were found to have a considerable effect on the fatigue crack growth behavior. Paris's law was adopted for the analysis of experimental results; the exponent m of the WM-LT specimen was determined to be 3.56, which was the largest value in this experimental conditions.

• Korean Journal of Materials Research
• /
• v.6 no.9
• /
• pp.905-918
• /
• 1996

초전도 마그네트 구조용 부재로 최근 개발된 오스테나이트계 스테인레스강 JN1 모재, GTA 용접부 및 열처리재에 대한 기계적 성질을 조사하기 위해 실온(293K)에서 극저온(4K)까지의 온도에서 소형펀치(Small Punch)시험을 실시하였다. GTA 용접부의 용융선 근방의 극저온 기계적 성질은 모재와 용접금속에 비해 크게 저하하였다. 4K에서 실험된 용융선 시험편으로 얻어진 하중-변위곡선상에서 부하의 초기 단계에 보통의 서레이션과 다른 pop-in이 관찰되었고, 이때 시험편 표면의 용융선 근처에서 약 0.1-1mm 정도의 크랙이 발생하였다. 열처리재의 기계적 성질은 열처리 시간과 온도의 증가 또는 시험온도의 저하에 따라 크게 저하되었다. 위의 결과에 기초하여 본 연구에서 실시한 소형 시험편을 사용하는 SP 시험법은 극저온에서 JN1 강의 모재와 열처리재뿐 만 아니라 GTA 용접부의 기계적 성질을 평가할 수 있는 유용한 시험법이었다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.4
• /
• pp.207-212
• /
• 2013

It is well known that fatigue failure occur on welded structures in industrial application due to the repetitive load force. In order to decrease the fatigue failure, we analysed the mechanical properties based on their structural aspect, roll steel (SS 400) welded onto stainless steels (STS 304) by $CO_2$ gas as well as structure roll steel welded onto itself. We compared the hardness, tensile and fatigue properties with two kinds of samples which had no defects on the welding part observed by X-ray topographic analysis. It was recognized that the tensile and fatigue strength of SS 400 welded onto itself by $CO_2$ gas was higher than that of SS 400 welded onto STS 304.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.23 no.1
• /
• pp.38-44
• /
• 2003

Performance demonstration with real flawed specimens has been strongly required for nondestructive evaluation of safety class components in nuclear power plant. Mechanical or thermal fatigue crack and intergranular stress corrosion cracking could be occured in the in-service nuclear power plant and mechanical fatigue crack was selected to study in this paper. Specimen was designed to produce mechanical fatigue flaw under tensile stress. The number of cycles and the level of stress were controlled to obtain the desired flaw roughness. After the accurate physical measurement of the flaw size and location, fracture surface was seal-welded in place to ensure the designed location and site. The remaining weld groove was then filled by using gas-tungsten are welding(GTAW) and flux-cored arc welding(FCAW). Results of radio graphic and ultrasonic testing showed that fatigue cracks were consistent with the designed size and location in the final specimens.

• Journal of Korean Society of Steel Construction
• /
• v.21 no.1
• /
• pp.55-62
• /
• 2009

Blast cleaning has been applied in steel bridges for cleaning forged surface and increasing adhesive property of applied coating systems. Blasting is the operation of cleaning or preparing a surface by forcible propelling a stream of abrasive metals against it. Blast cleaning may improve surface geometry and induce compressive residual stress, and eventually may increase fatigue life of weld joints. In this paper, fatigue tests were carried out on three types of non-load-carrying fillet welded cruciform joints, as-welded joints, blast-treated joints, and stress-relieved joints after blasting, in order to investigate effect of blast cleaning on fatigue behavior of the weld joints. By Blast cleaning, the weld toe radius was increased by 29% and compressive residual stress was induced near weld toes. Blast cleaning increased fatigue life and fatigue endurance limit of the weld joints. When the applied stress ranges decreased, the increment in fatigue life became larger. About a 150% increase in fatigue limit could be realized by using blast cleaning.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1997.05b
• /
• pp.17-22
• /
• 1997

ASME SA508 Class 3 원자로압력용기강을 대상으로, 용접열영향부(heat affected zone, HAZ)의 최고온도(peak temperature) 등온분포도(isothermal diagram)를 작성 및 해석하였고, 재현(simulated) 열영향부 시험편을 제작하여 미세조직검사 및 기계적특성 시험을 실시하였다. 그 결과, 최고온도 등온분포도를 이용하여, 미소열영향부(subzone of HAZ)의 미세조직(microstructure)에 미치는 예열(preheat)온도와 용접입열량(weld heat input)의 크기 효과를 예측할 수 있었다. 또한, 재현 HAZ 의 기계적특성 시험결과, 용접용융선(fusion line) + 1 mm 이내의 위치로 대표되는 열 cycle 조건에서는 모재보다 양호한 강도와 인성을 보였고, 용접용융선 + 2~3mm부근에서 가장 미세한 조직(fine tempered lower bainite)과 우수한 충격인성을 나타냈다. 한편, 용접용융선 + 약 5mm 위치에서의 열 cycle 을 재현한 시험편에서는 미세조직의 변화(spheroidization of carbides)와 함께 인성 및 기계적 특성이 저하하여 모재보다 낮은 값을 보이는 것을 발견할 수 있었다.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.6 no.3
• /
• pp.53-62
• /
• 1986

For the research on the fatigue fracture behavior in the welded joints of steel structures, base metal specimens and welded ones were selected, and the direct fatigue tests were carried out. Thereafter, fatigue-life (S-N) curves, plastic strain-number of cycles (${\varepsilon}_p$-N) curve, the extrapolated fatigue-life (${\varepsilon}_p$-$N_c$) curve, and da/dN-${\Delta}K$ curves were plotted. By these results the followings were obtained. It was shown that the ratio of fatigue strength at $2{\times}10^6$ cycles of the welded specimen to that of the base metal one was 0.6, and that 0.72 for the base metal and 0.65 for the welded one were the ratio of fatigue strength at $2{\times}10^6$ cycles to yielding stress. The S-N curve for the welded specimen was separated into two sections, the low gradient section and the steep section. As this result, it was shown that the more stress became to reduce, the more the reduction of fatigue strength became to be great. It was shown that fatigue strength at $2{\times}10^6$ cycles from this case was about 83 % of that from the S-N curve plotted with one section. It was thought that the reason was that weld flaw acted greatly on the fatigue strength within the low stress range. It was shown that at the instart of crack initiation plastic strain increased abrupt1y in the case of the welded specimen more than the case of the base metal specimen, and increased abruptly in the upper stress range in both cases. It was shown that the experimental constant ${\alpha}$, 0.42, in the base metal nearly accorded with Manson-Coffin's result, but this made a great difference with the case in the welded specimen. It was thought that it was due to the abrupt change of plastic strain and the influence of weld flaw.

• Proceedings of the KWS Conference
• /
• 1999.10a
• /
• pp.284-289
• /
• 1999

• Proceedings of the KWS Conference
• /
• 1992.04a
• /
• pp.85-89
• /
• 1992

• Journal of Power System Engineering
• /
• v.16 no.4
• /
• pp.66-73
• /
• 2012

본 연구는 횡방향 TIG 용접된 Al6013-T4 알루미늄 합금 용접부의 피로균열전파거동에 미치는 용접후열처리(PWHT)의 영향을 조사하는 것이 주목적이다. 기초적으로 인장시험, 경도 및 미세조직이 조사되었으며, 피로균열전파거동을 고찰하기 위한 피로 시험은 모두 중앙균열인장(CCT) 시험편에 대하여 수행되었다. T82열처리에 있어서 시효시간은 피로균열전파율, 인장강도 및 경도에 대단히 민감함을 나타내었으며, 모재와 열영향부재의 경우가 용접재보다 기계적 성질이 우수하였다. 횡방향 TIG 용접한 Al6013-T4 시험재의 용접후열처리 조건에 따라서 피로균열전파 저항에는 차이가 나타났으며, 본 실험의 조건하에서 24시간 인공시효 PWHT-82 시험편이 피로균열전파 저항이 가장 우수한 결과를 나타내었다.