• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.165-172
• /
• 2013

Power generating unit structures are designed and built to meet standard to secure its safety for expected life time. As the structures have been exposed to combined environment, degradation of structure material is accelerated and it can cause unexpected damage; evaluating precise mechanical properties of weak site like welded area is an essential research area as it is directly connected to safety issues. Existing measuring technique like tensile test requires specific size in testing specimen yet it is destructive method which is hard to apply on running structures. To overcome above mentioned limitation, IIT is getting limelight as it is non-destructive and simple method. In this study, latest technique is introduced to evaluate tensile property and residual stress by analyzing stress field occurs under the indenter while IIT is performed. Test on welded area, the weak site of nuclear structures have been practiced and confirmed that IIT can be usefully applied to evaluate integrity in industry.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.10 no.2
• /
• pp.105-115
• /
• 2012

Necessity of demonstration test to evaluate the structural integrity of a basket for accident conditions arose during license approval procedure for the WSPP's dry storage facility named MACSTOR/KN-400. A drop test facility for demonstration was constructed in KAERI site and demonstration tests for basket drop were conducted. As the upper welding region of a loaded basket was collided with a dropped basket during the drop test, the welding in this region was fractured and leakage happened after the drop test. The enhancement of basket design was needed since the existing basket design was not able to satisfy the performance requirement. The directions for design modification were determined and six enhanced designs were derived based on these directions. Structural analyses and specimen tests for each enhanced design were conducted. By evaluating structural analysis results and test results, one among six enhanced designs was decided as a final design for revision. The final design was the one to reduce the height of central post of a basket and to decrease the impact velocity with a dropped basket. Test basket models were fabricated with accordance with the final enhanced design. Additional demonstration test was performed for this test model and all the performance requirements were satisfied.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.7
• /
• pp.305-314
• /
• 2018

The steel-plate concrete composite beam is composed of a steel plate, concrete and a shear connector to combine the two inhomogeneous materials. In general, the steel plate is assembled by welding an existing composite beam. In this study, a new steel-plate concrete composite (SPCC) beam was developed to reduce the size of the shear connector and improve its workability. The SPCC beam was composed of folded steel plates and concrete, without any shear connector. The folded steel plate was assembled with high strength bolts instead of welding. To improve the workability in field construction, a hat-shaped cap was attached in the junction with the slab. Monotonic two-point load testing was conducted under displacement control mode. The flexural strength of the SPCC beam specimen was calculated to be 76% of that of the complete composite beam by using the plastic stress distribution method and strain compatibility method. The cap acted as the stud and accessory. The synthesis rate could be increased by controlling the gap of the cap, and the bending performance could be evaluated by using the strain fitting method considering the synthesis rate of the SPCC beam.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.79-79
• /
• 2010

저온용 무연 솔더의 대표 조성으로 고려되고 있는 Sn-58Bi(융점: $138^{\circ}C$) 공정(eutectic) 조성은 우수한 강도에도 불구하고 연성(ductility) 측면에서의 문제점이 지속적으로 보고되고 있다. 따라서 이 합금계의 연성을 최대로 개선시킬 수 있으면서도 실제 상용화가 가능한 합금 조성의 개발 연구가 요청된다. 본 연구에서는 Sn-Bi 2원계 조성에서 최대의 연성을 나타내는 것으로 보고된 Sn-40Bi 조성에 미량의 합금원소를 첨가함으로써 최대의 연성을 확보하는 한편, 그 연성 특성이 변형속도에 어느 정도 민감한지를 인장 실험을 통해 결정하고자 하였다. 합금원소로는 0.1~0.5 wt%의 Ag, Mn, In, Cu를 선택하였으며, 인장 시편을 제조하여 $10^{-2}$, $10^{-3}$, $10^{-4}\;s^{-1}$의 3종류로 변형속도를 변형시켜가며 응력-변형 곡선(stress-strain curve)을 측정하였고, 조성별, 변형속도별로 최대인장강도(ultimate tensile stress, UTS) 및 연신율 결과들을 정리하였다. 합금원소를 첨가한 조성의 경우는 모든 시험 조건에서 Sn-40Bi보다 우수한 연신률을 나타내는 것으로 측정되었으나, $10^{-2}\;s^{-1}$의 빠른 변형속도에서는 그 향상 정도가 상대적으로 감소하는 경향이 관찰되었다. 특히 Sn-40Bi-0.5Ag 조성의 경우 느린 변형속도에서 특히 눈에 띄는 연신률 값을 나타내며, 모든 변형속도 조건에서 가장 우수한 연성을 나타내었다. 한편 Sn-40Bi-0.1Cu 조성의 경우 변형속도에 따른 연신률의 변화 정도, 즉, 변형속도에 따른 연신률의 민감도가 매우 커 $10^{-4}\;s^{-1}$ 속도에서는 Sn-40Bi-0.5Ag에 버금가는 연신률 값이 측정되었으나, $10^{-2}\;s^{-1}$ 속도에서는 가장 나쁜 연신률 특성을 보여주었다. Sn-40Bi-0.2Mn 조성은 최고의 연신률 향상 특성을 나타내지는 않았으나, In을 첨가한 경우보다는 대체적으로 우수한 연성을 나타내었다. 이상의 각 합금별 연성 특성은 인장시험 전의 미세조직 관찰 결과와 인장시험 후 파면부의 조직변화 관찰 결과로부터 해석되었다. 그 결과 석출상의 형성 여부, 인장 시험 중 재결정 조직의 형성 여부, 라멜라(lamellar) 조직의 분율과 라멜라 간격(lamellar spacing)의 정도 또는 $\beta$-Sn과 라멜라 조직 사이의 결정립계와 라멜라 조직 내 결정립계에서의 슬라이딩 모드(sliding mode) 변형 정도, 석출상의 크기와 분포 정도 등이 연신률 및 변형속도 민감도와 같은 연성 특성에 가장 큰 영향을 미치는 인자인 것으로 분석되었다.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.80-80
• /
• 2010

전자제품의 소형화, 경량화, 고집적화가 심화됨에 따라 전자제품을 구성하는 회로의 미세화 또한 요구되고 있다. 이러한 요구는 경성회로기판 (rigid printed circuit board, RPCB) 뿐만 아니라 연성회로기판 (flexible printed circuit board, FPCB) 에도 적용되고 있으며 이에 대한 많은 연구 또한 이루어지고 있다. 연성회로기판은 일반적으로 절연층을 이루는 폴리이미드 (polyimide, PI)와 전도층을 이루는 구리로 이루어져 있다. 폴리이미드는 뛰어난 열적 화학적 안정성, 우수한 기계적 특성, 연속공정이 가능한 장점을 가지고 있으나, 고온다습한 환경하에서 높은 흡습성으로 인해 전도층을 이루는 구리와의 접합특성이 저하되는 단점 또한 가지고 있다. 또한 전도층을 이루는 구리는 고온다습한 환경하에서 산화 발생이 용이하기 때문에 접합특성의 감소를 야기할 수 있다. 따라서 본 연구에서는 고온다습한 조건하에서 sputtering and plating 공정을 통해 순수 Cr seed layer를 가지는 연성회로기판의 seed layer의 두께와 시효시간의 변화로 인해 발생하는 접합특성의 변화를 관찰하고 분석하였다. 본 연구에서는 두께 $25{\mu}m$의 일본 Kadena사(社)에서 제작된 폴리이미드 상에 sputtering 공정을 통해 순수 Cr으로 이루어진 각각 두께 100, 200, $300{\AA}$의 seed layer를 형성한 후 전해도금법을 이용, 두께 $8{\mu}m$의 구리 전도층을 형성한 시료를 사용하였다. 제작된 시료는 고온다습한 환경하에서의 접합 특성의 변화를 관찰하기 위하여 $85^{\circ}C$/85%RH 항온항습 조건하에서 각각 24, 72, 120, 168시간 동안 시효처리 한 후, Interconnections Packaging Circuitry (IPC) 규격에 의거하여 접합강도를 측정하였다. 시료의 전도층은 폭 3.2mm 길이 230mm의 패턴을 가지도록, 절연층은 폭 10mm, 길이 230mm으로 구성되었으며 이를 50.8mm/min의 박리 속도로 각 시편당 8회의 $90^{\circ}$ peel test를 실시하였다. 파면의 형상과 화학적 조성을 분석하기 위해 SEM (Scanning electron microscope)과 EDS (Energy-dispersive X-ray spectroscopy)를 사용하였으며, 파면의 조도 측정을 위해 AFM (Atomic force microscope)을 사용하였다. 또한 계면의 화학적 결합상태를 분석하기 위해 XPS (X-ray photoelectron spectroscopy)를 통해 파면을 관찰 분석하였다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.6
• /
• pp.126-136
• /
• 2018

A steel-plate concrete composite beam is composed of a steel plate, concrete and shear connector to combine inhomogeneous two materials. The steel plate is assembled by welding an existing composite beam. In this study, new steel-plate concrete composite beam, called a SPC Beam, was developed to reduce the shear connector and improve the workability. The SPC Beam was composed of folding steel plates and concrete, without a shear connector. The folding steel plate was assembled using high strength bolt instead of welding. To improve the workability in field construction, a hat-shaped Cap was attached to the junction with a slab. Monotonic load testing under two points was conducted under displacement control mode. The flexural strength of the specimen for positive moment and negative moment was calculated using the plastic stress distribution method. The test results showed that the flexural strength of the new SPC Beam had 80% of the strength of a complete composite beam. In addition, increasing the composite ratio was possible through clearance controls of the cap. In this study, the performance of the SPC Beam was verified through additional experiments and analyses with the cross-sectional shape and cap as variables, because the representative shape in the positive negative moment region is targeted.

• Journal of Korean Society of Steel Construction
• /
• v.16 no.6 s.73
• /
• pp.847-855
• /
• 2004

The criterion or specification on fatigue design has been generally based on fatigue strength curve derived by tests on specimens with varying thickness (10-30mm). Making the plate thicker, however, also decreases fatigue strength. It has been noted from the test results and the results of the analysis by fracture mechanics that the effect of thickness cannot be bypassed. From the several fatigue strength curves of specimen tests, modification of fatigue strength on plate thickness has been proposed. In this study, fatigue tests on SM520C-TMC were carried out, and the effects of thickness were evaluated. Finally, in consideration of the thickness, the modification of fatigue strength was derived. Comparing the results of this paper with those of previous studies, an outline of the behavior obtained is similar to previous ones, but the rate of decrease is smaller.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.373-380
• /
• 2000

It is useful to use NDE methods to assess the mechanical properties of materials since destructive methods are time-consuming and usually require cutting of sample from the material/component. In the present research, ultrasonic characteristics have been utilized to evaluate changes of mechanical properties due to heat treatment temperature and condition. The attenuation coefficient of ultrasonic wave increased as the heat treatment temperature because the grain size increased in size as the temperature. The attenuation coefficient decreased as the heat treatment has been progressed (quenched, tempered, PWHT). In the case of ultrasonic velocity measurement, velocity difference between quenched and tempered/PWHT was 40 m/s. There was a good relationship between the attenuation coefficient and the toughness. The relationship can be used for the nondestructive evaluation of the forged reactor vessels. Moreover, the method may be effectively used in the field application.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.110-110
• /
• 2018

여러 니켈합금 중 인코넬 600은 원전 가압경수로(PWR)의 튜브 재료로 널리 사용되는 재료이다. 스테인리스강과 비교하여 우수한 내식성과 기계적 특성으로 인해 화학설비, 발전설비, 그리고 해양설비 등과 같은 여러 산업분야에서도 널리 사용되고 있다. 그러나 가압경수로용 증기 발생기의 튜브 재료와 같은 특수 환경에서 예민화에 따른 입계부식 및 입계응력부식 등의 문제가 흔히 보고되고 있다. 이러한 내구성 문제는 설비 및 장비의 수명, 내구성 그리고 안정성 등의 치명적인 영향을 미친다. 따라서 용접, 열처리, 그리고 가공과정에서 발생하는 Inconel 600의 예민화 및 입계부식에 관한 연구가 활발히 진행되고 있다. 그러나 100시간 이상 장시간 열화된 시편에 대한 예민화 연구는 전무한 실정이다. 본 연구에서는 장시간 열화된 Inconel 600의 예민화를 평가하기 위해 최대 1,000시간까지 열화를 실시하였으며, 이에 대한 평가방법으로 Double-Loop Electrochemical Potentiokinetic Reactivation(DL-EPR) 시험법을 적용하였다. 본 실험에서 사용된 인코넬 600의 화학성분(wt, %)은 0.01 C, 0.05 Si, 0.14 Mn, 15.3 Cr, 0.5 Cu, 0.015 S, 그리고 나머지는 Ni 이다. 예민화 평가를 위한 등온 열화는 전기열처리로를 이용하여, $550^{\circ}C$와 $650^{\circ}C$에서 최대 1000시간까지 실시하였다. 열화에 따른 미세조직 변화는 scanning electron microscope와 energy dispersive x-ray spectroscopy를 이용하여 실시하였다. DL-EPR 실험은 $25^{\circ}C$의 0.1M $H_2SO_4$ + 0.001M KSCN(potasium thiocyanate) 수용액 하에서 실시하였으며, 분극은 OCP로부터 600 mV(SSE vs.)까지 1.67mV/s 주사속도로 forward scan을 실시 후, 동일한 속도로 OCP까지 reverse scan을 실시하였다. Degree Of Sensitization(DOS)값은 anodic scan peak($I_a$) 값과 reverse scan peak($I_r$) 값의 비로 산출하였다. $$i.e.\;DOS=I_r/I_a{\times}100$$. 그 결과, 온도 변수에 따른 Inconel 600강의 예민화 거동은 서로 상이한 경향을 나타내었다. $550^{\circ}C$의 경우, 열화가 진행됨에 따라 DOS값은 급격하게 증가하는 경향을 나타냈다. 반면, $650^{\circ}C$에서는 일정시간 이후부터 Cr 확산 현상에 의한 탈 예민화 현상이 관찰되었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2016.11a
• /
• pp.143-143
• /
• 2016

알루미늄 합금은 내구성과 내식성이 우수할 뿐만 아니라 다양한 표면개질을 통해 그 표면 특성을 더욱 향상시킬 수 있다. 특히 Al-Mg계 5083-H321 Al 합금의 경우 가공성 및 용접성이 우수하여 선체 재료로 널리 이용되는데, 이는 선체중량의 경량화가 가능하여 연료비 절감과 빠른 선속 등 다양한 이점을 지니기 때문이다. 그러나 선속의 고속화에 따라 선체에 가해지는 유체충격이 증가하고 정압 저하에 기인하여 캐비테이션-침식 손상이 증가할 뿐만 아니라 해수환경 특성 상염소이온의 존재로 부식이 가속화되는 등 침식 및 부식의 시너지효과로 손상은 크게 증가한다. 이에 대한 방지대책으로 다양한 표면개질 기법이 제안되고 있으나 강한 충격압이 동반된 캐비테이션 침식-부식 복합 손상 환경에서는 표면처리만으로는 불가능할 수 있다. 따라서 본 연구에서는 양극산화된 5083-H321을 대상으로 캐비테이션 환경 하에서 일정 전위를 인가하여 침식-부식 손상이 최소화되는 최적전위를 규명하고자 한다. 이를 위해 먼저 분극 실험을 통해 재료의 전기화학적 거동을 바탕으로 임의의 전위를 선정하고 해당 전위를 인가한 상태에서 캐비테이션 실험을 실시하였다. 이때 분극실험과 캐비테이션-전기화학 복합실험 모두 $25^{\circ}C$의 해수에서 실시하였으며, 전기화학적 분극실험은 유효면적이 $3.24cm^2$인 시편에 2 mV/s의 분극속도로 0 ~ -3 V 까지 인가하였고, Ag/AgCl 기준전극과 백금대극을 사용하였다. 캐비테이션-전기화학 복합 실험은 정전위를 인가한 상태에서 $30{\mu}m$의 진폭으로 20분간 실시하였으며, 혼팁과 시험편 사이의 거리는 1 mm로 일정하게 유지하였다. 실험 후 표면 손상의 정량적 분석을 위해 인가된 전위별 전류밀도를 비교하고, 무게감소량을 측정하였으며, 손상특성 분석을 위해 3D현미경과 주사전자현미경(SEM)을 통해 표면을 분석하였다.