• Journal of the Korean Applied Science and Technology
• /
• v.29 no.2
• /
• pp.295-301
• /
• 2012

The collagen-liposomes were prepared with hydrogenated phosphatidylcholine and by solvent injection method for maximum protection and stable absorption of collagen into the body. Cholesterol was added to phosphatidylcholine to increase the stability of liposome membrane. The mixture was dissolved in ethanol and propylene glycol and PBS Buffer was used to Stabilize ions. The properties collagen-liposome were analyzed by DLS, SEM and POM.

• Composites Research
• /
• v.17 no.4
• /
• pp.47-52
• /
• 2004

This paper established the procedure to fabricate the MWNT/PMMA nanocomposite by using together with injection molding and film casting processes. The fabrication process made it possible for MWNTs to be well dispersed in the PMMA matrix and also it could maintain the well-dispersed state effectively. And the mechanical material properties and SEM images of the fractural surface were observed. Moreover, a surfactant was used to disperse MWNTs more effectively and mechanical material properties were also investigated.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.22 no.3
• /
• pp.328-333
• /
• 1993

The effect of defatted and dehydrated beef muscle on the physical properties of thermoplastically extruded defatted soybean, cottonseed, peanut and sunflower seed flours were investigated. To minimize the adverse effect of meat fat and to increase the mixing efficiency of the meat with defatted oilseed flours at a given moisture level, beef muscle was extracted with chloroform-ethanol(2 : 1) at 2$0^{\circ}C$ and air dried. The variety of oilseed flours used had greater effects on color, expansion, bulk density, water absorption rate and textural strength of the extrudate than did the added level of defatted, dehydrated beef muscle (0 to 20% on a dry weight basis).

• Journal of the Korean Magnetics Society
• /
• v.10 no.6
• /
• pp.291-296
• /
• 2000

The manufacturing method of permalloy soft magnet with the Ni contents of 46.6 and 47.2 wt% was investigated by powder injection molding technology. The magnetic properties of permalloy were greatly affected on the residual carbon and oxygen content of the sintered magnet. Solvent extraction and thermal debinding process to minimize the residual carbon content in sintered magnet were developed by controlling the debinding atmosphere. The residual carbon content depends on the debinding condition of the binder system for powder injection molding and the residual oxygen content on the sintering atmosphere. The sintered magnet produced by powder injection molding process had a 50 ppm. residual carbon, 150 ppm. residual oxygen. The coercivity and maximum relative permeability of permalloy soft magnet were 0.46 Oe and 14,600 respectively.

• Journal of the Korean Ceramic Society
• /
• v.39 no.5
• /
• pp.467-472
• /
• 2002

Long Carbon Nanotubes(CNTs) were cut by diamond lapping film followed by observation using SEM. The paste was prepared by mixing shortened CNT powder, ${\alpha}$-terpineol used as a solvent, and ethylcellulose as a binder. This paste was deposited on glass substrate by screen printing and extruded by syringe. After screen printing, several post-treatments were performed to control the alignment of CNTs perpendicular to the substrate. The deposited CNTs were scratched by sand paper or diamond lapping film. It was also treated by attachment followed by an immediate detachment using the adhesive tape. SEM observation indicates that excellent vertical alignment of CNTs could be achieved by simple post-treatments from the screen printed-CNTs paste. Similar alignment of CNTs is also observed in the as-extruded CNTs paste.