• Composites Research
• /
• v.31 no.6
• /
• pp.323-331
• /
• 2018

The effect of stainless steel jagged-pin reinforcement on the pull-off strength of the composite hat-joint was studied by the test. The pins were physically and chemically surface-treated and inserted in the thickness direction over the interface where the skin and stiffener meet. The specimens including the jagged-pins were made by co-curing process. Diameters of the jagged-pins were 0.3, 0.5 and 0.7 mm. The pin areal densities were set to 0.5 and 2.0% based on the interface area where the skin and stiffener meet. The specimens using 0.3 mm diameter normal (un-jagged) pins with 2.0% areal density were additionally fabricated and tested to investigate the pin shape effect on the pull-off strength. The pull-off strengths of specimens reinforced with 0.5% areal density by 0.3, 0.5, and 0.7 mm diameter pins were 45, 19 and 9% higher than those of un-reinforced specimens, respectively. In case with 2.0% pin areal density, the strengths were 127, 45, and 11% higher than those of un-reinforced specimens, respectively. The test results show that the higher pin areal density results in the higher strength when the pin diameter is the same. When the pin areal density is the same, the smaller pin diameter leads to higher strength. When the joints using jagged-pins and normal pins in 2.0% areal density with 0.3 mm diameter, the joints of jagged-pins showed the 64% higher strength. From the results of this study, it was confirmed that jagged-pin reinforcement can be an effective method for improving the pull-off strength of composite hat-joint.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.41 no.12
• /
• pp.967-974
• /
• 2013

Recently the authors had proposed the z-pinning patch concept to simply manufacture z-pinned composite structures at industrial production site and manufactured composite single-lap shear joint specimens using the concept. Through static tensile test on the specimens they had obtained 54~68% improvement of the joint strength. As a sequential study of it, in this study, fatigue test has performed to measure an improvement of joint strength under cyclic loading. The z-pin's material is stainless steel and its surface was specially machined into zagged shapes and chemically corroded to increase the connection force with composite materials. Approximately 98~125% improvement of the joint strength under cyclic loading was obtained.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.41 no.8
• /
• pp.613-618
• /
• 2013

In this paper a new concept on z-pinning technology named by authors as 'z-pinning patch' will be introduced, which advantage is easy application at manufacturing site of composite structures. Using the trial manufactured z-pinning patch, the z-pinned composite single-lap shear joint specimens were successfully manufactured and tested to check the improvement of joint strengths. The z-pin's material is stainless steel and its surface was machined as zagged shape and chemically corroded to improve joint force with composite materials.

• Tunnel and Underground Space
• /
• v.13 no.5
• /
• pp.362-372
• /
• 2003

Since the occurrence of Portland cement, a great number of concrete structures were constructed. But the concrete structures have their own life times, which inevitably demand repairing treatments, especially on their surface parts. Currently many various methods have been developed and are being applied fer this purpose. In this study, a newly developed method using pneumatic chipping machine and anchor pin was adopted far repair of old concrete structure and the mechanical characteristics of cementing plane between existing and new concrete were tested. Comparing the removal methods for the decrepit part of existing concrete using pneumatic chipping machine and hydraulic breaker, the peak cohesion was higher when using chipping machine at the cementing plane. On the other hand, the residual cohesion was higher for the case of breaker. Step shaped chipping on the cementing plane was effective in increasing peak cohesion, which results 14% increase in the case of 30 mm step height and 22% in 50 mm height when compared with planar chipping plane. The use of anchor pin increased the residual cohesion, which restricted shear slip on the cementing plane after peak shear stress and the tensile strength of 32% compared with that of non-anchored case. According to the combined effect of step shaped chipping of 30 mm and anchor pin with an interval of 15 cm, the peak cohesion reached up to 77% and the residual cohesion showed 180% of the ones of the fresh concrete, respectively.

• Tribology and Lubricants
• /
• v.24 no.5
• /
• pp.234-240
• /
• 2008

It is well known that surface texturing improves the tribological properties of mechanical components for enhancing hydro-dynamic effect or serving as a micro reservoir. There are not, however, enough researches to reveal the effects of surface texturing on the tribological properties under grease lubrication which is used in lubricating many mechanical elements. In the present study, therefore, the effects of surface texturing on the tribological properties are investigated under grease lubrication based on an experimental approach. The results show that surface texturing decreases friction coefficient. It is found that the friction coefficient can be decreased by controlling the diameter and density of micro-dimple. The diameter of dimple is more effective under high load and low speed than otherwise. And, the density of dimple is effective under low load and high speed.