AZ31 마그네슘합금의 온간디프드로잉시 판재성형특성 (Formability of AZ31 magnesium sheet alloy of warm deep drawing)

  • 이명섭;강대민
    • 한국소성가공학회:학술대회논문집
    • /
    • 한국소성가공학회 2005년도 추계학술대회 논문집
    • /
    • pp.377-380
    • /
    • 2005
  • In this study, the experiments of warm deep drawing were done with heated die, and with heated die and cooled punch in order to investigate the formability of ZA31 magnesium sheet alloy of warm deep drawing. For this, warm deep drawing experiments were executed under various temperature, punch velocity and blankholder force. The results of warm deep drawing with heated die showed that fracture occurred punch part at punch velocity of 75mm/min and punch stroke of 10mm under temperature of $100^{\circ}C\~250^{\circ}C$, but did not occure under temperature of $275^{\circ}C\~400^{\circ}C$. And fracture at punch stroke of 25mm did not occurre at punch part under punch velocity of 30mm/min and $250^{\circ}C$, but occured under punch velocity of 75 and 125 mm/min. Also the results of warm deep drawing with heated die and cooled punch showed that the temperature happening maximum height under punch velocity of 10-100mm/min was $225-250^{\circ}C$. And necking occurred at punch shoulder under $20\~150^{\circ}C$, but at die wall under $200\~300^{\circ}C$.

  • PDF

AZ3l 마그네슘합금의 온간디프드로잉시 판재성형성 향상 (Improvement of Formability of AZ31 Magnesium Alloy Sheet during Warm Deep Drawing)

  • 이명섭;강대민
    • 소성∙가공
    • /
    • 제15권2호
    • /
    • pp.148-152
    • /
    • 2006
  • In this study, the experiments of warm deep drawing were done with heated die, and with heated die, and blankholder, and cooled punch in order to investigate the formability of AZ31 magnesium alloy sheet in warm deep drawing. For this, warm deep drawing experiments were executed under various temperatures and punch velocities. The results of warm deep drawing with heated die showed that fracture occurred around the punch part at punch velocity of 75mm/min and punch stroke of 10mm under temperature range of 373-523K, but did not occur under temperature range of 548-673K even punch stroke of 25mm. And fracture at the punch stroke of 25mm and the temperature of 523K did not occur under the punch velocity of 30mm/min, but occurred under punch velocity of 75 and 125mm/min. Also warm deep drawing with heated die and blankholder, and cooled punch showed that the temperature range happening maximum height under punch velocity of 10-100mm/min was around 498-523K. Finally, with heating and cooling technique necking of AZ31 magnesium alloy occurred at punch shoulder part under the temperature range of 293-423K, but at die wall part under the temperature range of 473-573K.