• Journal of the Korea Concrete Institute
• /
• v.14 no.6
• /
• pp.883-891
• /
• 2002

The chloride penetration in concrete structures is influenced by many factors such as types of cement and admixture proportion. Therefore, the effects of these factors on chloride diffusion must be correctly considered. The conventional diffusion analysis also neglected the existence of reinforcing bar in concrete structures. The purpose of the present paper is therefore to investigate the effect of reinforcing bar on the chloride diffusion in concrete structures. For this purpose, a comprehensive finite element analyses have been conducted to obtain chloride penetration profile. The results indicate that the chlorides are accumulated in front of a reinforcing bar and that the accumulation is much larger for the case of large diameter bars. The higher accumulation of chloride at bar location causes much faster corrosion of reinforcing steel. It can be concluded from the present study that the effects of reinforcing bars must be considered in chloride diffusion analysis for more realistic prediction of durable life of concrete structures.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.28 no.5A
• /
• pp.709-718
• /
• 2008

Developed is a chloride penetration analysis program in which changes of environmental conditions such as temperature, humidity and external chloride concentration, and the diffusion, convection and binding of chlorides are considered. In order to consider the changes of environmental conditions, analyses for temperature and moisture distribution are implemented simultaneously, and variation of diffusion coefficients due to temperature, humidity and age is also considered. By comparing the calculated total chloride contents with some experimental data, it has been confirmed that the proposed analysis program can trace measured chloride distribution well. Also, through some example analyses, the mechanism of accumulation of chlorides at near surface and acceleration of corrosion of steel reinforcement in case that the moisture distribution changes according to repeated drying and wetting cycles have been verified.

• Journal of the Korea Concrete Institute
• /
• v.15 no.1
• /
• pp.25-34
• /
• 2003

The degradation of reinforced concrete (RC) structures due to physical and chemical attacks has been a major issue in construction engineering. Deterioration of RC structures by chloride attack followed by reinforcement corrosion is one of the serious problems. An objective of this study is to develop a form of mathematical model of chloride ingress into concrete. In order to overcome some limits of the previous approaches, a chloride ingress model, consisting of chloride solution intrusion through the capillary pore and chloride ion diffusion through the pore water, was proposed. Moreover, the variability of chloride ion diffusivity due to the degree of hydration of cement, relative humidity in pore, exposure condition, and variation of chloride binding, was considered in the model. In order to verify the proposed model, the results predicted by the proposed model were compared with analysis results of Life-365, a computer program for predicting the service life of reinforced concrete structures exposed to chlorides. In conclusion, the proposed model would be promising to predict the chloride ion profile and to estimate the service life of RC structures.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.4
• /
• pp.600-608
• /
• 2022

This study investigates the effect of layered double hydroxide (LDH) on the healing performance of self-healing concrete by assessing the chloride penetration resistance of self-healing cement mortars using electrical chloride ion migration-diffusion test. Test results show that both mortars containing healing materials only and mortars containing healing materials and Ca-Al LDH together mostly had higher migration-diffusion coefficients right after cracking, but the migration-diffusion coefficients decreased more than that of OPC with increasing healing ages, and thus, they yielded higher healing capacities than OPC. Also, mortars containing Ca-Al LDH together with healing materials showed higher reduction of their migration-diffusion coefficients, and thus, higher healing capacities than mortars containing healing materials only. This suggests that as the self-healing product increases on the crack surface, the binding of chloride ions by LDH inside the crack increases.