고온고압장치(High Temperature and Pressure Vessels)의 적용을 위한 기초연구로서 9Cr-1Mo강 용접부의 연화특성에 대하여 검토하였다. 9Cr-1Mo 강재에 Bead-on-Plate용접을 실시한 후, 용접부의 기계적 성질과 그 현미경조직관찰 및 미세경도를 측정한 결과, As-Welded 및 용접 후열처리(PWHT)등의 조건에 관계없이 용접열향부의 변태역과 템퍼링역의 경계에서 모재의 경 도보다 낮은 경도값(연화역)을 나타내었으며 이러한 원인은 결정립계(Grain boundary)에 석출 되는 탄화물의 형성에 의한 뜨임 현상임이 판명되었다.
Weld repair of ASTM A-470 class 8 high pressure (HP) steam turbine rotor steel has been performed to extend the service life of older fossil units. Microhardness measurements were conducted across the weldment from unaffected base metal (BM) to weld metal (WM). The hardness of the BM was VHN 253, however it dropped up to VHN 227 at the heat affected zone (HAZ) close to unaffected BM for multipass SAW. This area of hardness drop is called "siftening zone" and has a width of 0.5-0.6mm. During creep rupture test, failure occurred around the softening zone and rupture time was 772.4hr at 19Ksi (132 Mpa) and 593.deg. C. Multipass MIG and TIG welding have been employed to reduce the softening zone width. The softening zone width for MIG was 0.3-0.4mm and for TIG was zero-0.4mm depending on heat inputs. However creep rupture time was decreased as softening zone width reduced. Creep rupture time also showed a close relationship with heat inputs in TIG process. The higher heat input, the longer rupture time. Most failure occurred at intercritical HAZ (ICHAZ), however rupture location was shifted to coarse grained HAZ (CGHAZ) as heat input decreased. The rupture surface showed tearing and dimple which indicated transgranular fracture. fracture.
In this paper, ultimate compressive strength of TMCP 50HT steel plates (yield stress .sigma.$_{o}$=36kg/mm$^{2}$) with HAZ softening is studied. Finite element method formulated by the author is applied to analyze the elasto-plastic large deflection behaviour of the plates. The influence of HAZ softening breadth, welding direction and slenderness ratio on the ultimate compressive strength is investigated. The results obtained are summarized as 1) With the increasing of the HAZ softening breadth, early plasticity on the plates is formed and then the ultimate compressive strength is decreased, in which about 8% of the ultimate strength for the plate with h/t=4(h: HAZ softening breadth, t: plate thickness) was reduced comparing with no HAZ softening. 2) The large decrease of the ultimate strength for the case that the welding direction is normal to the loading direction is occurred than the case that the welding direction is parallel to the loading direction. 3) The influence of HAZ softening on the ultimate compressive strength is serious for thick plates, while it may be negligible for thin plates.s.
Weldability of the TMCP steel manufactured by controlled rolling followed by accelerated cooling process was investigated. For comparison, two other steel plates produced by different manufacturing processes were selected; normalized and controlled rolled. Tandem submerged arc welding with both side one run technique was carried out. The results of this study can be summarized as follows; TMCP steel having the lowest carbon equivalent shows the best combination of mechanical properties, not only in the base metal but also in the heat affected zone. In the HAZ, the accelerated colling effect imarted on the trengthis releved by the weld thermal cycles, and thus the strength of the welded joint decrease substantially accompanied with the fracture in the HAZ. On the other hand, not only the softening but the fine microstructure can preserve the high toughness of TMCP steel in the HAZ.
Seo, Jun-Seok;Lee, Chang-Hee;Ryoo, Hoi-Soo;Kim, Hee-Jin
Proceedings of the KWS Conference
/
2010.05a
/
pp.18-18
/
2010
최근에 건조되는 선박이나 구조물들은 점차 대형화 되어가고, 이에 사용되는 판재들은 점차 고강도 극후판재화 되어가고 있다. 극후판재의 용접성을 향상시키기 위해서는 대입열 용접이 주로 적용되고 있는 실정인데, 30 mmt 이상의 후판을 1 pass로 용접하기 위해서는 EGW(Electro-gas welding) 기법을 사용한다. 대입열 용접은 용접입열(heat input)이 매우 높아 용착금속과 열영향부의 냉각속도가 매우 느려 용접열영향부에서 특히 fusion line 근처의 열영향부는 결정립 조대화 및 취약한 미세조직을 형성함으로서 저온인성을 크게 저하시키고, 연화 현상(softening effect)을 발생시켜 강도가 저하되는 문제점이 주로 발생하였다. 하지만 이런 문제점을 해결하기 위해 대입열용접에 사용된는 강재의 미세조직을 제어하여 AlN, TiN, $TiO_2$ 등의 석출물을 이용한 용접열영향부의 저온인성을 향상시켰다. 이러한 문제점이 발생하는 대입열용접에서 저온인성 시험은 주로 fuison line + 1, 2mm에서 수행한다. 하지만 대입열 용접시 용착금속의 냉각속도도 매우 느리기 때문에 용착금속의 위치에 따라 저온 인성 특성이 다르게 나타날 수 있다. 본 연구에서는 EGW 용착금속의 위치에 따른 저온인성 특성을 평가하기 위해 EH-36N, 40mmt 판재를 사용하여 1pole EG 용접 하였다. 용착금속의 저온인성 특성을 평가하기위해 충격 시편의 노치 위치가 fusion line - 2mm와 용접부 중앙을 기준으로 4곳을 선정하여 충격시험을 수행하였다. 또한 용착금속의 경도 분포를 알아보기 위해 micro vickers hardness tester(mitutoyo UR-501)을 사용해 hardness mapping 시험을 하였다. 용착금속의 저온인성은 미세조직과, 산소량에 따라 변화 할 수 있기 때문에 용착금속 위치를 달리하여 미세조직과 산소량도 각각 분석하였다. 용착금속의 저온인성을 향상시킬 수 있는 침상형페라이트와 비금속개재물의 상관관계에 관해 검토 하였다.
The use of high tensile steel plates is increasing in the fabrication of ship and offshore structures. The softening region which has lower yield stress than base metal is located to prevent cracking in the conventional high tensile steel. Also, thermo mechanical control process(TMCP) steel with low carbon equivalent has the softening region which occurs in the heat affected zone when high heat input weld is carried out. The softening region in the high tensile steel gives rise to serious effect on structural strength such as tensile strength, fatigue strength and ultimate strength. In order to make a reliable structural design using high tensile steel plates, the influence of the softening on plate strength should be evaluated in advance. In the previous paper, the authors discussed the ultimate compressive strength of 50HT steel square plates with softening region. In this paper, the ultimate compressive strength with varying the yield stress of softening region and the aspect ratio of the plate is investigated by using the elasto-plastic large deformation finite element method.
The corrosion fatigue test were carried out to evaluate the fatigue characteristics of accelerated cooled (ACC) TMCP high tensile strength steels and weld joint with high heat input by one side one run submerged are welding. In this paper, the fatigue crack growth behaviors were investigated with the center crack tension specimen of base metal and heat affected zone in substitute sea water and air, respectively Main results obtained are sunnarized as follows: 1. The fatigue crack growth rates in sea water faster than those in air environment for the different heat input values, crack growth rate of base metal is very fast and effect of heat input is not remarkable. 2. In HAZ (82kJ/cm, 116kJ/cm), the crack branching phenomena were observed in both air and sea water environment, 3. In SEM observation, the corrosion effect on base metal was larger than that on HAZ in corrosion environment.
Effectsof carbon content on the weldability of B-containing 620 grade high Cr ferritic cast steels were investigated. Cast steel with lower carbon content of 0.07% showed lower HAZ hardness because of the formation of lower carbon martensite in HAZ. It also showed less solidification cracking susceptibility in weld metal because of the formation of delta ferrite. However, hot ductility showed no difference between cast steels with lower and higher carbon contents. Cast steel with lower carbon content showed greater HAZ softening after PWHT in the region heated between AC1 and AC3 because of its higher base metal hardness.
마찰교반접합 (Friction Stir Welding)은 1991년 영국 TWI에서 개발된 접합 법으로서 회전하는 툴이 재료내부에 삽입되면 툴과 재료사이에서 발생하는 마찰열에 의하여 온도가 상승하게 되어 재료는 연화되고, 이러한 재료 내부에서 회전하는 툴이 이동하게 되면 재료 내부는 기계적 교반에 의해 소성변형이 일어남과 동시에 접합이 이루어진다. 마찰교반접합은 동적 재결정에 의한 접합부의 미세한 결정립 형성으로 인하여 기계적 특성이 향상되며 보호 가스가 필요 없어 친환경적임과 동시에 용융 용접 법에 비해 접합 시 에너지 소모가 적으며 또한 접합 후 접합부에서의 변형이 상대적으로 적다는 장점이 있다. 이러한 장점을 가진 마찰교반접합은 알루미늄 합금, 마그네슘 합금 그리고 동 합금과 같은 저 융점 비철재료에 많은 연구와 적용 사례들이 있어왔다. 하지만 최근에는 일반 탄소강, 연강, 오스테나이트계 스테인리스강, 니켈 합금, 티타늄 합금과 같은 고융점 재료에도 연구 및 적용이 진행되고 있는 추세이다. 페라이트계 스테인리스강은 가격이 비싼 Ni을 함유하지 않아 오스테나이트계 스테인리스강에 비하여 강재의 가격은 낮으면서도 고온특성 및 내식성이 우수하여 건축용, 자동차 배기계용으로 널리 사용되고 있다. 하지만 이런 장점을 가진 페라이트계 스테인리스강을 기존의 용융 용접 법으로 접합 시 용접부 및 열영향부에서의 결정립의 조대화로 인한 인성 및 연성이 저하되며, 특히 예민화된 열영향부 입계 내에 Cr 탄화물이 석출되어 입계주변에 Cr 결핍 층을 형성되어 입계부식이 발생되는 문제점이 발생된다. 본 연구에서는 마찰교반접합을 이용하여 두께 3mm의 409 스테인리스강에 대해 맞대기 접합을 실시하였다. 접합 변수를 툴의 재료 (WC-12wt%Co, $Si_3N_4$)로 하여 접합을 실시하였고 접합 후 외관상태 점검, 광학 현미경과 주사 전자 현미경을 통하여 미세조직을 관찰하였으며 황산-황산동 부식 시험을 실시하여 접합부의 부식 특성을 평가하였다.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.