• 한국세라믹학회지
• /
• 제35권6호
• /
• pp.635-639
• /
• 1998

When the low pressure injection molded parts are debinded by wicking and subsequent thermal pyrolysis the optimum transition point from wicking to thermal pyrolysis is just after the completion of the constant wicking rate period. Even when the partially debinded parts were heated at 5$^{\circ}C$/min after reaching the 1st falling rate period the debinding defects such as distortion and cracks were not found.

• 한국생산제조학회지
• /
• 제19권1호
• /
• pp.57-64
• /
• 2010

Metal Injection Molding (MIM) is attractive because it produces consistent, complex-geometry components for high-volume, high-strength, and high-performance applications. Also MIM using in optical communication field, display field, and semi-conductor field is a cost-effective alternative to metal machining or investment casting parts. It offers tremendous single-step parts consolidation potential and design flexibility. The objective of this paper is to study the suitability of design, flow analysis, debinding and sinterin processes, and capability analysis. The suitable injection conditions were 0.5~1.5 second filling time, 11.0~12.5 MPa injection pressure derived from flow analysis. The gravity of the product is measured after debinding an sintering. The maximum and minimum gravity levels are 7.5939 and 7.5097. the average and standard deviation are 7.5579 and 0.0122; when converted into density, the figure stands at 98.154%. According to an analysis of overall capacity, PPM total, which refers to defect per million opportunities(DPMO), stands at 166,066.3 Z.Bench-the sum of defect rates exceeding the actual lowest and highest limits-is 0.97, which translates into the good quality rate of around 88.4% and the sigma level of 2.47.

• 유기물자원화
• /
• 제15권4호
• /
• pp.100-106
• /
• 2007

피혁 제조 공정중 탈모 공정 이후 나피를 분할(Splitting)하여 얻어지는 피혁 가공 부산물(Limed pelt scrap)을 이용하여 탈회 및 탈지 과정의 전처리 공정을 거친 뒤 비크롬 탄닝과 열처리에 의한 방법과 glycidyl methacrylate (GMA)와 MMA와 같은 아크릴 모노머를 이용한 그라프트 공중합을 이용한 방법으로 우수한 내열성을 갖는 미세 콜라겐 분말을 제조하였다. 물성의 비교에서 본 연구의 방법으로 생산된 콜라겐 분말들이 열분해 온도, 열 저항성, 수분변화, 입도분포 등에서 더 나은 특성을 보였다.