• Composites Research
• /
• v.16 no.2
• /
• pp.33-40
• /
• 2003

In order to overcome one of the most pronounced shortcomings of conventional laminated composites, such as the low damage tolerance due to delamination, the thermoplastic materials and 3D (three-dimensional) preforms have been utilized in the manufacture of composite materials. From the newly developed process termed as the co-braiding, hybrid yarns of the thermoplastic fibers (PEEK) and reinforcing fibers (carbon) have been fabricated. In order to further enhance the delamination suppression, through thickness fibers have been introduced by way of 3D weaving technique in the fabrication of textile preforms. The preforms have been thermoformed to make composite materials. Complete impregnation of the PEEK into the carbon fiber bundles has been confirmed. For the comparison of mechanical performance of 3D woven composites, quasi-isotropic laminates using APC-2/AS4 tapes have been fabricated. Tensile and compressive properties of both the composites have been determined. Furthermore. the open hole, impact and CAI(Compression After Impact) tests were also carried out to assess the applicability of 3D woven textile reinforced thermoplastic composites in aerospace structures.

• Composites Research
• /
• v.31 no.4
• /
• pp.122-127
• /
• 2018

Sandwich composites of carbon fiber reinforced plastic(CFRP) and polymer foam will be used to automobile and aerospace industry according to increasing importance of light weight. In this study, mechanical and heat resistance properties of sandwich composites were compared with type of polymer foam (polyethylene terephthalate(PET), polyvinylchloride(PVC), epoxy and polyurethane). All types of polymer foams were degraded to 30, 60, 120, 180 minutes in $180^{\circ}C$. After heat degradation, the polymer foams were observed using optical microscope and compressive test was performed using universal testing machine(UTM). Epoxy foam had the highest compressive property to 2.6 MPa and after thermal degradation, the mechanical property and structure of foam were less changed than others. Epoxy foam had better mechanical properties than other polymer foams under high temperature. Because the epoxy foam was post cured under high temperature. As the results, Epoxy foam was optimal materials to apply to structures that thermal energy was loaded constantly.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.8
• /
• pp.562-570
• /
• 2018

New physical properties of polymer materials were obtained by blending two or three different type of polymers. TPE is used widely in the display, automotive and electronics industries. Consumers have sought emotionally more sensitive and advanced interior automotive parts. A polymer with high foamibility (Ed note: Please check this.) and flowability would be more plausible. TPE composed of foam is a good polymer material to satisfy these trends. In this research, two different TPE were tested, focusing on foamibility and flowability. Two type of TPE were prepared. The first was blended Homo-PP, oil and SEBS. The second was Co-PP, oil and SEBS. The blending temperatures were $180^{\circ}C$, $190^{\circ}C$, and $260^{\circ}C$(second one). The blending speed was 50rpm and blending time was 5 min. The MI of the blended material was affected by the MI of PP and not affected by the blending temperature. The hardness and tensile elasticity were less affected by the MI of PP and blending temperature. The hardness and tensile elasticity were lower at a higher SEBS/Oil content ratio. The soft touch feel was higher with high SEBS/Oil contents. The IPN (Interpenentration polymer network) structure was observed by dissolving the SEBS/Oil layer in xylene. Strain-hardening phenomena also was observed. TPE behaves in a rubber and foamed closed-cell improved its stability.