• Journal of Welding and Joining
• /
• v.8 no.4
• /
• pp.46-57
• /
• 1990

TMCP steel manufactured by controlled rolling followed by accelerated cooling process is known to have extra-ordinary mechanical properties such as tensile strength and toughness. However, there is much uncertainty about the fatigue fracture characteristics, especially, in the welded state of this steel. In case of this steel, the softening zone by welding is generated in heat affected zone in contrast with the case of conventional normalized high strength steel. This softening zone is considered to play significant roles in low cycle fatigue fracture of the welded part of this steel. In this paper, the low cycle fatigue behaviors of TMCP steel were inspected in as-received and welded state using the smooth specimen. The fatigue life-time was seperately investigated on the basis of failure of the specimen and crack initiation which is detected by differential strain method. Moreover, the low cycle fatigue characteristics of TMCP steel were quantitatively compared with those of the conventional normalized steel of same strength level.

• Journal of the Korea Concrete Institute
• /
• v.13 no.6
• /
• pp.602-609
• /
• 2001

A strut-and-tie model was proposed to predict the shear strength of RS beam which is a hybrid steel beam with reinforced concrete ends. The proposed model is capable of considering the concrete softening effects due to diagonal shear cracks at the embedded area of steel in concrete. It can predict tile failure strength of RS beam from the mathematical formulations which are based on equilibrium, compatibility, and the constitutive laws of cracked reinforced concrete. The previous experimental results of 15 RS beams were analyzed with the proposed model and the analytical results were also compared with formulas currently available. The comparison revealed that the proposed model can predict the strength of RS beam better than the others. The average ratio of experimental strengths to analytical results was 1.02 and the standard deviation was 0.126.

• The Journal of the Convergence on Culture Technology
• /
• v.9 no.2
• /
• pp.367-372
• /
• 2023

This study analyzed the use of scriptwriting and hologram technology for storytelling in the production of locally-centered cultural and artistic content. The musical <WolhwaJeon>, produced in the Gangneung area, was examined as a case study. The process of creating the script for the performance was used to establish the self-identity of the character "carp" and the stage visualization of the folktale "Yeonhwa." Furthermore, the use of hologram technology to actualize the inner expressions of the characters, deliver information, enhance spatiality, and visualize fantasy elements was examined. Through this approach, educational information about local folktales was provided to the local residents, and their pride in their region was heightened. This locally-centered content requires continuous development in a modern society that pursues cultural diversity, and future research is needed to produce and develop traditional and cultural content in other regions.

• Clinical and Experimental Pediatrics
• /
• v.51 no.11
• /
• pp.1205-1210
• /
• 2008

Purpose : The development of the corpus callosum occupies the entire period of cerebral formation. The myelination pattern on magnetic resonance imaging (MRI) is very useful to evaluate neurologic development and to predict neurologic outcome in high risk infants. The thickness of the corpus callosum is believed to depend on the myelination process. It is possible to calculate the length and thickness of the corpus callosum on MRI. Thus, we can quantitatively evaluate the development of the corpus callosum. We investigated the clinical significance of measuring various portions of the corpus callosum in neonate with neurologic disorders such as hypoxic brain damage and seizure disorder. Methods : Forty-two neonates were evaluated by brain MRI. We measured the size of the genu, body, transitional zone, splenium, and length of the corpus callosum. Each measurement was divided by the total length of the corpus callosum to obtain its corrected size. The ratio of corpus callosal length and the anteroposterior diameter of the brain was also measured. Results : There was no statistical significance in the sample size of each part of the corpus callosum. However, the corrected size or the ratio of body of the corpus callosum correlated with periventricular leukomalacia and hypoxic ischemic encephalopathy. Conclusion : The abnormal size of the corpus callosum showed a good correlation with periventricular leukomalacia and hypoxic ischemic encephalopathy in neonates. We can predict clinical neurological problems by estimation of the corpus callosum in the neonatal period.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.1
• /
• pp.62-68
• /
• 2001

In order to characterize the microscopic fracture behaviour of the weldment din stress corrosion cracking(SCC) phenomena, SCC and acoustic emission(AE) tests were carried out simultaneously and the correlation between mechanical paramenters obtained from SCC and AE tests was investigated. In the case of base metal, much more AE events were produced at -0.5V than at -0.8V because of the dissolution mechanism before the maximum load. Regardless of the applied voltages to the specimens, however, AE events decreased after the maximum load. In the case of weldment, lots of AE events with larger amplitude $range(40{\sim}100dB)$ were produced because of the singularities of weld HAZ in comparision to the base metal and post-weld heat-treated(PWHT) specimens. Numerous and larger cracks for the weldment were observed on the fractured surfaces by SEM examination. From these results, it was concluded that SCC for the weldment appeared most severely in synthetic seawater. Weld HAZ was softened by PWHT which also contributed to the reduced susceptibility to corrosive environment in comparison to the weldment.

• Journal of Welding and Joining
• /
• v.4 no.3
• /
• pp.43-49
• /
• 1986

Weldability of the TMCP steel manufactured by controlled rolling followed by accelerated cooling process was investigated. For comparison, two other steel plates produced by different manufacturing processes were selected; normalized and controlled rolled. Tandem submerged arc welding with both side one run technique was carried out. The results of this study can be summarized as follows; TMCP steel having the lowest carbon equivalent shows the best combination of mechanical properties, not only in the base metal but also in the heat affected zone. In the HAZ, the accelerated colling effect imarted on the trengthis releved by the weld thermal cycles, and thus the strength of the welded joint decrease substantially accompanied with the fracture in the HAZ. On the other hand, not only the softening but the fine microstructure can preserve the high toughness of TMCP steel in the HAZ.

• Journal of Ocean Engineering and Technology
• /
• v.10 no.3
• /
• pp.14-23
• /
• 1996

The corrosion fatigue test were carried out to evaluate the fatigue characteristics of accelerated cooled (ACC) TMCP high tensile strength steels and weld joint with high heat input by one side one run submerged are welding. In this paper, the fatigue crack growth behaviors were investigated with the center crack tension specimen of base metal and heat affected zone in substitute sea water and air, respectively Main results obtained are sunnarized as follows: 1. The fatigue crack growth rates in sea water faster than those in air environment for the different heat input values, crack growth rate of base metal is very fast and effect of heat input is not remarkable. 2. In HAZ (82kJ/cm, 116kJ/cm), the crack branching phenomena were observed in both air and sea water environment, 3. In SEM observation, the corrosion effect on base metal was larger than that on HAZ in corrosion environment.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.36 no.5
• /
• pp.377-383
• /
• 2016

The effect of long-term aging degradation on magnetic properties of ferritic 11Cr low-carbon steel was investigated. Coercivity and hysteresis loss measured from the hysteresis loops decreased with long-term aging time and showed that the relation was well fitted by a second order exponential function. Vickers hardness also decreased with aging time and resulted in mechanical softening. In addition, the microstructural evolution was observed by the scanning electron microscopy, backscattered electron image and X-ray diffraction. The $Cr_{23}C_6$ precipitates along grain boundary grew fast and Laves ($Fe_2W$) phase on martensitic lath boundaries in interior grains was developed. The solid solution atoms depleted in matrix and lath subgrains recovered owing to precipitate coarsening with long-term aging degradation. There was a close relation with softening of magnetic and mechanical properties.

• Journal of Korean Orthopaedic Sports Medicine
• /
• v.7 no.2
• /
• pp.75-83
• /
• 2008

과사용 증후군은 정상적인 조직에 최대하 부하(submaximal stress)가 지속되어 발생하는 것이다. 이와 같은 현상은 연부조직의 접합부(junction)에서 주로 일어나며 힘의 전달이 집중되는 곳, 조직의 역학적 성질이 변화되는 곳, 그리고 성장시 빨리 변화하는 성질이 있는 곳에 주로 생긴다. 근육의 불균형이 과사용 증후군의 가장 많은 원인이다. 과거의 부상 이후 부적절한 재활치료 및 각형성 또는 회전 부정정렬(angular and rotational malalignment) 등이 과사용 증후군의 원인이 될 수 있다. 스포츠 훈련 방법의 실수로도 과사용 증후군이 생길 수 있다. 전방 슬관절 동통시 감별해야 할 질환들은 jumper's knee, 슬개건염 혹은 대퇴 사두건염, Osgood-Schlatter 병, Sinding-Larsen-Johansson 병, 슬개골 연골 연화증, 슬개골 전(prepatellar) 혹은 슬개골 하(infrapatellar) 점액낭염, Hoffa's fat pad의 염증, 그리고 특발성 전방 슬관절 동통 증후군(idiopathic anterior knee pain syndrome)등이 있다. 후방 슬관절 통증의 원인 질환으로는 만성 슬와근 염좌, 슬괵건 점액낭염, 경골 골간단의 피로 골절 등이 포함되며 외측 슬관절 통증의 원인으로는 장경대 충돌 증후군(iliotibial band friction syndrome)등이 있을 수 있다. 이외 과사용 증후군과 관련된 슬관절 통증의 원인으로 다분 슬개골(multipartite patella), 내측 경골 스트레스 증후군(medial tibial stress syndrome), 박리성 골연골염, 반월상 연골의 퇴행성 변화 등이 있을 수 있다. 과사용 증후군의 진단 및 치료의 일반적인 접근법은 다섯가지 단계의 프로그램으로 요약될 수 있다. 첫째, 원인 요소를 확인하고, 둘째, 요소를 변경시키고, 셋째, 통증을 조절하고, 넷째, 능동적 재활을 시키고, 그리고 다섯째, 유지시키는 것이다.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.29-29
• /
• 2010

레이저 용접은 고밀도 에너지빔을 이용하는 용접방법으로 아크용접에 비해 빠른 용접과 깊은 용입이 가능하며, 낮은 열이력을 가지는 장점이 있다. 때문에 열에 의해 연화되는 고강도강의 용접에 큰 이점을 가지고 있다. 차체경량화 추세와 더불어 차량에 고강도강의 적용이 늘어나고 있는데 충돌시 차량 구조를 유지시켜주는 범퍼나 B-필러와 같은 부품에 적용되는 무도금 보론 합금강과 알루미늄 코팅 보론 합금강은 핫스템핑(Hot Stamping) 기술에 의해 제조된 소재로 약 1.5GPa의 인장강도를 가진다. 알루미늄 코팅 보론 합금강의 경우 제조공정과 이송 중 소재 표면산화에 의한 산화철발생 또는 표면 탈탄 현상을 방지하기 위해 알루미늄 코팅 처리를 하는데 이러한 코팅층이 용접시 용접부의 물성을 저하시키는 역할을 한다고 보고되어 있다. 본 연구에서는 1.5GPa급 무도금 보론 합금강과 알루미늄 코팅 보론 합금강을 대상으로 레이저 용접을 적용하여 용접부 특성을 파악하고자 하였다. 실험은 겹치기 형상으로 Fiber Laser, Disk Laser를 적용하여 진행하였으며 빔Size, 용접속도, Gap등을 변경하며 해당조건에서의 용입특성, 파단모드, 기계적특성 등을 알아보았다.