• Resources Recycling
• /
• v.10 no.6
• /
• pp.3-8
• /
• 2001

This study was examed about leaching behavior in order to separate plasticizer selectively before dechlorination from flexible PVC material in alkali solutions at $80~120^{\circ}C$. The dechlorination of that was not almost occurred below $100^{\circ}C$. But the yield of elution of plasticizer was 100% above 5M NaOH. Therefore, by controlling alkali concentration and reaction temperature, it is possible to extract the plasticizer selectively without taking dechlorination.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.05a
• /
• pp.40-40
• /
• 2007

• Fire Science and Engineering
• /
• v.16 no.4
• /
• pp.77-84
• /
• 2002

In this paper, we had analyzed comsbustion gases using a GASTEC colorimetric gas detector tube according to the method of NES 713 in order to combustion gases toxicity evaluation for beads polystyrene foam, extruded polystyrene foam, rigid polyurethane foam, flexible polyurethane foam, flexible polyvinyl chloride pipe, vinyl floor cover, polyethyelene foam(flame retardant untreated) and polyethyelene foam (flame retardant treated) of plastics material. As results of gas analyses by using this method, comsbustion gases producted from small specimens of plastics material had reached fatal to man at 30 minutes exposure time that had possesed toxicity index of more than 1. Toxicity indexes of each specimen were estimated range of 4.3∼179.2, flexible polyvinyl chloride showed the hightest toxicity index at 179.2, and beads polystyrene foams showed the lowest toxicity index at 4.3.

• Elastomers and Composites
• /
• v.15 no.1
• /
• pp.3-9
• /
• 1980

The oxygen permeability and it's proofness of te various commercial polymer films have been investigated at the constant pressure and temperature. Oxygen proofness, the reciprocals of the oxygen permeability for the various samples, were determined by means of a coulometric oxygen permeability tester. The testing of sample films was performed at constant temperature $(23{\pm}1^{\circ}C)$ under 1 atm. for 24 hours. The order of the relative proofness observed are as follows; oriented Nylon (O. Nylon)> oriented Polyester (O. PET)>nonoriented Nylon (N. Nylon)>nonoriented Polyester (N.PET)> rigid Polyvinyl chloride (Rigid PVC)>semirigid Polyvinyl chloride (Semirigid PVC)> oriented Polypropylene (O. PP)>plasticized Polyvinyl chloride (P. PVC)> casted Polypropylene (C. PP)> low density Polyethylene (LDPE)>high density Polyethylene (HDPE, Inflation)> high density-polyethylene (HDPE, T-die) The oxygen proofness of the films was increased with the polarity cf polymer, the film thickness and mechanical orientation and decreased with the addition of plasticizer in PVC. For the use of wrapping materials, one film with the polar property in the main chain of the polymer molecule and the others with nonpolar property in it are laminated for the protection from oxygen and moisture.