• Restorative Dentistry and Endodontics
• /
• v.33 no.5
• /
• pp.428-434
• /
• 2008

The purpose of this study was to compare the microtensile bond strength in Class I cavities associated with different light curing modes of same light energy density. Occlusal enamel was removed to expose a flat dentin surface and twenty box-shaped Class I cavities were prepared in dentin. Single Bond (3M Dental product) was applied and Z 250 was inserted using bulk technique. The composite was light-cured using one of four techniques, pulse delay (PD group), soft-start (SS group), pulse cure (PC group) and standard continuous cure (CC group). The light-curing unit capable of adjusting time and intensity (VIP, Bisco Dental product) was selected and the light energy density for all curing modes was fixed at $16J/cm^2$. After storage for 24 hours, specimens were sectioned into beams with a rectangular cross-sectional area of approximately $1mm^2$ Microtensile bond strength $({\mu}TBS)$ test was per- formed using a univel·sal testing machine (EZ Test, Shimadzu Co.). The results were analyzed using oneway ANOVA and Tukey's test at significance level 0.05. The ${\mu}TBS$ of PD group and SS group was higher than that of PC group and CC group. Within the limitations of this in vitro study, modification of curing modes such as pulse delay and soft start polymerization can improve resin/dentin bond strength in Class I cavities by controlling polymerization velocity of composite resin.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.349-349
• /
• 2012

산화제를 이용 기상중합법을 통해 합성되는 고전도도 Poly (3,4-Ethylenedioxythiophene)(PEDOT) 박막은 OTFT, RFID tag, 또는 연성 디스플레이 같은 분야에 다양한 응용 가능성을 가지고 있으며 이로 인해 최근에 연구가 활발히 진행되고 있다. PEDOT박막의 전극소재로써 가능성은 박막의 중합 정도와 표면 형상에 크게 좌우된다. 특히, Si-웨이퍼 기판 위에 산화제의 균일한 도포 및 산화제 자체의 높은 산도 ($pH{\leq}2$)에 따른 부반응의 억제는 기상중합법을 이용한 PEDOT박막의 합성에 있어 매우 중요하다. PEDOT의 효율적인 중합과 균일한 성장을 위해 산화제에 DUDO 와 PEG-PPG-PEG를 첨가한 혼합 산화제 용액을 제조 기상중합 방법을 통해 PEDOT박막을 제작하였다. 그 결과 산화제만을 사용하여 제작된 박막에 비해 전도도가 최대 3,660 S/cm로 향상된 PEDOT 박막이 합성되었다. 이러한 결과는 PEG-PPG-PEG가 산화제 용액의 균일 도포를 향상시키고 Base Inhibitor로 작용하는 DUDO는 PEDOT 성장 시 중합속도를 조절하고 부반응을 최소화 하여 효율적인 공액 이중 결합의 생성을 촉진한데 주로 기인한다. 따라서 그로인해 조밀하며 마이크로 스케일의 기공이 최소화된 PEDOT박막의 합성이 가능하였다. PEDOT박막의 특성 평가에는 4-point probe, optical microscopy, Field Emission-Scanning Electron Microscope, 등이 사용되었으며 또한 전도도의 향상 원인을 분석하고자 ATR-IR Spectrophotometer를 이용하여 합성된 박막의 작용기를 분석하였다. 이러한 고전도도의 PEDOT 박막이 OTFT의 전극소재로 사용된다면 OTFT소자의 성능 향상에 크게 기여 할 것으로 기대된다.

• The Journal of Korean Academy of Prosthodontics
• /
• v.58 no.4
• /
• pp.275-281
• /
• 2020

Purpose: Development of a latent antimicrobial soft liner is strongly needed to overcome a possible inflammation related with its dimensional degrade or surface roughness. Modified tissue conditioner (TC) containing chitosan-doped silver nanoparticles (ChSN) complexes were synthesized and assessed for their characterizations. Materials and methods: ChSN were preliminarily synthesized from silver nitrate (AgNO₃), sodium borohydride (NaBH₄) as a reducing agent and chitosan biopolymer as a capping agent. Ultraviolet-visible and Fourier transform infrared spectroscopy were conducted to confirm the stable reduction of nanoparticles with chitosan. Modified TC blended with ChSN by 0 (control), 1.0, 3.0 and 5.0 % mass fraction were mechanically tested by ultimate tensile strength (UTS), silver ion elution and color stability (n=7). Results: At 24 hour and 7 day storage periods, UTS values were not significant (P>.05) as compared with pristine TC (control) and silver ion was detected with the dose-dependent values of ChSN incorporated. Color stability of TC were influenced by ChSN add, with the higher doses, the significantly greater color changes (P<.05). Conclusion: A stable synthesized ChSN was acquired and modified TC loading ChSN was characterized as silver ion releasing without detrimental physical property. For its clinical application, antimicrobial test, color control and multifactor investigations are still required.