We investigated the optimum bonding conditions for thermo-compression bonding of electrodes between flexible printed circuit board(FPCB) and rigid printed circuit board(RPCB) with Sn-58Bi solder as interlayer. In order to figure out the optimum bonding conditions, peel test of FPCB/RPCB joint was conducted. The peel strength was affected by the bonding conditions, such as temperature and time. The fracture energies were calculated through F-x (Force-displacement) curve during peel test and the relationships between bonding conditions and fracture behaviors were investigated. The optimum condition for the thermo-compression bonding with Sn-58Bi solder was found to be temperature of $195^{\circ}C$ and time of 7 s.

• Journal of the Microelectronics and Packaging Society
• /
• v.11 no.1
• /
• pp.29-36
• /
• 2004

A flexible packaging scheme, which includes chip packaging, has been developed using a thinned silicon chip. Mechanical characteristics of thinned silicon chips are examined by bending tests and finite element analysis. Thinned silicon chips (t<30 $\mu\textrm{m}$) are fabricated by chemical etching process to avoid possible surface damages on them. And the chips are stacked directly on $Kapton^{Kapton}$film by thermal compressive bonding. The low height difference between the thinned silicon chip and $Kapton^{Kapton}$film allows electroplating for electrical interconnection method. Because the 'Chip' is embedded in the flexible substrate, higher packaging density and wearability can be achieved by maximized usable packaging area.

• Journal of the Korean Society for Precision Engineering
• /
• v.33 no.7
• /
• pp.601-606
• /
• 2016

In this paper, an energy harvester is developed that has advantages regarding piezoelectric noise minimization, mass production, and an easily available environmental energy source, electromagnetic induction, as well as low-frequency bandwidth and high amplitude. A process for fabricating a three-dimensional multilayered planar coil using micro-electro-mechanical systems (MEMS) on a flexible printed circuit board FPCB is introduced. Optimal shape and size were calculated via internal resistance and inductance, and a prototype was fabricated through the MEMS procedure while considering the possibility of mass production. Although the internal resistance matched the designed value, the electromotive force generated did not reach the intended amount. The main reason for the decrease in efficiency was the low area of coil outskirt exposed to the magnetic field while there was relative motion between the magnet and the coil.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2013.05a
• /
• pp.132-132
• /
• 2013

본 연구는 R/F-PCB(Rigid/Flexible Printed circuit Board)의 Cu Pattern에 최종 표면처리 방법으로 사용되는 ENIG(Electroless Ni/Immersion Gold) 공정을 대체하여 ECIG(Electroless Co/Immersion Gold)공정을 적용하고자 하는 것으로 무전해 니켈 도금의 장점인 고경도, 내마모성, 납땜성, 내식성을 가지면서 니켈 도금의 취약점인 연성을 개선한 도금액을 개발하고자 하였다. 개발된 도금액을 이용하여 Cu Pattern에 도금할 경우 일반 무전해 니켈 도금에서 나타나는 불량 원인 중 하나인 Space 부분에 도금이 되는 현상이 현저히 감소하였으며, 연성 또한 향상됨을 관찰할 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04b
• /
• pp.128-131
• /
• 2002

연성 AI 전극을 이용하여 플라스틱 기판 위에 대칭성 박막 다이오드를 제작하였다. 다이오드의 구조는 $Al/Ta_{2}O_{5}/Al$의 3층 구조로 되어 있다 상부 AI 전극 제작시 하부 AI 전극의 손상을 방지하기 위해 무(無)식각 공정을 개발, 적용하였다. AI 전극을 사용한 결과 단단한 Ta 전각에서 나타난 변형 빛 균열 문제가 해결되었다. 또한 상부 빛 하부의 대칭성 전극 구조로 제작함으로써 I-V 곡선이 완벽한 대칭형의 우수한 전기적 특성을 얻을 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.04a
• /
• pp.39-40
• /
• 2006

We prepared ZnO:Al (AZO) thin films on polycarbonate (Pc) and polyethersulfon (PES). Because the polymer substrate has weak thermal resistance. The AZO thin films were deposited at room temperature by facing targets sputtering (FTS) method In the work, AZO thin films were deposited with different thickness in 1mTorr and $O_2$ gas flow rate 0.05. The electrical, optical and crystallographic properties were measured From the results, the resistivity of $7.3{\times}10^{-4}{\Omega}cm$ and transmittance of over 80% in visible range were obtained.

• Journal of the Institute of Electronics Engineers of Korea SC
• /
• v.47 no.6
• /
• pp.97-104
• /
• 2010

In this paper, ICT (in circuit tester) inspection system and inspection algorithm is proposed and detects whether inferiority exists or not in the mounted device on the flexible PCB in cell phones or mobile display devices. The system is composed of PD (pin-driver) and GGM (ground guarding method). The structural characteristics of these flexible PCB are analyzed, which is needed to input or output the test signal. Test signal to investigate the characteristics of passive components is generated using modified circuit diagram and proposed inspection algorithm. PM (pin-map) is decided on the basis of circuit diagram and has the information about the kind of test signal to be applied and the pad number for the test signal to be connected. PD is designed to load a proper test signal for a specific pad and is adjusted according to PM so that the reconstructed circuit has minimum node and mash. The proposed ICT inspection system is realized using PD and GGM. Using the system, an experiment for each passive component is done to investigate the measurement accuracy of the developed system and an experiment for real flexible PCB model is done to verity the effectiveness of the system.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.79-85
• /
• 2007

This study was focused on the feasibility of ultrasonic bonding of Au stud flip chip bumps on the flexible printed circuit board (FPCB) with three different surface finishes: organic solderability preservative (OSP), electroplated Au and electroless Ni/immersion Au (ENIG). The Au stud flip chip bumps were successfully bonded to the bonding pads of the FPCBs, irrespective of surface finish. The bonding time strongly affected the joint integrity. The shear force increased with increasing bonding time, but the 'bridge' problem between bumps occurred at a bonding time over 2 s. The optimum condition was the ultrasonic bonding on the OSP-finished FPCB for 0.5 s.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.171-171
• /
• 2013

2층 FCCL (연성회로기판, Flexible Copper Clad Laminate)에 있어서 폴리이미드 필름과 구리의 접착력을 향상 시키기 위해 기존에 사용되고 있는 Ni-Cr대신 박리강도가 높고 에칭성도 매우 뛰어난 Ni-Mo-Nb 박막을 Roll-to roll 스퍼터 장비를 이용하여 개발하였다. 새롭게 개발된 Ni-Mo-Nb 박막은 기존 연구되어진 Ni-Cr 물질 대비 고온 박리강도 약 1.5~2.0배, 에칭성 8배 이상의 매우 우수한 특성을 보였다. Ni-Mo-Nb 접착층의 두께가 7~40 nm로 증가함에 따라 상온 박리강도가 향상 되는 것을 확인하였다. Ni-Mo-Nb 박막을 증착 하기 전 폴리이미드 기판표면을 RF 플라즈마 전처리 하였을 때 0.67 kg f/cm의 우수한 상온 박리강도를 나타내었으며 FCCL 샘플을 $150^{\circ}C$에서 168시간동안 열처리 한 후 접착력을 측정하였을 때도 0.54 kg f/cm의 높은 고온 박리강도를 보였다. FCCL의 박리강도, 표면 거칠기, 원소들의 화학적 결합, 박막의 미세구조를 peel test, atomic force microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy를 이용하여 폴리이미드 기판 플라즈마 전처리 효과를 확인하였다. 그 결과 플라즈마 전처리를 한 폴리이미드 기판의 경우 처리하지 않은 기판보다 상온과 고온에서 더 우수한 접착력을 가지는 것을 확인 할 수 있었는데 이것은 폴리이미드 기판의 표면 거칠기 증가에 의한 mechanical interlocking effect가 아닌 전처리를 통한 폴리이미드 표면 개질로 C-0, C-N와 같은 chemical functional group이 증가했기 때문인 것으로 확인되었다.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.05a
• /
• pp.39.1-39.1
• /
• 2009

본 실험은 연성과 광 투명도가 뛰어난 아크릴 (PMMA) 과 폴리카보네이트 (Polycabonate) 기판의 축전 결합형 플라즈마 (CCP) 건식 식각 연구에 관한 것이다. 특히 식각 반응기 내부의 압력 변화에 따른 두 기판의 건식 식각 특성 분석에 초점을 맞추었다. 실험에 사용된 기판은 두께 1mm의 아크릴 (PMMA) 과 폴리카보네이트 (Polycabonate)를 $1.5\times1.5\;cm^2$로 절단하여 Photo-lithography 공정을 통하여 감광제 (Photo-resist)로 패턴하였다. 식각 반응기 내부에 패턴 된 아크릴(PMMA) 과 폴리카보네이트 (Polycabonate)를 넣은 후 반응기 내부 진공 상태로 만들었다. 그 후 5 sccm $O_2$ 가스를 유량조절기 (Mass flow controller)를 통하여 식각 반응기 내부로 유입하여 실험을 하였다. 이때 식각 공정 변수는 식각 반응기 내부 압력과 샘플 척 파워이다. 특성평가 항목은 식각 후 기판 (Substrate)의 식각율 (Etch rate), 식각 선택비 (Selectivity) 그리고 기판 표면 거칠기 (RMS roughness)이다. 실험 결과는 표면 단차 분석기(Surface profiler)를 이용하여 기판 (Substrate)의 표면을 분석 하였다. 또한 OES (Optical Emission Spectroscopy) 를 이용하여 식각 중 내부 플라즈마의 상태를 분석하였다. 본 실험 결과에 따르면 5 sccm $O_2$ 가스와 100 W 척 파워를 고정한 후 반응기 내부의 압력을 25 mTorr에서 180 mTorr까지 변화시켜 실험한 결과 40 mTorr의 반응기 내부 압력에서 실험 자료 중 가장 높은 식각율로 아크릴 (PMMA)은 $0.46\;{\mu}m/min$, 폴리카보네이트 (Polycabonate)는 $0.28\;{\mu}m/min$의 결과를 얻었다. 또한 이 자료를 바탕으로 5 sccm $O_2$ 가스와 반응기 내부 압력을 40 mTorr로 고정시키고 RIE 척 파워를 25 W에서 150 W로 증가시켰을 때 아크릴 (PMMA)의 식각율은 $0.15\;{\mu}m/min$에서 $0.72\;{\mu}m/min$까지 증가하였고, 폴리카보네이트 (Polycabonate) 의 식각율은 $0.1\;{\mu}m/min$에서 $0.36\;{\mu}m/min$까지 증가하였다.