• Composites Research
• /
• v.18 no.2
• /
• pp.38-45
• /
• 2005

Phase transformation behaviors and crystal structures of Nitinol shape memory alloy $(54.5Ni-45.5Tiwt\%)$ are investigated by varying annealing heat treatment conditions through DSC (Differential Scanning Calorimetry) and XRD (X-Ray Diffraction). Annealing heat treatment conditions were considered as heat treated times of 5min, 15min. 30m1n, and 45min, as well as heat treated temperatures of $400^{\circ}C,\;500^{\circ}C,\;525^{\circ}C,\;550^{\circ}C,\;575^{\circ}C,\;600^{\circ}C,\;700^{\circ}C,\;800^{\circ}C,\;and\;900^{\circ}C$ According to the results, annealing heat treatment conditions such as heat treated times and heat treated temperatures were found to affect significantly on phase transformation behaviors and crystal structures of Nitinol shape memory alloy.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2009.11a
• /
• pp.46.2-46.2
• /
• 2009

휴대전화, 랩톱 컴퓨터 등 각종 모바일기기 및 디스플레이 기기의 경박단소화 및 고기능화에 따라 연성회로기판(FPCB)의 사용량이 증가하고있다. 연성회로기판의 핵심소재인 동박적층필름(FCCL)은 폴리이미드필름과 접착층, Cu 층으로 구성되는데, 이 중접착층으로 사용되는 Ni-20Cr합금은 에칭공정 후 Cr의 잔류에 의해 불량률 증가가 문제되고 있어, Ni-Cr합금 스퍼터링 타깃의 Cr 함량 저감 또는 Cr-free Ni합금 개발 등이 요구되고 있다. 본 연구에서는 차세대 FCCL 본드층에 적합한 Ni기 합금을 개발하기 위한 기초연구로써 Cr 함량 및 가공열처리조건에 따른 미세조직과 집합조직 변화를 조사하였다. 4N급의 고순도Ni과 Cr을 진공 플라즈마 용해장치로 용해하여Ni-xCr (x=5, 10, 15, 20wt.%)합금 잉곳을 만들고, 이를 두께감소율 90%로 냉간압연한 후, $600^{\circ}C$ 및 $800^{\circ}C$에서 10~120분 동안 어닐링하여 시편을 준비하였다. 광학현미경으로 미세조직을 관찰하고, Micro-Vickers 경도시험을 통해 어닐링 조건에 따른 경도변화를 조사하였다. 또한 SEM-EBSD를 이용하여 집합조직 및 입계특성을 분석하였다. $600^{\circ}C$ 어닐링 시 Cr함량이 증가할수록 재결정 완료시간이 증가하여 Ni-20Cr합금의 경우 2시간이상 어닐링에도 재결정이 일어나지 않았다. $800^{\circ}C$ 어닐링 시 10분 어닐링 조건에서 4종류 합금 모두 재결정이 완료되었으며, 동일한 어닐링 조건에서 Cr함량이 증가할수록 결정립이 작아지는 것으로 나타났다. $800^{\circ}C$ 2시간 어닐링 조건에서 Ni-5Cr 합금의 주요 집합조직은 {223}<113>과 {122}<112>로 나타났으며, 이중 {223}<113>은Cr 함량이 증가함에 따라 점차 {122}<112>에 가까운 방향으로 변화되어 Ni-20Cr 합금의 경우 {123}<112>만이 형성되었다. 이러한 집합조직의 변화는 적층결함에너지 감소에 의한 ${\Sigma}3$ 입계의 분율 증가와 밀접한 관련이 있는 것으로 사료된다.

• Composites Research
• /
• v.22 no.2
• /
• pp.1-6
• /
• 2009

The mechanical characteristics of gamma-ray irradiated UHMWPE specimens were investigated under various heat treatment conditions. The heat treatment was performed in the range of annealing and remelting temperatures. The annealing treatment below the temperature of $130^{\circ}C$ hardly induced changes in the tensile strength, the strain at the failure and the hardness. However the remelting treatment above $140^{\circ}C$ deteriorated those mechanical properties. It was shown in an FTIR analysis that the annealing treatment caused some oxidation of free radicals created by the pretreatment of the irradiation. These quantitative data represented by the behavior of mechanical properties might be used as basic informations for the design and analysis of various artificial joints.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.426-429
• /
• 2003

In this study, phase transformation characteristics of Nitinol shape memory alloy with 54.5wt%Ni-45.5wt%Ti were investigated by varying with annealing treatment and cutting conditions through DSC(differential scanning calorimetry). Annealing treatment conditions were considered as heat treated time of 5 min, 15 min, 30 min, and 45 min, heat treated temperature of 40$0^{\circ}C$, 50$0^{\circ}C$, 5$25^{\circ}C$, 55$0^{\circ}C$, 575$^{\circ}C$, $600^{\circ}C$, $700^{\circ}C$, 80$0^{\circ}C$, and 90$0^{\circ}C$, and environmental condition of heat treatment under vacuum or air. Cutting conditions were considered as no cutting, one side cutting, and two side cutting. Tensile test was also conducted on Nitinol shape memory alloy to investigate thermomechanical characteristics by varying with annealing heat treatment histories. According to the results, annealing treatment and cutting conditions were found to significantly affect on phase transformation and thermomechanical characteristics of Nitinol shape memory alloy.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.208-208
• /
• 2003

RF 마그네트론 스퍼터링법을 이용하여 Ar과 $O_2$의 유량을 25sccm씩 흘리면서 $SiO_2$/Si기판 위에 Sn $O_2$ 박막을 증착하였다. 증착된 박막은 columnar 구조로 성장하였으며 많은 입자들이 뭉쳐서 형성된 양배추꽃(cauliflower) 형태의 뭉친 입자(agglomerates)를 가지는 표면형상이 관찰되었다. 분위기에 따른 어닐링 효과를 확인하기 위하여 50$0^{\circ}C$에서 공기와 질소 분위기하에서 열처리하였다. 열처리한 후 표면거칠기가 개선되었으며, 표면형상의 변화가 발생하였다. 특히 50$0^{\circ}C$, 질소분위기에서 어닐링한 경우는 양배추꽃 형태의 표면형상이 소수의 작은 입자가 뭉친 형태로 분리되면서 입도분포가 개선되었다. 이러한 결과는 어닐링 과정에서 발생되는 응력을 완화시키기 위하여 표면형상의 변화가 발생하는 것으로 판단된다. XPS 측정 결과, 질소 분위기에서 어닐링한 후에 OIs와 Sn5/3d 피크가 낮은 결합에너지에 위치하고 있어 산소공공의 농도가 어닐링 전에 비하여 증가하였음을 확인할 수 있다. 어닐링 전후에 Sn $O_2$ 박막의 면저항 측정 값은 XPS 결과와는 달리 질소 분위기 어닐링한 후에 오히려 면저항값이 크게 증가하였다. 이러한 결과는 질소 분위기 어닐링한 후 표면형상의 변화에 기인하여 입자간의 연결성이 저하되어 면저항값이 증가한 것으로 추정된다. 산소분위기에서 어닐링한 후에 전체적으로 전기적 특성의 재현성이 개선되었으며 Sensitivity( $R_{air}$/ $R_{gas}$)가 향상되었음을 확인하였다.하였다.석을 통하여 La의 분포를 확인하였으며, HRTEM 분석을 통하여 미세구조분석을 실시하였다.2463eV였다. 10K에서 광발광 봉우리의 919.8nm (1.3479eV)는 free exciton(Ex), 954.5nm (1.2989eV)는 donor-bound exciton 인 I2(DO,X)와 959.5nm (1.2921eV)는 acceptor-bound exciton 인 I1(AO,X) 이고, 964.6nm(1.2853eV)는 donor-acceptor pair(DAP) 발광, 1341.9nm (0.9239eV)는 self activated(SA)에 기인하는 광발광 봉우리로 고찰되었다.가 높을수록 방출전류가 시간에 따라 급격히 감소하였다. 각 duty비에서 방출전류의 양이 1/2로 감소하는 시점을 에미터의 수명으로 볼 때 duty비 대 에미터 수명관계를 구해 높은 duty비에서 전계방출을 시킴으로써 실제의 구동조건인 낮은 duty비에서의 수명을 단시간에 예측할 수 있었다. 단속적으로 일어난 것으로 생각된다.리 폐 관류는 정맥주입 방법에 비해 고농도의 cisplatin 투여로 인한 다른 장기에서의 농도 증가 없이 폐 조직에 약 50배 정도의 고농도 cisplatin을 투여할 수 있었으며, 또한 분리 폐 관류 시 cisplatin에 의한 직접적 폐 독성은 발견되지 않았다이 낮았으나 통계학적 의의는 없었다[10.0%(4/40) : 8.2%(20/244), p>0.05]. 결론: 비디오흉강경술에서 재발을 낮추기 위해 수술시 폐야 전체를 관찰하여 존재하는 폐기포를 놓치지 않는 것이 중요하며, 폐기포를 확인하지 못한 경우와 이차성 자연기흉에 대해서는 흉막유착술에 더 세심한 주의가 필요하다는 것을 확인하였다. 비디오흉강경수술은 통증이 적고, 입원기간이 짧고,

• Polymer(Korea)
• /
• v.36 no.2
• /
• pp.131-136
• /
• 2012

Residual stress is developed in the injection molded articles during the molding process due to temperature variation and shear stress. The residual stress causes the deformation and warpage in the injection molded parts shortly within several days or after several years. Therefore, the injection molding conditions should be optimized to reduce the residual stress. And residual stress in the part should be also relaxed after molding process to maintain its shape. According to the annealing conditions, such as relative humidity, temperature and time, this study investigates the relaxation of residual stress generated in the transparent injection molded specimens. Through the experimental results, it was realized that the residual stress was relaxed at a relative humidity higher than 50%. Utilizing photoelasticity equipment, it was found that the residual stress was rapidly relaxed near glass transition temperature. Additionally, we recognized that the specimen shrunk along the flow direction but expanded to the perpendicular direction of the flow during the annealing processes, which resulted in the warpage of the specimen.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2000.04a
• /
• pp.39-39
• /
• 2000

열간단조후 절삭가공하여 냉간 성형가공하는 알루미늄 제품은 열간단조하면 재료가 연화되어 있어 절삭가공시 연속적인 칩이 발생하여 공구와 피삭재를 감고 회전함으로서 가공면 손상, 공구파손 및 작업자의 안전을 초래함에 따라 가공이 어려워 단지 절삭성 개선 목적만을 위해 중간공정으로 T4 열처리하여 절삭가공하고 다시 어닐링처리하여 냉간성형을 하고 최종열처리를 한다. 따라서 본 연구는 열간단조후 제품을 급냉시키면 용제화처리의 효과를 얻어 재료가 경화됨으로써 절삭성이 개선될 수 있다는 이론에 근거하여 T4 열처리를 대체할 수 있는 후처리 방법에 대해 연구하였다. 최적의 후처리방법을 구하기 위해 열간단조후 수냉과 공냉처리를 비교 분석하였고, 열간단조후 냉각처리까지 지연된 시간과 수냉과정에서의 유지시간에 따른 분석을 통해 최적의 작업조건을 선정하였다.

• Journal of the Korean Society for Heat Treatment
• /
• v.17 no.2
• /
• pp.78-86
• /
• 2004

Effects of the annealing parameters on the formation of ferrites transformed at low temperatures were studied in cold-rolled ultra low carbon steels with niobium and/or chromium. Niobium and chromium were found to be effective in the formation of the low temperature transformation ferrites. The low temperature transformation ferrites more easily formed when both higher annealing temperature and longer annealing time, allowing substitutional alloying elements to distribute between phases, are in combination with faster cooling rate. It was found from EBSD study that the additions of niobium or chromium resulted in the increase in the numbers of high angle grain boundaries and the decrease in those of the low angle grain boundaries in the microstructures. Both granular bainitic ferrite and bainitic ferrite were characterized by the not clearly etched grain boundaries in light microscopy because of the low angle grain boundaries.

• Composites Research
• /
• v.34 no.5
• /
• pp.311-316
• /
• 2021

In this study, TiC/steel metal matrix composites were fabricated by powder metallurgy process using Fealloy powders with 3 wt.% Cr and 10 wt.% Cr, respectively, as matrix material. Subsequently, the composite samples were heat treated by the annealing and quenching-tempering(Q-T), respectively, to understand the effect of heat treatment on the mechanical properties of the composites. The correlation between microstructure and structural strength depending on the chromium content and the heat treatment conditions was studied through tensile, compressive, and transverse rupture test and microstructural analysis. In the case of TiC/steel composite containing 10 wt.% Cr, the tensile strength and transverse rupture strength at room temperature were significantly lowered by the influence of coarse chromium carbide formed at the TiC/steel interface. On the other hand, both TiC/steel composites containing 3 wt.% Cr and 10 wt.% Cr showed much higher compressive strength of about 4 GP after quenching-tempering compared to the annealed specimens regardless of the presence of the chromium carbide.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.36 no.5
• /
• pp.454-462
• /
• 2023

Flash lamp annealing (FLA) of metal nanoparticle (NP) ink has provided powerful strategies to fabricate high-performance electrodes on a flexible substrate because of its rapid processing capability (in milliseconds), low-temperature process, and compatibility with to roll-to-roll process. However, metal NPs [e.g., gold (Au), silver (Ag), copper (Cu), etc.] have limitations such as difficulty in synthesizing fine metal NPs (diameter less than 10 nm), high price, and degradation during ink storage and FLA processing. In this regard, organometallic ink has been proposed as a material that can replace metal NPs due to their low-cost (usually 1/100 times cheaper than metal nano inks), low-temperature processability, and high material stability. Despite these advantages, the fabrication of flexible electrodes through FLA treatment of organometallic compounds has not been extensively researched. In this paper, we experimentally guide how to determine the optimal conditions for forming electrodes on flexible substrates by considering material parameters, and flashlight processing parameters (energy density, pulse duration, etc) to minimize the difficulties that may arise during the FLA of organometallic ink.