• Journal of the Korean Electrochemical Society
• /
• v.3 no.2
• /
• pp.100-103
• /
• 2000

Polymeric gel electrolytes based on polyacrylronitile blended with poly(vinylidene fluoride-co-hexafluoro-propylene)(P(VdF-co-HFP), which were reinforced with glass fiber cloth(GFC) to increase the mechanical strength, were prepared for the practical use in secondary battery. Test cell consisting of $LiCoO_2$ as a cathode and mesophase pich-based ca.bon fiber (MCF) as an anode material showed a capacity of 110 mAh/g based on the cathode weight at 0.2C rate at room temperature. Over $80\%$ of initial capacity was retained after 400cycles, indicating that GFC is suitable for a reinforcing material to increase the mechanical strength of gel based electrolytes.

• Journal of Soil and Groundwater Environment
• /
• v.10 no.5
• /
• pp.11-17
• /
• 2005

Characteristics of phenanthrene removal in the Electrokinetic (EK)-Fenton process were investigated in a 2-dimensional test cell in a viewpoint of the effect of gravity and electrosmotic flow (EOF). When the constant voltage of 100 V was applied to this system, the current decreased from 1,000 to 290 mA after 28 days, because soil resistance increased due to the exhaustion of ions in soil by electroosmosis and electromigration. Accumulated EOF in two cathode reservoirs was 10.3 L and the EOF rate was kept constant for 28 days. At the end of operation, the concentration of phenanthrene was observed to be very low near the anode and increased in the cathode region because hydrogen peroxide was supplied from anode to cathode region following the direction of EOP. Additionally, the concentration of phenanthrene decreased at the bottom of the test cell because the electrolyte solution containing hydrogen peroxide was largely transported toward the bottom due to a low capillary action in the soil with high porosity. Average removal efficiency of phenanthrene by EK-Fenton process was 81.4% for 28 days. In-situ EK-Fenton process would overcome the limitations of conventional remediation technologies and effectively remediate the contaminated sites.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.4
• /
• pp.268-272
• /
• 2008

$LiFePO_4$ material was synthesized by electrospinning method to obtain optimal particle size($50{\sim}100\;nm$) without carbon coating or ball milling. This material showed an orthorthombic structure with Pnma space group without any impurities, such as FeP or $Fe_2P$, in the XRD pattern. The particle morphology and particle shape were observed by SEM analysis. Li/$LiFePO_4$ cell showed a high initial discharge capacity of 135 mAh/g, at current density of $0.1\;mA/cm^2$ with a cut-off voltage of 2.8 to 4.0V. This cell exhibited a perfect cycle performance over 99.9% cycle retention rate up to 50 cycles.

• Journal of Sensor Science and Technology
• /
• v.10 no.5
• /
• pp.292-303
• /
• 2001

This work reports the tunneling effects of the lateral field emitters. Tunneling effect is applicable to the VMFS(vacuum magnetic field sensors). VMFS uses the fact that the trajectory of the emitted electrons are curved by the magnetic field due to Lorentz force. Polysilicon was used as field emitters and anode materials. Thickness of the emitter and the anode were $2\;{\mu}m$, respectively. PSG(phospho-silicate-glass) was used as a sacrificial layer and it was etched by HF at a releasing step. Cantilevers were doped with $POCl_3(10^{20}cm^{-3})$. $2{\mu}m$-thick cantilevers were fabricated onto PSG($2{\mu}m$-thick). Sublimation drying method was used at releasing step to avoid stiction. Then, device was vacuum sealed. Device was fixed to a sodalime-glass #1 with silver paste and it was wire bonded. Glass #1 has a predefined hole and a sputtered silicon-film at backside. The front-side of the device was sealed with sodalime-glass #2 using the glass frit. After getter insertion via the hole, backside of the glass #1 was bonded electrostatically with the sodalime-glass #3 at $10^{-6}\;torr$. After sealing, getter was activated. Sealing was successful to operate the tunneling device. The packaged VMFS showed very small reduced emission current compared with the chamber test prior to sealing. The emission currents were changed when the magnetic field was induced. The sensitivity of the device was about 3%/T at about 1 Tesla magnetic field.

• Journal of the Korean Applied Science and Technology
• /
• v.33 no.1
• /
• pp.83-91
• /
• 2016

We studied the effect of battery deep cycle according to the way of active materials formation and the creation condition of electrode material, 3BS ($3PbO{\cdot}PbSO_4{\cdot}H_2O$) and 4BS ($4PbO{\cdot}PbSO_4$), in order to develop the batteries for Idle Stop & Go system. During the curing with active materials of anode and cathode, we found that the final creased active material was deformed by temperature control and it effects the durability of batteries. AGM battery and Flooded battery with 3BS active materials have excellent initial performance. And AGM battery with 4BS active materials shows the lower performance relatively. To compare and analyze of the formation efficiency of active materials, we tested the formation chagging steps with 3 steps and 9 steps differently. The results are that AGM battery with 4BS active materials is better on initial performance than AGM battery with 3BS. After the comparison of durability by DOD 17.5% life test, AGM battery is more suitable than flooded battery for the ISG system which needs the frequent deep cycle. In conclusion, AGM battery is the most suitable for ISG system and the life performance shows 80% difference according to the way of formation and curing of AGM batteries.

• Journal of the Korea Organic Resources Recycling Association
• /
• v.11 no.4
• /
• pp.120-129
• /
• 2003

The anodic alumina is synthesized using 0.3M oxalic acid and the barrier layers of the anodic alumina are removed using the 20wt% $H_2SO_4$ solution. The structure of the anodic alumina is analyzed by XRD and SEM. It is observed by SEM that the size of anodic alumina pore is about 60nm. And the uniformity of the anodic alumina surface under the 20wt% $H_2SO_4$ solution is poorer than the unifomity of the the normal anodic alumina surface. The anodic alumina and the carbon are used cathode and anode in$Cd(NO_3)_2{\cdot}4H_2O$, $Co(NO_3)_2{\cdot}6H_2O$ and $PbSO_4$ solutions. In this study, the constant D.C. electrical current is flowed in each solution for 24hours. It is found that the voltages so far as 4.6, 3.4 and 5.1V at $Cd(NO_3)_2{\cdot}4H_2O$, $Co(NO_3)_2{\cdot}6H_2O$ and $PbSO_4$ solutions increase with increasing the flowing current time and after the voltage does not change which values are 4.2, 2.7 and 2.4V, respectively. The amount of metal ions in solutions decrease with increasing the flowing current time until the flowing current time is 18hours and the metals are formed at the surface of anodic alumina. After the metal ions are removed using the anodic alumina, and $Cd^{2+}$, $Co^{2+}$ and $Pb^{2+}$ ions are removed again using flow cell with retriculate vitreous carbon(RVC) working electrode. The concentration of $Cd^{2+}$, and $Co^{2+}$ions decrease until the flowing time of the solutions is 20minutes and the concentration of $Pb^{2+}$ ion decreases until that time is 30minutes. In this case, the removal effects of $Cd^{2+}$, $Co^{2+}$ and $Pb^{2+}$ ions are 34.78, 28.79 and 86.38%, respectively. And it is possible that both $Cd^{2+}$ and $Co^{2+}$ions are adsorbed in pore of RVC at the same time and the removal effects of $Cd^{2+}$ and $Co^{2+}$ions are 32.30 and 31.37%.

• Journal of the Korean Electrochemical Society
• /
• v.14 no.4
• /
• pp.231-238
• /
• 2011

In this work, the numerical analysis for the zincate behavior at a zinc electrode with an electrolyte flow was carried out for a ZAFC. The Nernst-Planck equation with a boundary condition of Butler-Volmer type was adopted to describe electrochemical effects of mass transfer, migration, kinetics of electrode. The Navier-Stokes equation, coupling to the Nernst-Planck equation, is also applied to describe the internal electrolyte flow fields. The validity of the numerical model is proved through the comparative analysis between numerical and experimental results. The concentration of zincate and the current density were also investigated at a zinc anode according to various electrolyte velocities. We have found the concentration of zincate decreased and the current density increased with an increase in the electrolyte velocity.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.313-313
• /
• 2009

OLED 소자는 직접발광, 광시야각, 그리고 빠른 응답속도 때문에 동영상에 적합하여 최근 각광받고 있는 디스플레이장치 중의 하나이다. OLED 소자의 양극재료로는 높은 광투과율과 $\sim10^{-4}{\Omega}\;cm$ 수준의 낮은 전기 비저항을 갖는 ITO (Sn-doped $In_2O_3$)가 널리 사용되고 있다. 하지만 원료 물질인 인듐의 수급량 부족으로 인한 문제점과 독성, 저온증착의 어려움, 스퍼터링시 음이온 충격에 의한 막 손상으로 저항의 증가의 문제점이 있고, 또한 액정디스플레이의 투명전극으로 사용될 경우 $400\;^{\circ}C$정도의 높은 온도와 수소 플라즈마 분위기에서 장시간 노출 시 열화로 인한 광학적 특성변화가 문제가 된다. 반면에 Al이 도핑 된 ZnO (AZO)박막은 넓은 밴드갭 (3.37eV)와 400nm에서 700nm 사이의 가시광 영역에서 80% 이상의 우수한 투과성을 지니고 있다. 특히 Al이 도핑된 ZnO는 박막의 전기적 특성이 크게 향상되어 디스플레이나 태양전지로의 응용이 가능하다. 또한 비교적 낮은 비용과 플라즈마에서의 안정성, 무독성, 그리고 전기전도성과 같은 많은 이점이 있다. 그 결과 AZO 박막은 ITO기판을 대안하는 지원물질로 활발히 연구가 진행되고 있다. 본 연구에서는 TCO 박막의 면 저항과 표면 거칠기에 따른 OLED 소자의 특성을 분석하였다. ITO와 AZO 박막은 챔버 내 다양한 가스 분위기(Ar, Ar+$O_2$ and Ar+$H_2$)에서 R.F Magnetron Sputtering방법으로 증착하였다. TCO 박막의 구조적인 이해를 돕기 위해서 X-ray diffraction 과 FESEM으로 분석하였다. 광학적 투과도와 박막의 두께는 ultraviolet spectrophotometer (Varian, cary-500)와 surface profile measurement system으로 각각 측정하였다. 면저항 charge carrier 농도, 그리고 TCO 박막의 이동도와 같은 전기적특성은 four-point probe와 hall effect measurement(HMS-3000)로 각각 측정하였다. TCO 박막의 표면 거칠기 조절을 위해 photo lithography 공정을 사용하여 TCO 박막을 화학에칭 하였다. 미세사이즈 패턴 마스크가 사용되었으며 에칭의 깊이는 에칭시간에 따라 조절하였다. TCO 박막의 표면 형태는 FESEM과 AFM으로 관찰하였다. 투명전극으로 사용되는 ITO 및 AZO 기판 상용화를 위해 ITO 및 AZO 기판 위에 ${\alpha}$-NPB, Alq3, LiF, Al 의 순서로 증착 및 패터닝함으로써 OLED 소자를 제작하였다. 전류밀도와 전압 그리고 발광휘도와 전압과 같은 전기적 특성은 spectrometer(minolta CS-1000A)를 이용하여 측정하였다.

• Journal of the Korean Electrochemical Society
• /
• v.6 no.1
• /
• pp.6-12
• /
• 2003

Plasma carbon black(PB) which prepared by plasma pyrolysis of methane was treated at 800, 1300 and $2100^{\circ}C$ under $2\times10^{-2}$ torr. Four different samples including raw PB were added to $LiCoO_2$, cathode active material of lithium secondary battery, to investigate effects of properties of plasma black as conductors on electrochemical characteristics. Based on our experimental results, PB conductors with low amount of surface functional groups and high electrical conductivity enhanced the cyclability and the initial discharge capacity. However, deterioration of rate capability and cyclability were observed (or the plasma black treated at $2100^{\circ}C$ For the plasma black conductor prepared from plasma pyrolysis, the effects of properties of carbon black on electrochemical characteristics were combined results of changes in electrical conductivity and structural properties such as agglomeration of plasma black. The conductivity of plasma black increased with treatment temperature, while dispersion of plasma black decreased. As a result, the high cyclability of cell was observed at $800^{\circ}C$ of heat treatment temperature.

• Korean Chemical Engineering Research
• /
• v.59 no.3
• /
• pp.339-344
• /
• 2021

In order to improve the PEMFC (Proton Exchange Membrane Fuel Cell) durability, it is important to accurately evaluate the durability of the membrane in a short time. Recently, DOE (Department of Energy) reported a protocol that combines the chemical and mechanical durability of membranes to evaluate them effectively. This protocol applies chemical/mechanical deterioration to the membrane by repeating wet/dry while OCV (Open Circuit Voltage) holding. The problem of this protocol is that it is highly affected by electrode degradation due to change cycles in OCV and that the evaluation time is long. By using oxygen instead of air as the cathode gas while leaving the other conditions of the DOE protocol as it is, the durability evaluation time could be reduced from 408 hours to 144 hours. By reducing the number of voltage change cycles to 1/3, the electrode degradation due to the voltage change cycle was reduced to 1/12 when oxygen was used compared to air at the end, thereby enabling more accurate evaluation of polymer membrane durability.