• Journal of the Korean Geotechnical Society
• /
• v.24 no.11
• /
• pp.157-166
• /
• 2008

To investigate the relationship between compressive strength ($q_u$) of Lightweight Air-mixed soil (LAS) and its physical deformation coefficient ($E_{50}$), a series of unconfined compressive tests have been performed on specimens of LAS according to various dredged soil types by percentage of sand, silt and clay. From the results it was found that the cement content ($C_i$) and unit weight (${\gamma}_m$) are most influence factors on strength, and percentage of sand, silt, clay by grain size analysis (KS F2302) have more effect on compressive strength than other physical properties of soil. It was also found that the rate of strength (a) increases with curing time, but it reduces with the increase of percentage of clay ($C_%$).

• Journal of Korean Society of Coastal and Ocean Engineers
• /
• v.23 no.1
• /
• pp.1-10
• /
• 2011

Recently harbor remodeling projects are seriously considered to enhance the loading and unloading capability of old container terminals and to make decrepit ports as eco-friendly harbor and waterfront spaces in many countries. In such a case, quantitative and qualitative evaluations on concrete harbor facilities are mandatory to determine the current structural integrity condition of aged materials. Once the remodeling project is determined to be carried out, the reusability of individual structural members and facilities including caissons, cell-blocks, and tetra-pods need to be decided based on the simple and economic visual inspection and/or nondestructive testing. In this study, the systematic quantitative evaluation procedure for determining the structural integrity condition and the reusability is studied based the nondestructive testing and evaluation methods. Conventional methods including Schmidt hammer test and ultrasonicpulse velocity methods and elastic wave based methods including impact echo test and surface wave test are applied to the old harbor facilities in five different sites. The compressive tests are also carried out to determine the elastic modulus and compressive strength of concrete materials.

• Tunnel and Underground Space
• /
• v.22 no.5
• /
• pp.339-345
• /
• 2012

Information on the deformation behavior and fracture strength of rocks subjected to dynamic loadings is important to stability analyses of underground openings underground vibration due to rock blasts, earthquakes and rock bursts. In this study, Split Hopkinson Pressure Bar (SHPB) system was applied to estimate dynamic compressive and tensile fracture strengths of limestone and also examine deformation behavior of limestones under dynamic loadings. A micro-focus X-ray CT scanner was used to observe non-destructively inside the impacted limestone specimens. From the dynamic tests, it was revealed that the limestone have over 140MPa dynamic compressive strength and the strain-rate dependency of the strength. Dynamic Brazilian tensile strength of the limestone exceeds 21MPa and shows over 3 times static Brazilian tensile strength.

• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1066-1072
• /
• 1999

The physical properties of polymer concrete were investigated for development of high-performance construction materials. Various specimens of polymer concrete were prepared using unsaturated polyester resin as the polymer-binder with the various dosage of calcium carbonate as microfiller (5~20 wt %) and fine aggregate(10~50 wt %). For the evaluation of the physical properties of polymer concretes, tests such as compressive strength, flexural strength, water absorption test, hot water immersion test, acid resistance test and pore size distribution analysis were conducted. As a result, it is concluded that compressive and flexural strengths of polymer concretes increased up to 4 times than those of conventional cement concrete. Whereas the compressive and flexural strengths of polymer concretes tested after hot water immersion, compared with those of polymer concretes tested before hot water immersion, decreased about 67%, 47%, respectively. By hot water immersion, total pore volume and porosity(%) of polymer concretes were remarkable increased due to decomposition of polymer binder. And also, it is showed that water absorption(%) and weight loss(%) of polymer concrete specimens by acid immersion, compared with those of ordinary portland cement concrete, decreased about 1/100, 1/27, respectively.

• Proceedings of the Korean Society of Disaster Information Conference
• /
• 2016.11a
• /
• pp.319-321
• /
• 2016

본 논문에서는 지반함몰이 발생한 현장에 긴급복구를 위한 팽창기능제의 개발에 대한 내용이다. 현재 유동화토에 대한 기준이 없어 공동에 채워지는 채움재와 비슷한 압축강도인 0.3MPa을 기준으로 하여 흙의 일축압축시험 방법을 이용하여 실험을 진행하였다. 팽창기능제의 최적배합 실험과 팽창률에 따른 압축강도를 측정하여 뒤채움재로써의 기능 특성을 평가하였다. 실험결과, 팽창기능제 A의 경우 팽창률 750%이하에서 팽창기능제 B의 경우는 모든 실험체에서 목표 강도를 만족하였다.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.12 no.1
• /
• pp.109-116
• /
• 2008

In order to test the adhesive capacity of carbon fiber sheet, a static loading method for bending-behavior-type beam specimens, cut in half was developed and test was conducted with compressive strength of concrete set as the test parameter. The tests were performed to prescribe adhesive shear strength based upon the result of shear failure as well as verification of testing method. First of all, the test method proved to be reliable in determining the adhesive shear strength. The test result also exhibited two types of variations in adhesive shear strength. Among two types of variations, average and minimum values for adhesive shear strength, relatively stable results, 3.41MPa and 2.11MPa, respectively. Particularity in the adhesive shear strength with respect to compressive shear strength was not found.

• Proceedings of the KSR Conference
• /
• 2005.05a
• /
• pp.604-609
• /
• 2005

화강풍화토의 강도와 변형특성을 조사하기 위하여 불포화배수 삼축압축시험을 실시하였다. 0, 45, 90 이차압축시의 변형거동에 관한 시간의존성은 다짐각도와 관계가 없는 것으로 판단되었다. 다짐각도가 압축강도와 변형에 미치는 영향은 특히 낮은 구속압력시에 크다. 다짐각도가 다르다 하더라도 다일러턴시 비율은 다일러턴시로 인한 강도증가와 상관하여 변화한다. 따라서 다짐풍화토는 초기 비등방성 조직을 갖고 있는 모레와 같이 비등방성 역학적 성질을 갖는다고 할 수 있다.

• Tunnel and Underground Space
• /
• v.16 no.5 s.64
• /
• pp.405-412
• /
• 2006

It is well known that shotcrete is the most important support member for the construction of large underground spaces. Generally, the strength of the field shotcrete is heavily dependent on the field mixing and spraying conditions so that it is different from the strength of the shotcrete mixed in laboratories. As a support member, the early strength of shotcrete unlike concrete is very important to the initial stabilization of the underground spaces. Therefore, the field methods to efficiently test the early strength of shotcrete have been highly required. This paper aimed to verify the pneumatic pin penetration test and the point load test for measuring the early strength of the field shotcrete. As a result of the experiments through a series of uniaxial compression, pin penetration, and point load tests for the range of the early shotcrete strength, two equations to estimate reliably the uniaxial compressive strength by the pin penetration and the point load tests were acquired.

• Journal of the Society of Disaster Information
• /
• v.13 no.3
• /
• pp.348-357
• /
• 2017

In this study, we examined the physical properties of cement mortar by replacing a part of the amount of fine aggregate in moist mud flat. I analyzed the possibilities of using bricks. Flow measurement results show that the flow value increases as the mixing ratio of cement and fine aggregate increases and the flow value decreased as the replacement ratio of moist mud flats decreased. Chloride contents were also found to decrease with decreasing substitution rate of moist mud flats. As a result of the compressive strength measurement, the compressive strength increased in inverse proportion as the displacement ratio of moist mud flats decreased in most mixing ratio. As a result of tensile strength measurement, the tendency was similar to compressive strength and the intensity increased as the replacement ratio of moist mud flats decreased.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.1
• /
• pp.25-35
• /
• 2018

This study presents microstructural characteristics and strength properties of alkali-activated kaolin(K)-fly ash(FA) blends binders. The compressive strength, X-ray diffraction(XRD), thermogravimetric(TG) analysis and SEM/EDS were measured for hardened samples. The results were shown that all the samples had developed the compressive strength over time, regardless of replacement levels of K. It was found that when the amount of K increased, the strengths of samples decreased. In XRD result, no new crystalline phases were observed in all the hardened samples other than the crystalline components of raw FA and K, whereas TG analysis showed that N-A-S-H gel was formed as a reaction product in all the samples. Samples did not have the typical microstructure of dense, and there is little significant difference between the microstructures of the samples despite the differences in the strength testing results with replacement ratios of K. This study showed that the strength of sample was larger for lower Si/Al ratio of reaction product formed in sample. According to the correlation between Si/Al ratio and strength in this study, it is expected that if a chemical additive is used for lowering the Si/Al ratio of reaction product(i.e., increasing the $Al_2O_3$ solubility) in alkali-activated K-FA blends binders, strength improvement in K-FA blends binders could be achieved.