• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.29-36
• /
• 2017

The purpose of this study is to investigate experimentally the effect of types of alkali-activators and curing conditions on the compressive and tensile behavior of fiber-reinforced cementless composites. Two types of alkali-activators and two curing conditions were determined and density test, compressive strength test, and uniaxial tension test were performed. Test results showed that the cementless composite with sodium silicate showed higher performance in terms of strength, tensile strain capacity, and toughness than that with calcium hydroxide and sodium carbonate. The effect of curing conditions depends on the types of alkali-activators.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.2
• /
• pp.158-165
• /
• 2019

The purpose of this study is to investigate analytically the flexural behavior of beam reinforced by an alkali-activated slag-based fiber-reinforced composite. The materials and mixture proportion were selected to manufacture an alkali-activated slag-based fiber-reinforced composite with high tensile strain capacity over 7% and compressive strength and tension tests were performed. The composite showed a compressive strength of 32.7MPa, a tensile strength of 8.43MPa, and a tensile strain capacity of 7.52%. In order to analyze the flexural behavior of beams reinforced by ultra-high-ductile composite, nonlinear sectional analysis was peformed for four types of beams. Analysis showed that the flexural strength of beam reinforced partially by ultra-high-ductile composite increased by 8.0%, and the flexural strength of beam reinforced fully by ultra-high-ductile composite increased by 24.7%. It was found that the main reason of low improvement in flexural strength is the low tensile strain at the bottom of beam. The tensile strain at bottom corresponding to the flexural strength was 1.38% which was 18.4% of tensile strain capacity of the composite.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.3
• /
• pp.69-75
• /
• 2017

Ultra-high performance concrete and high ductile cementless composite are considered as promising construction materials because those exhibits higher performance in terms of high strength and high ductility. The purpose of this study is to investigate experimentally the compressive strength and tensile behavior of ultra-high performance concrete and high ductile cementless composite. A series of experiments including density, compressive strength, and uniaxial tension tests were performed. Test results showed that the compressive strength and tensile strength of alkali-activated slag based high ductile cementless composite were lower than those of ultra-high performance concrete. However, the tensile strain capacity and toughness of alkali-activated slag based high ductile cementless composite were higher than those of ultra-high performance concrete. And it was exhibited that a high ductility up to 7.89% can be attainable by incorporating polyethylene fiber into the alkali-activated slag based cementless paste.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.3
• /
• pp.260-267
• /
• 2021

The purpose of this study was to experimentally investigate the effects of curing methods on the compressive strength and tensile behavior of alkali-activated slag-based fiber-reinforced composite with a water-to-binder ratio of 15%. Three kinds of mixtures according to the curing conditions were prepared and compressive strength and tension tests were performed. Test results showed that the compressive strength and the first cracking strength of composites decreased when high temperature curing and air curing were adopted, while tensile strain capacity of composites increased. It was also observed that crack spacing and crack width of composites decreased by applying high temperature and air curing.

• Journal of Urban Science
• /
• v.9 no.1
• /
• pp.1-6
• /
• 2020

The thermoelectric characteristics of alkali activated slag composites containing multi-walled carbon nanotubes (MWCNT) was investigated in the present study. Three different MWCNT contents and exposed temperatures were considered, and their thermoelectric-related properties and internal structures were analyzed. It was found that the alkali activated slag composite with MWCNT 2.0 wt.% and the exposed temperature of 150℃ were the optimal condition to obtain the highest Seebeck coefficient and power factor. Based on the feasibility study, the extended size thermoelectric module with 130 elements was fabricated, and tested the electricity production capacity. Consequently, the present thermoelectric module produced 30.83 ㎼ of electricity at ∆T=178.4℃.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.3
• /
• pp.255-261
• /
• 2019

The purpose of this study is to investigate effects of types of synthetic fibers on mechanical properties of alkali-activated slag composite. Materials and mixture proportion for matrix are determined, and the compressive strength, tensile performance, and cracking patterns of three composites reinforced by polypropylene, polyvinyl-alcohol, and polyethylene fibers. From the test results, it was observed that polyvinyl-alcohol fiber-reinforced composite and polyethylene fiber-reinforced composite had similar tensile performance. On the other hand, polypropylene fiber-reinforced composite showed low tensile performance. And it was exhibited that other factors except tensile strength and aspect ratio of fiber influence significantly tensile behavior of composite.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.9 no.2
• /
• pp.200-207
• /
• 2021

The purpose of this study is to investigate experimentally the effects of type of superplasticizer on tensile behavior and cracking pattern of alkali-activated slag-based cementless composite. Three mixtures were prepared according to type of superplasticizer, and the compressive strength and tension tests were performed. Test results showed that differences of tensile strength, tensile strain capacity, and toughness of composites were up to 28.1%, 39.1%, and 66.2%, respectively, according to type of superplasticizer, although fiber balling or poor dispersion of fibers in fresh composites was not observed. It was also observed that the type of superplasticizer influenced number of cracks and maximum fiber bridging stress.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.3
• /
• pp.160-166
• /
• 2018

The purpose of this study is to investigate experimentally the effects of aspect ratio of polyethylene fiber on the compressive strength and tensile behavior of alkali-activated cementless composite. Two mixtures were determined according to aspect ratio values of polyethylene fibers, and the compressive strength and tension tests were performed. Test results showed that the effect of aspect ratio of fiber on the compressive strength was negligible and the tensile strength, ductility, and number of cracks of the mixture including the fiber with high aspect ratio were higher than those of the mixture including the fiber with low aspect ratio. On the other hand, the crack spacing and crack width were low in the mixture including the fiber with high aspect ratio.

• Journal of the Korea Institute of Building Construction
• /
• v.9 no.4
• /
• pp.63-73
• /
• 2009

Recently, the use of lightweight panels in building structures has been increasing. Of the various lightweight panel types, styrofoam sandwich panels are inexpensive and are excellent in terms of their insulation capacity and their constructability. However, sandwich panels that include organic material are quite vulnerable to fire, and thus can numerous casualties in the event of a fire due to the lack of time to vacate and their emission of poisonous gas. On the other hand, lightweight foamed concrete is excellent, both in terms of its insulation ability and its fire resistance, due to its Inner pores. The properties of lightweight concrete is influenced by foaming agent type. Accordingly, this study investigates the insulation properties by foaming agent type, to evaluate the possibility of using light-weight foamed concrete instead of styrene foam. Our research found thatnon-heating zone temperature of lightweight foamed concrete using AP (Aluminum Powder) and FP (animal protein foaming agent) are lower than that of light-weight foamed concrete using AES (alkyl ether lactic acid ester). Lightweight foamed concrete using AES and FP satisfied fire performance requirements of two hours at a foam ratio 50, 100. Lightweight foamed concrete using AP satisfied fire performance requirements of two hours at AP ratio 0.1, 0.15. The insulation properties were better in closed pore foamed concrete by made AP, FP than with open pore foamed concrete made using AES.

• Journal of the Korean GEO-environmental Society
• /
• v.15 no.3
• /
• pp.33-40
• /
• 2014

In this paper, mechanical and germination characteristics of stabilized dredged soils were investigated to recycle dredged soil in eco-friendly manner such as waterfront construction. Non sintering binder (NSB), which was developed by using interchemical reactions between slag, high-calcium fly ash, alkali activator on the dredged marine clay, was added to dredged soil. Ordinary portland cement was also used for the comparison of two binders. Experimental tests such as flow test and unconfined compressive test were carried out to evaluate characteristics of stabilized dredged soil. Leaching test, pH measure, vegetation germination test were also conducted to consider environmental applicability. The unconfined compressive tests shows that unconfined compressive strength (UCS) also increases with the increase of curing time and mixed ratio. UCS of NSB mixtures were higher than those of OPC mixtures. Germination tests showed that germination and sprouting date are better in NSB mixture than OPC mixture. It can be explained that germination decreased as pH and 7-day strength increased.