• Applied Chemistry for Engineering
• /
• v.29 no.3
• /
• pp.258-263
• /
• 2018

This study attempted to utilize ultrafine precipitated calcium carbonate for fluoride removal from the wastewater of electronics industries. An average particle size of the calcium carbonate was $0.96{\mu}m$, and pH of the aqueous slurry was 10 with 70% in mass. The suspension solution showed approximately 2 mL/hr of the sedimentation rate. The present calcium carbonate solution could be comparable to the conventional aqueous calcium source, $Ca(OH)_2$, for the neutralization and removal of fluoride ions. Depending on the amount of an additional alkali source, less amounts of test Ca-source slurries were required to reach the solution pH of 7.0 than that of using the aqueous calcium hydroxide. It was also found from XRD analysis that more calcium fluoride precipitates were formed by the addition of calcium carbonate solution rather than that of calcium hydroxide. In addition, Minteq equilibrium modelling estimated various ion complexes of fluoride and calcium in this process.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.2 no.2
• /
• pp.135-143
• /
• 2004

An experimental study on the sorption of U(VI) onto a Korean granite was performed as a function of the geochemical parameters such as contact time, pH, ionic strength, and carbonate concentration using a batch procedure. The distribution coefficient,$K_d$, was about 1-200 mL/g depending on the experimental conditions. The sorption of U(VI) onto granite particles was greatly dependent upon the contact time, pH, and carbonate concentration, but insignificantly dependent on the ionic strength. It was noticed that the sorption of U(VI) onto granite particles was highly correlated with the uranium speciation in the solution, which was dependent on the pH and carbonate concentrations. It was deduced from the kinetic sorption experiment that a two-step first-order kinetic behavior could dominate the kinetic sorption of U(VI) onto granite particles. In the alkaline range of a pH above 7, U(VI) sorption was greatly decreased and this might be due to the formation of anionic U(VI)-carbonate aqueous complexes as predicted by the speciation calculations.

• Journal of the Korean Applied Science and Technology
• /
• v.32 no.1
• /
• pp.116-126
• /
• 2015

The present study utilized a shuttle mechanism of wet chemical absorption using MEA. In addition, industrial by-products containing a large amount of inorganic alkali substances were utilized for wet carbonization process. Chemical pretreatment of industrial by-products extracted calcium ions. ICP result of calcium ion was obtained up to 17,900 ppm(17.9%) by acidic substance. And also, In this work, 94% of recovery rate was obtained using wet MEA absorption process from $CO_2$ flow at the ambient condition. Through the liquid carbonation process, a sludge was fixed with rate of 0.175 mg of $CO_2$ per mg of sludge. It was found from XRD results that the structure of final product was composed of a calcite structure which is general structure of $CaCO_3$.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.121-121
• /
• 2017

본 연구는 비전도성 폴리머 표면을 개질하여 감광성 금속을 유전체 표면에 흡착시키고, 감광성 금속의 광화학 반응을 이용하여 귀금속 촉매를 비전도성 폴리머 표면에 선택적으로 흡착시켜 무전해 Cu 도금을 수행하여 금속패턴을 형성하였다. 기능성 유연 필름은 일반적으로 투명한 플라스틱 고분자 기판을 기반으로 전기 전자, 에너지, 자동차, 포장, 의료 등 다양한 분야에서 폭넓게 활용 되고 있으며, 본 연구에서는 습식 도금 공정을 이용하여 폴리이미드 필름상에 $10{\mu}m$ 이하의 미세패턴을 형성하기 위한 공정을 개발하고자 하였다. 비전도성 폴리머 표면에 무전해 도금을 위해서 우선 폴리머 필름의 표면을 개질하는 공정이 필요하다. 이에 KOH 또는 NaOH 알카리 용액을 이용하여 표면을 개질하였으며 개질된 표면에 감광성 금속이온의 흡착시키기 위한 감광성 금속이온은 주석을 사용하였으며, 주석 용액의 안정성 및 퍼짐성 향상을 위해 감광성 금속 용액의 제조 및 특성을 관찰하였으며, 감광성 금속화합물이 흡착된 비전도성 유전체 표면을 포토마스크를 이용하여 특정 부위, 즉 표면에 금속패턴 층을 형성하고자 하는 곳은 포토마스크를 이용하여 광원을 차단하고 그 외 부분은 주 파장이 365nm와 405nm 광원을 조사하여 선택적으로 감광성 금속화합물의 산화반응을 유도하는 광조사 공정을 수행하였다. 광원이 조사되지 않은 부분에 귀금속 등의 촉매 입자를 치환 흡착시켜 금속 패턴이 형성될 수 있는 표면을 형성하였다. 위의 활성화 공정이후에 활성화 처리된 표면을 세척하는 수세 공정을 거친 후 무전해 도금공정에 바로 적용할 경우 미세한 귀금속 입자가 패턴이 아닌 부분 즉 자외선(UV) 조사된 부분에도 남아있어 도금시 번짐 현상이 발생한다. 이에 본 연구에서는 활성화 처리 후 약 알칼리 용액에 카르복실산을 혼합하여 잔존하는 귀금속 입자를 제거한 후 무전해 Cu 도금액을 이용하여 $10{\mu}m$ 이하의 Cu 금속 패턴을 형성하였다.

• Applied Chemistry for Engineering
• /
• v.23 no.3
• /
• pp.284-288
• /
• 2012

This work deals with the chemical characterization of glycine aqueous solution in $CO_2$ absorption. Three alkali elements were impregnated into the glycine in order to facilitate the formation of amino functionalities. The analysis by IR revealed the transformation of ammonium ions to the amino group. In addition, the NMR analysis showed that the substitution of metal cations to the chemical shift of hydrogen and carbon atoms in glycine; in order of lithium glycinate, sodium glycinate and potassium glycinate depending on the electro negativity. Meanwhile, the $CO_2$ absorption at room temperature was the highest in primary amine solution, but at the increasing temperature sodium glycinate could capture more $CO_2$ than that of the pure amine solution.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.10 no.1
• /
• pp.48-55
• /
• 2022

This study uses the recovered water as mixing water and artificial lightweight aggregate pre-wetting water as part of a study to increase the recycling rate and reduce greenhouse gas of the ready-mixed concrete recovered during the concrete transport process, and cement fine powder of blast furnace slag(BFS) and fly ash(FA). The engineering characteristics of the three-component lightweight aggregate mortar used as a substitute were reviewed. For this purpose, the flow, dry unit mass, compressive strength, drying shrinkage, neutralization depth, and chloride ion penetration resistance of the three-component lightweight aggregate mortar were measured. When used together with the formulation, when 15 % of BFS and 5 % of FA were used, it was found to be positive in improving the compressive strength and durability of the mortar.

• Membrane Journal
• /
• v.32 no.6
• /
• pp.496-513
• /
• 2022

In this study, we sought to verify the applicability of anion exchange membrane water electrolysis system using FAA-3-50, Neosepta-ASE, Sustainion grade T, and Fujifilm type 10, which are commercial anion exchange membranes. The morphology of the commercial membranes and the elements on the surface were analyzed using SEM/EDX to confirm the distribution of functional groups included in the commercial membranes. In addition, mechanical strength and decomposition temperature were measured using UTM and TGA to check whether the driving conditions of the water electrolyte were satisfied. The ion exchange capacity and ion conductivity were measured to understand the performance of anion exchange membranes, and the alkaline resistance of each commercial membrane was checked and durability test was performed because they were driven in an alkaline environment. Finally, a membrane-electrode assembly was manufactured and a water electrolysis single cell test was performed to confirm cell performance at 60℃, 70℃, and 80℃. The long-term cell test was measured 20 cycles at other temperatures to compare water electrolysis performance.

• Transactions of the Korean hydrogen and new energy society
• /
• v.34 no.2
• /
• pp.132-140
• /
• 2023

In this study, rotary magnet holder (RMH) was manufactured to analyze the ion transport effect according to the rotating magnetic field for the hydrogen production efficiency by alkaline water electrolyte. In the experiment, the voltage signal according to the magnet arrangement inside the RMH, the rotation speed, and the rotation time was measured using the voltage measurement module. As a result of the voltage signal measurement experiment, the average potential difference increased as the rotation speed of the RMH increased. Through the results of the voltage signal measurement experiment, the most efficient magnet arrangement (case 2) was applied to the RMH to conduct a water electrolysis experiment. A 20% NaOH aqueous solution was filled in the electrolytic cell, and a direct current 2 V constant voltage was applied to measure the current value according to the RMH rotation to compare the hydrogen generation amount. When rotating at 100 RPM, the hydrogen production efficiency increased by 8.06% compared to when not rotating. Considering the area exceeding +25 mA, which was not measured at the beginning of the experiment, an increase in hydrogen production of about 10% or more can be expected.

• Transactions of the Korean hydrogen and new energy society
• /
• v.33 no.1
• /
• pp.19-27
• /
• 2022

A series of QPAE/TiO₂-x (x = 1, 4, 7 and 10 wt%) organic/inorganic composite membranes were prepared as electrolyte membranes for alkaline anion exchange membrane fuel cells by controlling the content of inorganic filler with quaternized poly(arylene ether) (QPAE) random copolymer. Among the prepared QPAE/TiO₂-x organic/inorganic composite membranes, the highest ionic conductivity was 26.6 mS cm^-1 at 30℃ in QPAE/TiO₂-7 composite membrane, which was improvement over the ionic conductivity value of 6.4 mS cm^-1 (at 30℃) of the pristine QPAE membrane. Furthermore, the water uptake, swelling ratio, ionic exchange capacity, and thermal property of QPAE/TiO₂-x composite membranes were improved compared to the pristine QPAE membrane. The results of these studies suggest that the fabricated QPAE/TiO₂-x composite membranes have good prospects for alkaline anion exchange membrane fuel cell applications.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.614-623
• /
• 1993

Electrical characteristics of LiF-$Li_{2}O-B_{2}O_{3}-P_{2}O_5$ glasses with fixed $Li_2O$ content have been investigated by using AC impedance spectroscopy. Part of the total lithium ions present in these glasses contributes to conduction, and the changes in electrical conductivity with composition was inconsistent with the weak electrolyte model. The power law could not be used to determine the hopping ion concentration in these glasses. Both mobile carrier density and mobility have been modified as Li were added in the form of LiF. The formation of $(B-O-P)^-,di^-$, and metaborate group gave additional available sites for Li+ diffusion causing the enhancement of conductivity. The observed maximum conductivity was $2.43 \times 10^{-4}$S/cm at $150^{\circ}C$ at the composition containing 8mol% LiF. The decomposion potential amounted to 5.94V. The Li/glass electrolyte/$TiS_2$ solid-state cell showed open circuit voltage of 3.14V and energy density of 22 Wh/Kg at $150^{\circ}C$.