• Textile Coloration and Finishing
• /
• v.11 no.5
• /
• pp.22-29
• /
• 1999

The increase in color depth of polyester fiber dyed with black disperse dyes was investigated with respect to the kinds of resins and alkali treatment. The color depth of the dyed polyester fiber increased continuously according to the concentration of resins coated onto the fabrics. The alkali treatment to polyester fiber before dyeing also enhanced the color depth. It was thought that the polyester fiber was hydrolyzed by alkali resulting micropores on the sample. And the following treatment with a resin, Jet Black T-101, to the polyester fiber increased the color depth much higher. The successive process of alkali treatment, dyeing and Jet Black T-101 treatment could give the best color depth to polyester fiber. Although the alkali treatment reduced the tensile strength of polyester fiber, the color depth of polyester fiber enhanced sufficiently within the range of practically acceptable weight loss and strength. To analyze the micropore on the polyester fiber formed by alkali treatment, nitrogen porosimeter was used. As the weight loss of polyester fiber treated with alkali increased, the BET(Brunauer-Emmett-Teller) surface area, total pore volume, and average pore size of the sample increased.

• Textile Coloration and Finishing
• /
• v.12 no.6
• /
• pp.380-388
• /
• 2000

The porosity of polyester fibers treated with sodium hydroxide aqueous solution was investigated using a nitrogen porosimeter, and the dyeability of the treated fibers was discussed in terms of the porosity. In pore distribution, the polyester fibers treated with sodium hydroxide aqueous solution were characterized by higher amount of pores below $10\AA$ than those of the untreated fibers, and by shift of the pore size having maximum accumulated volume from $10\AA$ for the untreated fibers to $5~6\AA$. As the weight loss of the polyester fibers treated with sodium hydroxide aqueous solution increased, BET surface area and total pore volume increased linearly, but average pore size, showing some different aspect, increased steeply at earlier stage and then approached the maximum value. The dye uptakes of the polyester fibers treated with sodium hydroxide aqueous solution increased with the BET surface area, the total pore volume and the average pore size. The alkali treatment increased the surface area of polyester fibers, so that the chance of contact between the fiber and dye molecules increased. In addition, the pores created on the surface of polyester fibers by alkali treatment might act as pathways for dye molecules into the polyester fibers.

• Proceedings of the Korean Society of Dyers and Finishers Conference
• /
• 2011.03a
• /
• pp.37-37
• /
• 2011

열가소성 고분자 물질인 PET[poly(ethylene terephthalate)]는 섬유 및 필름, 음료병 등에 널리 사용되는 대표적인 범용 소재이며, 전체 PET 제조업은 2013년 약 200억불에 달할 것으로 예상되는 큰 시장이다. 최근 급격한 산업화에 따른 전 세계적인 환경오염의 심각성이 부각되면서 기업들의 환경 친화적인 제조 활동 및 생산 프로세스의 개선이 요구되고 있다. 현재 폴리에스테르 수지를 제조하기 위해 국내외 업체에서 가장 널리 사용 되고 있는 중합촉매는 중금속 원소인 고순도 삼산화안티몬($Sb_2O_3$)이며 통상 중합공정 중에 150~300ppm의 촉매가 사용된다. 세계보건기구(WHO)의 국제암연구기관(IARC)에서는 안티몬을 인체 발암성이 있는 물질로 분류 하여 현재 유럽을 중심으로 안티몬 사용을 제한하는 환경 규제가 가속화 되고 있다. 폴리에스테르 수지 제조 공정중 안티몬 촉매를 사용할 경우 정련, 염색, 알칼리 감량시 중금속(안티몬)검출에 따른 수질 오염 및 폐수처리비용이 증가하게 되며 대량의 중합촉매 사용에 따른 이물 증가로 작업성 및 품질 문제가 상존하게 된다. 따라서 이러한 제조 공정중의 고위험성 물질을 대체할 친환경, 고부가가치 신규 무독성 PET 소재 및 제품이 각광을 받게 될 것이다. 이번 연구에서는 티타늄계(Ti-based) 무독성 촉매를 이용하여 PET 중합을 실시한 Sb-free PET원단의 염색특성을 알아보는 것으로 분산염료 3종 (Red, Yellow, Blue)으로 염색이 완료된 원단을 spectrophotometer 를 이용하여 L, a b값과 K/S값으로 측정하였다. 동일한 염색 조건을 위해 두 종류의 원단을 하나의 실린더에서 기존 PET 염색과 동일한 조건으로 염색을 실시하였으며 실험 결과 전반적으로 기존 PET와 유사한 염색 특성을 보였다. 염색견뢰도 평가에서도 Sb-free PET원단과 기존 PET원단의 세탁 견뢰도, 마찰 견뢰도, 일광 견뢰도를 비교 했을 시 두 원단 모두 4~5급으로 우수한 견뢰도를 나타내었다.

• Textile Coloration and Finishing
• /
• v.4 no.3
• /
• pp.65-73
• /
• 1992

To control the hydrolysis rate of PET fabric with NaOH, HCl and $CH_3$COOH(HAc), as regulating reagent, were added to the 0.5 M NaOH solution. The concentrations of acids in 0.5 M NaOH were varied. PET fabrics were treated with aqueous solutions of acids in 0.5 M NaOH under different conditions. The weight loss of PET fabric, the rate of hydrolysis, the apparent activation energy (E$_{\alpha}$), the handle value, the etched surface of treated PET fabric, and the effect of salts such as NaCl, $CH_3$COONa(NaAc), and NH$_4$Cl on the weight loss were discussed. Acids in the aqueous 0.5 M NaOH solution decreased the weight loss of PET fabric bacause of neutralization of OH- and the weight loss of PET fabrics treated with corresponding concentration of aqueous NaOH solution to the concentrations of the aqueous solutions of acids in 0.5 M NaOH was lower than that of PET fabrics treated with aqueous solutions of acids in 0.5 M NaOH. The addition of NaCl to aqueous NaOH solution accelerated the reaction of OH- with PET greatly, the addition of NaAc increased the weight loss slightly, but the addition of NH$_4$Cl decreased the weight loss. It was thought that the very remarkable result that NaCl in aqueous NaOH solution promoted the hydrolysis of PET with NaOH would contribute to the conservation of energy and NaOH in the weight loss finishing process of PET fabric. The etched surface and the handle value of treated PET fabric were independent of the difference in the kinds of acids and salts added.nd salts added.

• Proceedings of the Korean Society for Emotion and Sensibility Conference
• /
• 1999.11a
• /
• pp.157-161
• /
• 1999

본 연구에서 직물의 열, 수분 전달특성과 KES-FB의 역학적 특성치, 직물표면의 fractal dimension을 측정하여 주관적 의복 착용 쾌적감을 예측하고자 하였다. 실험의복에 사용된 직물은 면 100% 평직물, 면/PET 혼방직물, 피치가공된 면/PET 혼방직물, PET 100% 평직물, 알칼리 감량가공된 PET 100% 크레이프 직물이었으며, 실험의복의 형태는 긴 소매 셔츠로 하였다. 착용실험은 온도 29$\pm$0.5$^{\circ}C$, 상대습도 75$\pm$2%RH, 기류 0.15m/s를 유지하는 항온항습실에서 실시하였고 36명의 여성 피험자(20-23세)들이 참여하였다. 의복 착용감의 하위 구성차원을 파악하기 위해 실험결과를 요인분석한 결과 5 개의 요인으로 추출되었다. 제 1 요인은 체온상승, 수분특성과 관련이 있는 온열.발한감이었으며, 제 2 요인은 무게ㆍ두께감, 제 3 요인은 회복특성감, 제 4 요인은 표면접촉감, 제 5 요인은 온냉감으로 구성되었다. 직물의 표면특성을 정량화하는 방법으로 도입한 fractal dimension 의 분석값들과 종래의 가장 보편적으로 이용되어 온 KES_FB 의 표면 특성치들이 주관적 착용쾌적감 예측에 얼마나 기여하는지 비교해 본 결과, 표면접촉감은 fractal dimension, 접촉점들의 총면적, 접촉점들의 평균 axis ratio, MMD, SMD와 높은 상관을 나타내었다. 또한 종합적 착용쾌적감에 대해서는 SMD 를 제외한 척도들이 유의한 상관을 보였으며, 그 중에서도 fractal dimension 과 접촉점들의 총면적은 0.8 이상의 높은 상관을 나타내었다. 착용쾌적감을 예측하기 위한 회귀분석결과에서는 fractal dimension 만으로 쾌적감의 74%가 설명되었으며 공기 투과도를 첨가하면 두 변수로 $R^2$=.792가 되었다. 설명되는 누적분산값은 67.18%였다.주관적 평가의 결과와 객관적 평가 결과를 이용해 마직물의 태를 평가하는 산출식을 제시하였다. 태 평가치의 경우 16가지 특성치를 모두 넣는 방법과 stepwise 방법, 또 Kawabatark 사용한 순차적 군 회귀법의 세가지 방법의 회귀식 중 16가지 특성치를 모두 넣는 방법의 결정계수가 가장 높았다.tosterone농도는 107.7$\pm$12.0 pmol／l이었고, 남성의 타액내 농도는 274.2$\pm$22.1 pmol／l이었다. 이상의 결과로 보아 본 연구에서 정립된 EIA 방법은 RIA를 대신하여 소규모의 실험실에서도 활용할 수 있을 것으로 사려된다.또한 상실기 이후 배아에서 합성되며, 발생시기에 따라 그 영향이 다르고 팽창과 부화에 관여하는 것으로 사료된다. 더욱이, 조선의 ${\ulcorner}$구성교육${\lrcorner}$이 조선총독부의 관리하에서 실행되었다는 것을, 당시의 사범학교를 중심으로 한 교육조직을 기술한 문헌에 의해 규명시켰다.nd of letter design which represents -natural objects and was popular at the time of Yukjo Dynasty, and there are some documents of that period left both in Japan and Korea. "Hyojedo" in Korea is supposed to have been influenced by the letter design. Asite- is also considered to have been "Japanese Letter Jobcheso." Therefore, the purpose of this study is to look into the origin of the letter designs in t