• Applied Chemistry for Engineering
• /
• v.20 no.1
• /
• pp.52-61
• /
• 2009

In this study, TAPEH (t-amyl peroxy 2-ethyl hexanoate) was selected for the reaction initiator which is a core factor for developing acrylic polyol binder. Tone M100 (caprolactone acrylate), 4HBA (4-hydroxy butyl acrylate), and 2HEMA (2-hydroxy ethyl methacrylate) were used for hydroxy-monomers. To check the applicability of raw materials mentioned above into the binders of 2 components acrylic polyurethane paint and reduce the VOC, the reactivity and film performance by different kinds of aliphatic polyisocyanate hardeners which are already generalized were reviewed. As the Tin-based catalyst has been regulated, the comparison test of reactivity and performance between the conventional catalyst and non-toxic metal catalyst recommended as the alternative was conducted as well. As a result, we were able to obtain the basic data which are necessary for applying 2 components high solid polyurethane paint and also reached a conclusion that it can be applied for developing new paints in terms of high performance, workability and environmental care.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.160-161
• /
• 2021

To prepare polyurethane coatings for top coatings of automobiles, acrylic resins containing 75% of solids were synthesized by a radical polymerization. The viscosity of the acrylic resins was increased with increasing OH values. Crosslinked acrylic-urethane clear coatings were obtained by curing reaction between the synthesized acrylic resins and hexamethylene diisocyanate(HDI) trimer(Desmodur N-3600). The physical properties from the following studies were carried out : viscosity(Zahn cup #2), adhesion, pensil hardness, and 60° specular gloss. Various properties of the acrylic-urethane clear coatings as top coatings of mobile coat were evaluated on the coating specimens. Adhesion property to a substrate, 60° specular gloss, and pencil hardness of prepared paint showed quite good properties.

• Korean Chemical Engineering Research
• /
• v.55 no.5
• /
• pp.586-592
• /
• 2017

In this study, acrylic resins with solids content of 75% were prepared by addition polymerization of n-butyl acrylate (BA), methyl methacrylate (MMA), 2-hydroxypropyl methacrylate (HPMA) and acetoacetoxyethyl methacrylate (AAEM) monomers. At this time, the glass transition temperature ($T_g$) of the acrylic resin was changed to 20, 30 and $40^{\circ}C$, and the hydroxyl value (OH value) was changed to 60, 90 and 120. As a result, the viscosity of acrylic resin increased with increasing $T_g$ and hydroxyl (OH) value. The synthesized acrylic resin was designed to have a high cross-link density to maintain high elasticity and high durability. The crosslinked acrylic resin was used to prepare an acrylic urethane clear coating by curing reaction with a block isocyanate (Desmodur BL-3175). The physical properties of the clear paints were analyzed by measuring viscosity, adhesion, pencil hardness and $60^{\circ}$ specular gloss. Acrylic urethane clear coatings were prepared as specimens and evaluated for various properties to be applied as top coatings for coil coating. The prepared coatings were excellent in adhesion, excellent in $60^{\circ}$ specular gloss and pencil hardness, and eco-friendly.

• Journal of the Korean Applied Science and Technology
• /
• v.38 no.2
• /
• pp.476-487
• /
• 2021

To prepare acrylic resin coatings containing 70% of solids, we used n-butyl methacrylate(BMA), methyl methacrylate(MMA), 2-hydroxyethyl methacrylate(2-HEMA), and acetoacetoxyethyl acrylate(AAEA), caprolactone acrylate(CLA) as raw materials, the glass transition temperature(T_g) of acrylic copolymer was adjusted around 50 ℃. The viscosity and molecular weight of the acrylic resins was increased with increasing OH values. Di-tert-amyl peroxide was found to be the suitable initiator to get high-solids acrylic resins. The optimum reaction conditions found in the study are 5 wt% of initiator, 4 wt% of chain transfer agent, 4 hrs of dropping time, and 140 ℃ of reaction temperature. The structure of the synthesized resins were characterized by FT-IR and ¹H-NMR spectroscopy. Number average molecular weight of 1900~2600 and molecular wight distribution of 1.4~2.1 were obtained. Crosslinked acrylic urethane clear coatings were obtained by curing reaction between the synthesized acrylic resins and hexamethylene diisocyanate trimer(Desmodur N-3300), the equivalent ratio of NCO/OH was 1.2/1.0. The physical properties from the following studies were carried out: viscosity(Zahn cup #2), adhesion, drying time, pot-life, pensil hardness, and 60° specular gloss. Various properties of the acrylic urethane clear coatings were also evaluated on the coating specimens. Adhesion property to a substrate, drying time, pot-life, pencil hardness, and 60° specular gloss of prepared paint showed quite good properties. Futhermore, prepared paint containing 10% of CLA showed quite good properties for adhesion, low viscosity and high hardness.

• Proceedings of the KAIS Fall Conference
• /
• 2009.12a
• /
• pp.84-87
• /
• 2009

본 연구는 건축용 바닥재로 널리 이용되는 PVC 상재의 표면을 열에 의한 손상으로부터 보호하기 위하여 기존에 사용하는 광경화형 우레탄-아크릴 수지에 내열성(anti-cigar burning)을 향상시킨 광경화형 수성도료 개발에 관한 것이다. PVC 바닥상재용으로 사용되는 내열기능성이 없는 우레탄-아크릴 수지에 인계화합물을 주원료로 합성한 내열재, 구아니딘을 주원료로 합성한 내열재, 일시적 방염제로 사용되는 제 2인산암모늄을 수지의 양 대비 함량(wt%)을 10, 20, 30%로 변화하여 첨가한 후 배합하여 수지의 내열성을 향상시킨 코팅액을 제조하였다. 제조한 코팅액은 코팅층의 두께조절이 가능한 Bar-coating을 사용하여 PVC 바닥상재에 코팅한 후, 내열성, 부착력, 내화학성, 코팅두께 등의 코팅층 표면물성을 평가하였다. 연구결과, 수지에 인계화합물을 주원료로 합성한 내열재 30%를 혼합하여 제조한 코팅액을 Bar-coater No.12로 코팅한 코팅표면이 열에 의한 손상이 가장 적고, 부착력 100%, 내화학성 양호로 가장 좋은 물성을 보였다. 전반적으로 내열재 함량이 높고 코팅 두께가 두꺼울수록 내열성이 우수한 것으로 나타났다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.11 no.2
• /
• pp.608-613
• /
• 2010

This study is on development of UV-cured water soluble coating composition which have more improved anti-cigar burning to prevent a surface of PVC tile from damage of heat. To make an anti-cigar burning coating solution, thermostable agent that synthesize main materials phosphorus compound, guanidine and ammonium phosphate dibasic used temporary flame retardants, changing their contents from 10 to 30wt% against quantities of resin and compounded. After coating PVC tiles using bar-coating method that can adjust a thickness, we estimated surface properties of coated layer such as anti-cigar burning, adhesive power, chemical resistance, thickness of coating, and so on. Results showed that a coating composition added 30 wt% of phosphorus compound and coated with No.12 bar-coater had the best optimized surface property in anti-cigar burning effect, adhesive power and chemical resistance. Also, we could find anti-cigar burning effect was improved as thermostable agents content and coating thickness increased.