• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.689-692
• /
• 2008

HSC(High Strength Concrete) have superior properties well as improvement in durability compared with normal strength concrete. In spite of durability of HSC, explosive spalling of concrete is serious problem in structure safety. Therefore, Solving methods are required to control the explosive spalling. The properties of concrete are affected by changes of temperatures. Compressive strength and elasticity modulus were degraded depending on a rise of temperatures. Also, change in microstructure and dehydration of concrete subjected to high temperatures. This paper is concerned with change in microstructure and dehydration of the alumino silicate fire protection materials at high temperatures. The testing methods of fire protection materials in high temperature properties are make use of SEM, TG-DSC and XRD. From the experimental test results, influence of high temperatures on microstructure of alumino-silicate fire protection material was identified, including chemical dehydration of C-S-H and CH. The chemical dehydration of CH under various temperatures from to 450 to 600$^{\circ}$C has been measured using the TG-DSC. However, developed alumino silicate fire protection materials showed good stability in high Temperatures. Thus, the results indicate that it is possible to fireproof panels, fire protection of materials.

• Journal of the Korea Concrete Institute
• /
• v.19 no.4
• /
• pp.475-482
• /
• 2007

The property and applicability of the organic-inorganic synthesized penetrating and reinforcing agent, which is developed in order to improve durability of concrete structures and prevent deterioration that may occur as service years increased, are researched with experimental works. TEOS (tetra-ethoxyorthosilicate) and acrylate monomer are synthesized by the solution polycondensation method in order to formulate silicate with sol-gel process and improve durability of concrete. Additional substances such as isobutyl-orthosilicate is supplemented in order to improve the performance of the agent. After the developed organic-inorganic penetrating reinforcing agent penetrates, a flexible impact alleviating layer is formed with organic monomers as well as the agent strengthens concrete by filling up the internal pore of concrete with stable compounds after penetration. Penetrating and reinforcing agent can be applied as an effective life management method because it makes concrete more durable against the aging factors, such as chloride ion, carbonation, freezing-thawing, and compound aging.

• Applied Chemistry for Engineering
• /
• v.29 no.1
• /
• pp.112-116
• /
• 2018

In this study, the mixing characteristics of water glass and additives (Si, alkali metal), which are one of the main raw materials of silicate based binder used in the production of molds during casting process, were examined. Molecular structures of water glass, additives and mixtures were analyzed FT-IR and viscosity measurements and their correlation were compared. The addition of Si source to the water glass accelerated the Si networking in the material and increased the viscosity. When the alkali metal was added, the viscosity of the water glass decreased by suppressing the Si networking of the water glass. Viscosities of the water glass and lithium silicate (LS) mixtures increased when the content of LS was less than 20 wt% and gradually decreased when the content was more than 20 wt%. By adding KOH to the water glass, the viscosity could be lowered and it could be used effectively to mix with colloidal silica (CS) or potassium methyl siliconate (PMS).

• Journal of the Korean Ceramic Society
• /
• v.31 no.5
• /
• pp.572-580
• /
• 1994

With low thermal expansion coefficients, eucryptite (Li2O.Al2O3.2SiO2) and spodumene (Li2O.Al2O3.4SiO2) in LAS ceramic system show good thermal shock resistance. In this study, sillimanite or kaolin group silicate minerals and Li2CO3 were used as starting materials, and if necessary SiO2 or Al2O3 were added for making stoichiometrically formed specimens. By this process, eucryptite powders were synthesized and characterized. The powder mixtures of lithiumcabonate and silicate minerals calcined at 80$0^{\circ}C$ for 2 hrs were made into powder compacts. $\beta$-Eucryptite single phase was formed via intermediate phases of Li2SiO3 and LiAlO2 et al, by heating at 110$0^{\circ}C$ or 120$0^{\circ}C$ for 10 hrs from those powder compacts. When using the sillimanite group minerals, Virginia kyanite or andalusite was reacted to form eucryptite at 120$0^{\circ}C$and CMK International kyanite were completed at 110$0^{\circ}C$. When kaolin group minerals were used, it was found that the synthesizing temperature (100$0^{\circ}C$) of $\beta$-eucryptite from the mixture of New Zealand white kaolin was lower than that from Hadong pink kaolin (110$0^{\circ}C$). The Microstructure of systhesized powder showed the irregular lump shape such as densed crystallines.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.6
• /
• pp.486-490
• /
• 2012

$La_{7.33}Bi_2(SiO_4)_6O_2$ specimens were fabricated by standard solid-state synthesis route for solid oxide electrolytes. The calcined powders exhibited uniform particles with a mean particle size of about $28{\mu}m$. The room-temperature structure of $La_{7.33}Bi_2(SiO_4)_6O_2$ specimens was analyzed as hexagonal, space group P63 or P63/m, and the unit cell volume increased with increase a sintering temperature. The specimens sintered at $1,175^{\circ}C$ showed X-ray patterns of homogeneous apatite single phase without the second phase such as $La_2Si_2O_7$ and $La_2SiO_5$. The specimen sintered at $1,175^{\circ}C$ showed the maximum sintered density of 5.49 $g/cm^3$. Increasing the sintering temperature, total conductivities increased, activation energy decreased and the values were $1.98{\times}10^{-5}Scm-1$ and 1.23 eV, respectively.

• Membrane Journal
• /
• v.16 no.2
• /
• pp.144-152
• /
• 2006

Elastomer-clay nanocomposite membranes were prepared by melt intercalation mothod with internal mixer. We are used NMR, Ionomer, SEBS (Styrene Ethylene Butadien styrene Copolymer) as elastomer, and modified clay. Gas barrier property of the elastomer-clay nanocomposites membranes were investigated by a gas permeability of $CO_2,\;O_2,\;N_2$ at room temperature. Gas permeability through the elastomer-clay nanocomposite membranes increased due to increased tortuosity made by intercalation of clay in elastomer.

• Korean Chemical Engineering Research
• /
• v.44 no.4
• /
• pp.393-398
• /
• 2006

There have been a lot of works in order to develop an excellent adsorbent for separation of olefin and paraffin. In the present work, the adsorption characteristics of mesoporous MCM-41 containing silver ion for 1-butene and n-butane were studied. The adsorption ability for the 1-butene depending on thermal treatment were also investigated.MCM-41 exhibits much higher adsorption amounts for 1-butene as well as n-butane, compared to those of Ag/13X zeolite. In case of MCM-41 containing silver ion, the adsorption amount of 1-butene dramatically increased due to the ${\pi}$-complexation, whereas the adsorption amount of n-butane decrease. The Ag/MCM-41 after the thermal treatment at 373 K under evacuation exhibit the highest 1-butene/n-butane adsorption ratio, expecially at low pressure (100 Torr).

• Resources Recycling
• /
• v.27 no.3
• /
• pp.58-65
• /
• 2018

For the recycling of coal ash from the domestic circulating fluidized bed boilers, a lime-based sorbent with 0.2~0.4 mm size was prepared by using limestone powder and CFBC fly ash. Mixing a small amount of slaked lime in the lime-based absorbent lead the formation of calcium silicate on the surface of the particle and the strength of absorbent particle was improved. As a result of comparing the desulfurization characteristics, it was found that the conversion rate was about 10% higher than that of commercially available limestone desulfurization used in the furnace, which is confirmed that it can be used as a desulfurization absorbent.

• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.225-230
• /
• 1999

Low pressure metal organic chemical vapor deposition (LPMOCVD) of $Li_2O$ solid thin films from Li(DPM) in nitrogen-oxygen or argon-oxygen atmosphere was experimentally investigated by using a small hot wall tubular type reactor. XRD and ESCA analysis revealed that $Li_2CO_3$ film grew in nitrogen-oxygen atmosphere and $Li_2O$ grew in argon-oxygen atmosphere. The grown lithium oxide or carbonate reacted with silicon or silica base materials to produce silicates. The CVD model analysis by means of the well-known micro trench method and Monte Carlo simulation was not fully successful, but a set of data on gas phase reaction rate constant and surface reaction constant was obtained.

• Applied Chemistry for Engineering
• /
• v.5 no.4
• /
• pp.714-721
• /
• 1994

Titanium and zirconium-containing MFI type zeolites have been prepared hydrothermally. Incorporation of titanium or zirconium into the framework of zeolite has been demonstrated by XRD, FT-IR, $^{29}Si$ MAS NMR analysis, and the catalytic benzene hydroxylation or n-hexane oxidation was used for checking the properties of catalysts. Pure titania and zirconia powder showed no catalytic activity at all for these reactions but Ti and Zr modified zeolite had the high activities in both reactions. The catalytic activity strongly depended on the kind of solvents, and the conversion of benzene or n-hexane increased with the increasing content of Ti and Zr in zeolites.