• Polymer(Korea)
• /
• v.27 no.2
• /
• pp.120-128
• /
• 2003

The effects of catalyst, accelerator and blend composition on the cure behavior of unsaturated polyester resin (UPE), vinyl ester resin (VE) and their blends were studied using differential scanning calorimetry(DSC). The DSC thermograms strongly depend on each variable. The result shows that the small exothermic peak at 115$^{\circ}C$ is due mainly to the UPE component in the UPE/VE blends and the large one at 134~138 $^{\circ}C$ is due mainly to the VE component. The results also indicate that the change of the DSC thermogram measured after each blend was exposed to high temperature 18$0^{\circ}C$ and the fast curing conditions of a few tens seconds provide useful information on understanding the thermal processing of a blend at high speed. The measurements of resin flow time represent that there are three distinct stages of cure in the UPE/VE blends: induction, transition and macro-gelation stages, as similarly reported for UPE by others earlier. The thermal stability and flexural properties of the cured UPE are significantly improved by blending it with the VE, depending on the composition.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.547-553
• /
• 2017

Thermal analysis of three energetic materials used in pyroelectric device was performed using Differential Scanning Calorimetry (DSC). The theoretical method for extracting the reaction rate equation of energetic materials using DSC experimental data is proposed and the reaction rate extraction is performed. The results of the DSC were analyzed by the conversion method such as Friedman. Activation energy and frequency factor according to mass fraction were extracted to complete the reaction rate equation. The extracted reaction rate equation has a form that represents the entire chemical reaction process, not the assumption that the chemical reaction process of the high energy material is a main step in several stages. It has considerable advantages in terms of theoretical and accuracy as compared with the chemical reaction rate form extracted through conventional thermal analysis experiments. Using the derived reaction rate equation, we predicted the performance change of three energetic materials operating on actual storage condition over 20 years.

• Korean Journal of Materials Research
• /
• v.26 no.5
• /
• pp.235-240
• /
• 2016

Appropriate thermo-mechanical properties of nickel-based superalloys are achieved by heat treatment, which induces precipitation and solid solution hardening; thus, information on the temperature ranges of precipitation and dissolution of the precipitates is essential for the determination of the heat treatment condition. In this study, thermal analyses of nickel-based superalloys were performed by differential scanning calorimetry method under conditions of various heating rates of 5, 10, 20, or 40K/min in a temperature range of 298~1573K. Precipitation and dissolution temperatures were determined by measuring peak temperatures, constructing trend lines, and extrapolating those lines to the zero heating rate to find the exact temperature under isothermal condition. Determined temperatures for the precipitation reactions were 813, 952, and 1062K. Determined onset, peak, and offset temperatures of the first dissolution reaction were 1302, 1388, and 1406K, respectively, and those values of the second dissolution reaction were 1405, 1414, and 1462K. Determined solvus temperature was 1462K. The study showed that it was possible to use a simple method to obtain accurate phase transition temperatures under isothermal condition.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2017.05a
• /
• pp.172-178
• /
• 2017

Thermal property is one of the important characteristic in the field of energetic materials. As the energy material is released during decomposition, DSC(Differential Scanning Calorimetry) is frequently used for the thermal analysis. In case of the dynamic DSC measurements, thermal dynamic change like melting is prevented from the thermal property measurements. And due to the predicting kg scale, the conditions of the heat exchange with the environment significantly is changed. In this study, As the method to resolve the problem, we predict the thermal aging property using the AKTS thermokinetic program from DSC measurements which performed isothermal method. Predicting the thermal aging properties from ARC(Accelerating Rate Calorimetry) measurement, we compare two results.

• Polymer(Korea)
• /
• v.25 no.5
• /
• pp.649-656
• /
• 2001

Miscibility of poly(4-vinylpyridine) (P4VP) blends with poly(vinyl acetate-co-vinyl alcohol) (VAc-VAL copolymers) was investigated as a function of comonomer composition of VAc-VAL copolymers. Differential scanning calorimetry (DSC) and thermo-optical microscopic (TOM) analysis confirmed that P4VP is miscible with VAc-VAL copolymers containing more than 30 mole% VAL. Fourier transform inflated (FT-IR) spectroscopic analysis revealed that the strong intermolecular hydrongen bonding interaction between the vinylpyridine and VAL hydroxyl group was formed. Theoretical phase diagram was constructed by the calculation using the Association model, a thermodynamic model for hydrogen-bonded polymer blend systems developed by Coleman et al. The calculated theoretical binodal phase diagrams were in good agreement with the experimentally determined cloud point curves.

• Polymer(Korea)
• /
• v.33 no.4
• /
• pp.313-318
• /
• 2009

Copolyimides were synthesized from bis (3-aminophenyl) sulfone (APS) and 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) containing a fluorine substituent ($-CF_3$) with different mole ratios of 3,3',4,4'-diphenylsulfonetetracarboxylic dianhydride (DSDA) containing a sulfone group (-$SO_2$-). The PI films were obtained from poly (amic acid) (PAA) by solution casting through thermal imidization on a glass plate. Wide-angle X-ray diffraction (XRD), scanning electron microscopy (FE-SEM), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), universal tensile machine (UTM) measurements, and UV-Vis spectrometry were used to assess thermo-mechanical properties, morphology, and optical transparency. Thermal properties and optical transparency decreased with increasing DSDA mole fraction. In contrast, mechanical properties increased with increasing DSDA mole fraction. As compared to conventional PI films, however, the PI copolymer films in this work were found to exhibit better optical transparency.

• Polymer(Korea)
• /
• v.32 no.6
• /
• pp.580-586
• /
• 2008

Copolyimides were synthesized from 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) and 1,3-bis(3-aminophenoxy)benzene (BAPB) with different mole ratios of 2,2-bis[4-(4-aminophenoxy)pheny1]hexafluoropropane (BAPP). The solution cast film of poly(amic acid) (PAA) was heat treated at different temperatures to create copolyimide films. The PI copolymer films were found to exhibit good optical transparencies. The thermomechanical properties, morphology, and optical transparency of PI films were examined using fourier transform infrared spectroscopy (FT-IR), wide-angle X-ray diffraction (XRD), scanning electron microscopes (SEM), differential scanning calorimeter(DSC), thermo-gravimetric analyzer (TGA), universal tensile machine (UTM), and IN - Vis. spectrometer. The glass transition temperature ($T_g$), ultimate strength, and initial modulus linearly increased with increasing BAPP mole fraction. However, thermal stability($T_D{^i}$) of the copolyimide remains constant regardless of BAPP loadings. It was found, however, that the optical transparency decreases slightly upon increasing the BAPP content because of the formation of the charge transfer complexes.

• Polymer(Korea)
• /
• v.32 no.3
• /
• pp.256-262
• /
• 2008

Copolyimides containing pendant trifluoromethyl ($CF_3$) groups were synthesized from 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) and bis[4-(3-aminophenoxy)phenyl]sulfone (BAPS) with various concentrations of 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane(BAPP) to poly(amic acid)(PAA), followed by thermal imidization. These copolyimides were readily soluble in N,N'-dimethylacetamide (DMAc) and could be solution-cast into a flexible and tough film. The thermomechanical properties, morphology and an optical transparency of the copolyimide films were determined using differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), wide angle X-ray diffraction (XRD), scanning electron microscopy (SEM), universal tensile machine (UTM), and a UV-Vis spectrometer. The cast copolyimide films exhibited high optical transparency with a cut-off wavelength (${\lambda}_0$) of $275{\sim}319\;nm$ in UV-vis absorption and a low yellow index(YI) value of $3.65{\sim}10.37$. The thermo-mechanical properties of copolyimide films were enhanced linearly with increasing a BAPP content. In contrast, the optical transparency of the copolyimide films was found to get worse with increasing a BAPP content.

• Journal of the Korean Society of Propulsion Engineers
• /
• v.18 no.5
• /
• pp.35-42
• /
• 2014

Thermal analysis properties and adhesive properties of self-healing agents were evaluated through differential scanning calorimetry, reaction heat measurement, and adhesive shear test. D1E0, D3E1, D1E1, D1E3, and D0E1, depending on the mixing ratio of DCPD and ENB, were considered as self-healing agents. The amount of Grubbs' catalyst, depending on the type of self-healing agents, was varied from 0.1 wt% to 1.5 wt%. In the case of DCPD, the polymerization reaction occurred faster and the stabilized adhesive strength increased as the amount of catalyst increased; however, a large amount of catalyst was required. ENB had excellent reactivity with a small amount of the catalyst; however, high reaction heat was observed at the early stage of polymerization. Thermal analysis properties and adhesive properties of self-healing agents can be controlled by varying a mixing ratio of DCPD and ENB. Among the self-healing agents used for this study, the D3E1 would be one of the most preferable candidates with regard to maximum adhesive strength, reaching time to maximum adhesive strength, stabilized adhesive strength, and reaction heat.

• Resources Recycling
• /
• v.16 no.4
• /
• pp.40-46
• /
• 2007

This research constructed property analysis for an high additional value construction materials. We try to utilize by the addition material of soil stabilizer. It was described to the material properties analysis of a sludge. A sample used 4 kinds of filtration cake which occurs by 4 companies and 3 kinds of sludge before filtration. ph of a sludge, a particle analysis and a scanning electron microscope observation were performed. We analyzed on the chemical ingredient by XRF, the phase by XRD, observed and analyzed the thermo-property of the sludge and the amount of the volatile constituent by TG-DTA.