• Journal of Ocean Engineering and Technology
• /
• v.1 no.2
• /
• pp.67-73
• /
• 1987

The feasibility for a practical use of underwater wet arc welding process is experimentally investigated by using low hydrogen and high oxide type electrodes and TMCP steel plates. Main results are summarized as follows: 1)The absorption speed of the coated low hydrogen and high titanium oxide type eletrodes becomes constant after about 30 minutes in water, and more steeping time in water does not influnce welding arc behavior. 2) By bead appearance and X-ray inspection, the high titanium oxide type electrode is better than the low hydrogen type in underwater arc welding process. 3) The mechanical properties of underwater wet arc welds depend upon welding conditions more than those of in-air welds, and the optimum welding condition can be obtained. 4) Because of quenching effect by rapid cooling rate in underwater wet welding, the maximum hardness of HAZ is increased relatively higher in underwater wet welding, process.

• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2001.05a
• /
• pp.276-281
• /
• 2001

Wet Underwater arc welding process is inverstigated by using experimentally developed flux coated underwater arc welding electrode and SS400 steel plate of 12mm thickness as base metal. Two kinds of different flux covered wet arc welding electrode of 3.2mm diameter (UW-1, UW-2) are individually developed and one of the improved underwater welding electrode (UW-2) may be put to practical use for underwater arc welding process.

• Journal of Ocean Engineering and Technology
• /
• v.14 no.4
• /
• pp.56-61
• /
• 2000

This study has been performed for mechanical properties of underwater wet welding electrode with rolled steel (KR-RA) for ship structure, one kind (E 4313) of domestic covered arc welding electrode used in the air and two kinds (UWE-01, UWE-02) of underwater covered arc welding electrode experimentally developed on the same welding condition. The results obtained were as follows : The hardness value of underwater covered arc welding electrode (UWE-01) was about 8.3% lower than domestic covered arc welding electrode(E 4313) in heat affected zone of test of UWF-02 was lower about 4.5%. Tensile strengths of UWE-01 were about 0.9%, and those of UWE-02 were about 6.5% higher than those of domestic covered arc welding electrodes (E 4313) in test specimens. The impect value of UWE-01 were about 15.5%, and those of UWE-02 were about 21.7% highter than those of domestic covered arc welding electrodes(E 4313) in test specimens. So mechanical properties of the underwater arc welding electrode were improved by the composition ratios of covering materials.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.23 no.2
• /
• pp.61-65
• /
• 1987

In this study, the characteristics of TRC (tensile restraint crack) critical stress in the gravity type underwater wet welding process and in the in-air welding have been investigated for Y, y and 45$^{\circ}$r grooves using the KR Grade A-3 steel plates and the E4303 covered electrodes. The following results were obtained: (1) In the TRC tests, the initial critical stress of Y groove is higher than those of the 45$^{\circ}$r single bebel grooves in both in-air and underwater weldings, and the cold fracture sensitivity is higher in the underwater welding than in the in-air welding. (2) The hardness of underwater weld metal is the highest in heat affected zone is about Hk 365 in the in-air weld but Hk 670 in the underwater weld which is higher for cooling speed is more rapid, resulting in the lower critical stress by increase of fracture sensitivity. (3) The diffusible hydrogen quantity for 48 hours is about 18cc/100g-weld-metal in the in-air welding but 48cc/100g-weld-metal in the underwater welding. So that, in the case of underwater welding the diffusible hydrogen penetrates about 3 times more than that in the in-air welding.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.23 no.2
• /
• pp.15-15
• /
• 1987

In this study, the characteristics of TRC (tensile restraint crack) critical stress in the gravity type underwater wet welding process and in the in-air welding have been investigated for Y, y and 45°r grooves using the KR Grade A-3 steel plates and the E4303 covered electrodes. The following results were obtained: (1) In the TRC tests, the initial critical stress of Y groove is higher than those of the 45°r single bebel grooves in both in-air and underwater weldings, and the cold fracture sensitivity is higher in the underwater welding than in the in-air welding. (2) The hardness of underwater weld metal is the highest in heat affected zone is about Hk 365 in the in-air weld but Hk 670 in the underwater weld which is higher for cooling speed is more rapid, resulting in the lower critical stress by increase of fracture sensitivity. (3) The diffusible hydrogen quantity for 48 hours is about 18cc/100g-weld-metal in the in-air welding but 48cc/100g-weld-metal in the underwater welding. So that, in the case of underwater welding the diffusible hydrogen penetrates about 3 times more than that in the in-air welding.

• Journal of Advanced Marine Engineering and Technology
• /
• v.25 no.5
• /
• pp.1122-1129
• /
• 2001

Underwater wet arc welding process was experimentally investigated by using the six types of flux coated electrodes of 3.2 mm diameter and the KR-RA steel plate of 11 mm thickness as base metal. Two types of electrodes were domestic covered arc welding electrode(CR13, CR14) and another two types of wet welding electrodes(UWCS, TN20)were imported goods, and the other two type (UWX1, UWX2) were individually designed flux coated electrodes for experimental welding purpose. Main experimental results are summerized as follows: 1. It is ascertained that individually designed flux coated electrode(UWX1) could be used in practice with KR-RA steel plate for underwater wet arc bead welds. 2. Welding arc can be generated easily and considerably kept in stable using TN20 and UWX1 electrodes. 3. The micro Vickers hardness value and the portion of martensite in the HAZ were increased in all the electrodes by rapid cooling rate, but it is relatively maintain stable for UWCS, TN20 and UWX1 electrodes.