• The Journal of Korean Academy of Prosthodontics
• /
• v.46 no.5
• /
• pp.511-519
• /
• 2008

Statement of problem: An incompatibility between the initiator systems of self-curing composite resins and light-curing adhesives was supposed recently. Purpose: The purpose of the study was to evaluate the influence of activators for self/dual bonding on dentin shear bonding strengths. Material and methods: Fifty human molars were divided into 5 groups. A flat dentin surface was created for each tooth. A self-curing composite resin (Luxacore) was bonded with the following adhesives (n = 10); One-Step, Prime&Bond NT, AdheSE, Prime&Bond NT and AdheSE were also used in combination with activators. Shear bond strengths were measured after 24 hours of water storage. The specimens were loaded in shear in the Instron until failure at a 1 mm/min crosshead speed. Data were compared using one-way ANOVA and Tukey HSD test (${\alpha}$= 0.05). Results: The dentin adhesive systems in order of decreasing median bond strength were One-Step > Prime&Bond NT with activator, AdheSE with activator > Prime&Bond NT, AdheSE. Among adhesives, One-Step had the highest bond strength. Prime&Bond NT with activator had higher bond strengths than Prime&Bond NT that was used alone, and so was AdheSE. Conclusion: Shear bond strengths were increased in Prime&Bond NT and AdheSE when these were used with activators comparing used without activators. But using activators was not effective clinically comparing One-Step.

• The Journal of Korean Academy of Prosthodontics
• /
• v.34 no.4
• /
• pp.791-799
• /
• 1996

The purpose of this study was to compare the shear bond strength of adhesion bridge by various resin cements. One hundred and foully 1st premolars were used. The teeth were cut below 2mm from CEJ and the coronal portions were used. The coronal portions were embeded with the acrylic resin and trimmed with sic paper until the flat plane with ${\phi}$ 4mm above acrylic resin sticks in height 5mm were casted with nonprecious metal and the using surfaces were treated with sic paper from #200 to #1200 and polished with alminum oxide paste. And then, the using surfaces were sandblasted and treated with the electrochemical etching. The teeth were divided into three groups of fourty two each. In group I, teeth and specimens were cemented with Panavia 21 In group II, teeth and specimens were cemented with Superbond In group I, teeth and specimens were cemented with All-Bond & composite resin cement Each group was subdivided into three subgroups according to the storage period ; one-day storage, fifteen-day storage, and thirty-day storage. The special jig was made. Then, the specimen and jig were mounted to Instron Universal Testing Machine and the failure were measured. The results were as follows. 1. There was statisfically significant difference between the failure loads of group I and group II and III after one day storage(P<0.01), 2. There was statisfically significant difference between the failure loads of group II and group I and III and between group I and group III at fifteen day storage(P<0.01). 3. There was statisfically significant difference between the failure loads of group I and II and group III after thirty day storage(P<0.01). 4. There was statisfically significant difference between the failure loads of one day storage and fifteen and thirty days storages in group III (P<0.01).