• 대한기계학회논문집
• /
• 제13권5호
• /
• pp.901-910
• /
• 1989

본 연구에서는 2상계 스테인리스강의 모재 및 용접부에 대하여 대기중의 피로시험과 인공해수중의 부식피로 시험을 모재부와 용접부의 .alpha.,.gamma.상의 상비율 변화에 따른 조직의 변화 및 용접잔유응력의 영향이 크랙전파에 미치는 영향을 검토하였다. 응력-스트레인의 히스테리스곡선에서 균열닫힘 거동을 실측하고 이들의 결과로 부터 유효응력확대계수와 균열전파속도와 관계를 정리하여 이들의 문제를 해석하였다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 춘계학술대회 논문집
• /
• pp.117-124
• /
• 2002

The lightness of components required in automobile and machinery industry is requiring high strength of components. In particular, manufacturing process and new materials development for solving the fatigue fracture problem attendant upon high strength of suspension of automobile are actively advanced. In this paper, the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in high temperatures($100^{\circ}C,\;150^{\circ}C,\;180^{\circ}C$) was investigated with considering fracture mechanics. So, we can obtain followings. (1) Compressive residual stress is decreased in high temperature, that is, with increasing temperature. (2) The effect of compressive residual stress on fatigue crack growth behavior in high temperature is increased below ${\Delta}K=17{\sim}19MPa\sqrt{m}$. The fatigue crack growth rate is increased with increasing temperature. The fatigue life is decreased with increasing temperature. (3) The dependence of temperature and compressive residual stress on the parameters C and m in Paris' law formed the formulas such as equations (3),(4),(5),(6),(7),(8),(9),(10). (4) It was investigated by SEM that the constraint of compress residual stress for plastic zone of fatigue crack tip was decreased in high temperature as compared with room temperature.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2002년도 춘계학술대회 논문집
• /
• pp.281-287
• /
• 2002

Nowadays, many components used in machinery industry is required lightness and high strength. Therefore, the effects of compressive residual stress by shot-peening which is method to improve fatigue lift of spring steel (JISG SUP-9), which used in suspension of automobile, on fatigue crack growth characteristics was investigated with considering fracture mechanics. So, we can obtain followings 1. The fatigue crack growth rate on stage II is conspicuous with the size of compressive residual stress and is dependent on Paris equation. 2. Although the maximum compressive residual stress is deeply and widely formed from surface, fatigue life does not improve than when maximum compressive residual stress is formed in surface. 3. The threshold stress intensity factor range is increased with increasing compressive residual stress. 4. In fracture surface of fatigue crack growth it is investigated that compressive residual stress remarkably retards fatigue crack growth.

• Journal of Advanced Marine Engineering and Technology
• /
• 제27권1호
• /
• pp.82-90
• /
• 2003

Nowadays, many components used in machinery industry is required lightness and high strength. The shot-peening method is used in order to improve the fatigue life of spring steel(JIS G SUP-9) which is used in suspension of automobile. The compressive residual is induced in this shot-peening process. This paper investigated the effect of the residual compressive stress on the fatigue crack growth characteristics. Main results are summarized as follows. 1. The fatigue crack growth rate on stage II is conspicuous with the level of compressive residual stress and is dependent on Paris equation. 2. Although the maximum compressive residual stress is deeply and widely formed from surface, it does not improve the fatigue life comparing when maximum compressive residual stress is formed in surface. 3. The threshold stress intensity factor range is increased with increasing compressive residual stress. 4. In fracture surface of fatigue crack growth it is investigated that compressive residual stress remarkably retards fatigue crack growth.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.256-261
• /
• 2007

The purpose of this study is to investigate the effect of shot peening on the fatigue strength and fatigue life of two kinds of aluminum alloys. The fatigue strength behavior of aluminum alloys were estimated by the stress ratio and shot velocities. The fatigue life and strength increased with increasing the test shot velocity. However, at the shot velocity range between 50m/s and 70m/s, the compressive residual stress phenomena were observed in test conditions of different shot velocity. The optimal shot velocity is acquired by considering the peak values of the compressive residual stress, dislocations, brittle striation, slip, and fisheye on the fracture surface of test specimen. It was observed from the SEM observation on the deformed specimen that the brittle striation, fisheye were showed in the intergranular fracture structure boundaries at the this velocities. Therefore, fatigue strength and fatigue life would be considered that shot velocity has close relationship with the compressive residual stress.

• 대한기계학회논문집A
• /
• 제27권1호
• /
• pp.200-207
• /
• 2003

In this paper, the effect of the compressive residual stresses which were obtained under the various shot velocities of shot balls on the fatigue behaviors of a spring steel, were investigated. The examination of CT specimen test were executed with the materials(JISG SUP9) which are being commonly used for the springs of automotive vehicles. As a result, the optimal shot velocity of shot balls were acquired considering the peak values of the compressive residual stresses on the surface of specimen and effect on the speed of the fatigue crack propagation da/dN in stage II and the threshold stress intensity factor range Δ$K_{th}$ in stage I. Also the material constant C and the crack propagation index m in the formula of paris law da/dN= C $({\Delta}K^m)$ were suggested in this work to estimate the dependency on the shot velocity.

• 대한기계학회논문집
• /
• 제19권2호
• /
• pp.451-462
• /
• 1995

Single overload tests performed to examine the crack retardation behavior for the specimen thickness and overload ratios. Delayed crack length was tend to increase in small thickness and big overload ratio but was difference between delayed crack length and plastic zone size that expected in specimen thickness. So retardation behavior that estimated in plastic zone size, was not sufficient. Crack tip branching and striation distribution, secondary mechanisms that effected in retardation behavior, was examined by experiment and finite element analysis. Crack tip branching was affected by micro structure, and appeared the more complicatedly according to increasing damage by overload and decreasing crack driving force in base line stress level. And crack tip branching the branching angle decreased crack driving force in the crack tip. And a characteristic of the fractography on retardation zone was that striation distribution did not appear due to decreased crack driving force.

• 대한기계학회논문집A
• /
• 제35권5호
• /
• pp.555-559
• /
• 2011

본 연구는 유압 피스톤 펌프 재료로 사용되고 있는 SACM645소재를 사용하여 모재, QT(quenching & tempering) 시험편 및 QT 질화시험편의 피로특성을 조사하였다. 피로특성 조사결과는 다음과 같다. QT 질화시험편은 피로한도가 인장강도의 80%로 나타나 아주 높은 값을 나타내었다. 이것은 시험편 표면에 단단한 질화처리를 실시하여 피로균열의 발생을 지연시켰고, 피로균열이 발생하더라고 소재가 단단하여 균열진전속도가 늦었다고 판단된다. 파면 관찰결과 피로균열진전 영역에서는 모두 스트라이에이션이 관찰되었고, 피로균열진전 이외의 영역에서 QT 시험편은 벽개파괴의 양상을, 모재와 Qt 질화시험편은 딤플 파괴의 양상을 나타내었다.

• 대한기계학회논문집A
• /
• 제40권6호
• /
• pp.565-571
• /
• 2016

본 논문은 Alloy 617 모재와 용접재에 대한 저사이클 피로 시험 후의 파괴 시험편에 대한 거시적 및 미시적 파면해석을 나타낸다. 용접재 시험편은 Alloy 617의 가스텅그스텐아크 용접 패드로부터 채취, 제작하였다. 본 연구의 목적은 Alloy 617의 모재와 용접재 시험편의 저사이클 파괴 모드 및 기구의 거시적 및 미시적 양상을 고찰하는 것이다. 전변형률 제어 피로시험이 상온에서 0.6, 0.9, 1.2 및 1.5%에 대하여 수행되었다. Alloy 617 모재의 거시적 파면은 피로하중 축에 수직인 평평한 형태의 양상을 보였으나, 용접재 시험편의 경우는 상대적으로 전단/별모양의 양상의 파괴를 나타내었다. 두 시험편 모두 피로균열전파 영역에서는 명확한 스트라이에이션이 관찰되었다. 한편, 모재의 피로균열은 피로 하중 축에 수직인 방향으로 결정입내를 따라 전파하였으나, 용접재 시험편의 경우 하중 축에 거의 $45^{\circ}$의 경사진 형태의 결정입내로 나타났다.