• Restorative Dentistry and Endodontics
• /
• v.33 no.2
• /
• pp.115-124
• /
• 2008

The purpose of this study was to measure the polymerization shrinkage and hygroscopic expansion of resin-based temporary filling materials and to evaluate microleakage at the interface between the materials and cavity wall. Five resin-based temporary filing materials were investigated: Fermit (Vivadent), Quicks (Dentkist), Provifil (Promedica), Spacer (Vericom), Clip (Voco). Caviton (GC) was also included for comparison. Polymerization shrinkage of five resin-based temporary filling materials was measured using the bonded disc method. For the measurement of hygroscopic expansion, the discs of six cured temporary filling materials were immersed in saline and a LVDT displacement sensor was used to measure the expansion for 7 days. For estimating of microleakage, Class I cavities were prepared on 120 extracted human molars and randomly assigned to 6 groups of 20 each. The cavities in each group were filled with six temporary filling materials. All specimens were submitted to 1000 thermocycles, with temperature varying from $5^{\circ}C/55^{\circ}C$. Microleakage was determined using a dye penetration test. The results were as follows: 1. Fermit had significantly less polymerization shrinkage than the other resin-based temporary fill ing materials. Fermit (0.22%) < Spacer (0.38%) < Quicks (0.64%), Provifil (0.67%), Clip (0.67%) 2. Resin-based temporary filling materials showed 0.43-1.1% expansion in 7 days. 3. Fermit showed the greatest leakage, while Quicks exhibited the least leakage. 4. There are no correlation between polymerization shrinkage or hygroscopic expansion and microleakage of resin-based temporary filling materials.

• Journal of the Korea Concrete Institute
• /
• v.17 no.4 s.88
• /
• pp.581-586
• /
• 2005

High-performance concrete (HPC), which is particularly sensitive to self-desiccation, is required to be durable even in severe environmental conditions, i.e. costal area, cold district, etc. However, in recent years, some attention was particularly given to cracking sensitivity of high performance concrete at early age. It has been argued and demonstrated experimentally that such concrete undergoes autogenous shrinkage due to self-desiccation at early age under restrained condition, nd, as a result, internal tensile stress may develop, leading to micro cracking and macro cracking. This shrinkage-introduced crack produces a major serviceability problem for concrete structures. One possible method to reduce cracking due to autogenous shrinkage is the addition of expansive additive. Tests conducted by many researches have shown the beneficial effects of addition of expansive additive for reducing the risk of autogenous shrinkage-introduced cracking. However, the research on hydration model of expansion additive has been hardly researched up to now. This paper presents a study of the hydration model of Ettringite-Gypsum type expansive additive. As a result of comparing forecast values with experiment value, proposed model is shown to expressible of hydration of expansive additive.

• Journal of the Korean Ceramic Society
• /
• v.38 no.2
• /
• pp.183-192
• /
• 2001

산업부산물을 이용하여 3CaO.3Al$_2$O$_3$.CaSO$_4$(C$_4$A$_3$S) 클링커를 합성하였다. 이때, 원료 물질은 산업부산물로 플라이 애쉬, 고로 수쇄 및 괴재슬래그를 $Al_2$O$_3$원으로 그리고 부산석고를 SO$_3$원으로 이용하였으며, CaO원으로 천연석회석을 사용하였다. 제조된 $C_4$A$_3$S 클링커를 CaSO$_4$, CaO를 배합하여 CSA계 팽창재를 제조하였으며, 일반 포틀랜드 시멘트(OPC)에 10 wt.% 첨가하여 수화 및 물성 특성을 조사하였다. 주요 수화생성상은 에트링자이트 및 수산화칼슘이었다. 수화시 에트링자이트의 생성으로 인해 팽창 및 경화체가 치밀화되어 건조수축이 감소되었고, 강도(압출, 인장, 휨)가 향상되었다.

• Cement
• /
• s.108
• /
• pp.57-60
• /
• 1987

이 논문에서는 통상의 포졸란 대신에 제올라이트 물질 즉, 화산 응회암을 적절히 분쇄한 후 혼합해서 만든 시멘트의 특성 변화에 대해 논하였다. 이러한 치환이 알칼리-골재 팽창 반응을 최소화시키고 장기강도를 향상시키는 장점이 있다는 사실도 밝혀냈다. 특히 제올라이트를 미리 열처리해서 첨가했을 때 이러한 팽창감소 효과가 현저하다는 것도 발견하였다. 강도증진 효과는 포졸란 유리상의 활성도에 비해 제올라이트 광물의 활성도가 높기 때문으로 해석되며 팽창의 감소는 비정질 수화 규산염이 먼저 알칼리와 반응을 하는 성질이 있기 때문으로 판단된다.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.29 no.1
• /
• pp.11-18
• /
• 2002

Compomer, like resin composite, undergoes shrinkage during setting. But, due to the structure of glass ionomers and their hydrophilic nature, water sorption and subsequent expansion may lead to compensation of the shrinkage. The purpose of this study was to, evaluate the change of mliroleakage after 30day-water-storage of compomer and composite resin. 40 sound third molars were used for the microleakage test. Z-100 resin was used for the control groups(Group I and III), Dyract AP for the experimental groups(Group II and IV). The storage time was 1 day in Group I, II and 30days in Group III, IV. The result from the this study can be summarized as follows; 1. No significant difference could be found in microleakage of occlusal margin between each group(p>0.05). 2. In microleakage of gingival margin, no significant difference could be found between group I and II, and between group I and III (p>0.05). 3. Group IV was showed less microleakage than group II and group III in gingival margin(p<0.05).

• Journal of the Korean Geotechnical Society
• /
• v.36 no.11
• /
• pp.97-106
• /
• 2020

Swelling properties and shear strength behavior of MgO-Sand mixtures with hydration procese of MgO are compared according to different MgO contents (W_MgO/W_Total=0, 30, 50, 70, 100%) in this study. The specimens are prepared by mixing with crushed MgO refractory bricks and silica sand. After hydration, the particle size and the specific gravity of MgO were decreases. Through microstructure observation and X-ray diffraction analysis, it is confirmed that MgO changes from the cubic structure of Periclase to the hexagonal cubic structure of Brucite after hydration. As the MgO content increases, both swelling rate and swelling pressure of the mixtures increase. W_MgO/W_Total=30% specimen shows relatively low swelling pressure and swelling rate because produced Mg(OH)₂ mainly fills the pores between sand particles. However, in the case of MgO more than 50%, swelling pressure and swelling rate increase significantly because Mg(OH)₂ fills the pores of sand particles at first and then either pushes out sand particles or Mg(OH)₂ particles after filling the pores. As a result of the direct shear test, before hydration, the mixtures show a dilative behavior on high MgO contents and a contractive behavior on low MgO contents. However, after hydration, the behavior of all mixtures changes to contractive behavior. The threshold fraction of fine (i.e., Mg(OH)₂) contents of the hydrated MgO-Sand mixtures reveals approximately 60% compared with normalized shear strength.

• Magazine of the Korea Concrete Institute
• /
• v.21 no.1
• /
• pp.61-67
• /
• 2009

본 연구에서는 초고강도 콘크리트의 자기수축 제어대책으로서 팽창재를 이용하는 경우의 적절한 첨가량 및 유효성에 대하여 확인하였고, 재팽창 현상에 대해서 검토하였다. 그 결과 물시벤트비가 극히 낮은 초고강도 콘크리트의 특성상 과첨가의 경우는 미반응의 팽창재가 잔존하고 재팽창 할 가능성이 있는 것으로 나타났으며 초고강도 콘크리트용의 팽창재로서는 가능한 미수화 팽창재가 잔존하지 않는 팽창재 즉 팽창성능을 충분히 가지면서 수화반응이 빠른 조강성의 비표면적이 큰 팽창재가 바람직한 것을 제안하고 있다.

• Cement Symposium
• /
• no.30
• /
• pp.80-88
• /
• 2003

• Journal of the Korean Ceramic Society
• /
• v.40 no.3
• /
• pp.234-240
• /
• 2003

Hardened cement pastes of OPC which contains 10 wt% CSA type expansive additives were immersed in aqueous solution of 10 wt% MgS $O_4$.7$H_2O$ and then investigated by compressive strength, XRD. SEM and DSC etc.. According to the results including the hydration products and the microstructure of the hardened paste, the case of CSA type expansive additives［No. 6(C/(equation omitted) : 2.29, A/(equation omitted) : 0.16)] prepared from raw materials increased the resistance to $Mg^{2＋}$, S $O_4$$^{2-}$ ion diffusion than that of OPC paste due to the densification by the formation of fine ettringite in the first stage and the hydrates according to $\beta$-C$_2$S hydration in the late period.

• Resources Recycling
• /
• v.21 no.6
• /
• pp.12-22
• /
• 2012

This study investigated a utilization technology of light burned dolomite. light burned dolomite ($CaMg(CO_3)_2$) generated in furnace (steel manufacturer) is an alternative to quick lime. Using light burned dolomite has an effect on reducing the consumption of fluorite slag MgO concentration in supersaturated solution by prolonging the life of softening effect. Armophous MgO, not containing periclase is formed by firing dolomite under $800^{\circ}C$. It has larger surface area and higher reactivity than periclase, and also shows better expansion effect than quicklime. Due to those effects, therefore, armophous MgO produced from light burned dolomite is used as an alternative expansion agent in mortar. In the experiment, characteristics of light burned dolomite were compared to those of existing expansion agents such as anhydrite and quicklime. Then, each expansion and shrinkage rates were measured over a period of about 3 months in both of 1m Jis mold at labscale and apartment mortar flooring at field scale. In the result, it was observed that light burned dolomite in mortar flooring more compensates for the expansion and shrinkage rates than the existing expansion agents, showing low expansion rate of below 0.05% and also decreases the crack.