• Journal of the Korea Concrete Institute
• /
• v.23 no.3
• /
• pp.331-338
• /
• 2011

The purpose of this study is to use organisms or micro-organism functions for eco-friendly water-purification of cement bricks, utilizing bioremediation. Many researches have been performed in the past to improve water quality by using effective micro-organisms in construction materials. In order to purify water using micro-organisms, this research used soybean paste bacteria, an effective micro-organism that was identified through 16S rDNA sequence analysis performed in Daegu S. Environment Protection Institute in addition to Natto bacteria that was studied in the previous research. With these effective micro-organisms with water-purification ability, this study examined their water-purification possibility on cement bricks. This study used Zeolite to immobilize micro-organisms to bricks, and confirmed that the micro-organisms were attached on Zeolite from SEM analysis. The experimental results showed that specific micro-organisms can be used to effectively remove contamination an used to develop eco-friendly construction materials. The study on micro-organisms for material purification shows great promises as a future research topic.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.35 no.2
• /
• pp.81-89
• /
• 2019

Purpose: This study aimed to investigate the correlation between the solubility and the amount of fluoride release when a resin surface coating agent is applied to RMGIC. Materials and Methods: To measure the fluoride release and solubility, Fuji II $LC^{(R)}$and $Filtek^{TM}$ Z350XT without a surface coating, Fuji II $LC^{(R)}$ with G coat $plus^{TM}$ and Fuji II $LC^{(R)}$ with $Permaseal^{(R)}$ were prepared. And the amount of fluoride release and solubility were measured. Results: There was no significant difference in the daily fluoride release between the surface coating agents. The cumulative fluoride release was significantly different between the groups using RMGIC at 56 days (P < 0.05). In the solubility measurement, RMGIC without surface coating was significantly different only on the 7th day compared to the other three groups (P < 0.05). Conclusion: Surface coating agents can prevent the degradation of properties by the initial solvent in RMGIC. Therefore, fluoride is preserved inside the restorative material and the effect of surface coating after the addition is reduced, so that the effect on fluoride release and storage is also reduced.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.38 no.1
• /
• pp.9-17
• /
• 2022

Purpose: The purpose of this study is to investigate how open contacts impact the natural teeth and dental implant prostheses. Materials and Methods: Following criteria were used to select 20 implant crowns with open proximal contacts as the experimental group (Group A): the restorations were delivered in Chosun University Dental Hospital between 2008 and 2018, the restorations are in the posterior region, opposing teeth are fixed dental prostheses, neighboring teeth are sound natural teeth, the patient had been on the maintenance program for at least 3 years. Another 20 implant crowns with closed proximal contacts were selected as the control group (Group B) using the same criteria. Between the two groups, dental caries and food impaction of the neighboring natural teeth and marginal bone-loss of the implants were compared and evaluated. Results: There was no statistically significant difference between Group A and Group B in the occurrence rates of dental caries, food impaction, and marginal bone-loss. The amount of marginal bone-loss, however, revealed statistically significant differences between the two groups, with Group A showing 0.80 ± 0.39 mm loss and Group B showing 1.1 ± 0.43 mm loss. Conclusion: Implant prostheses with open contacts could be clinically considered in select cases as such restorations revealed no harmful effects on neighboring teeth and implant restorations within the perimeters of this study.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.33 no.2
• /
• pp.233-243
• /
• 2006

The aim of this study was to investigate the relationship between the C-factor and shrinkage strain values of composite resin and examine the strain values in different incremental filling techniques. Experiment consisted two aims. First, we compared with strain value in two different C-factors(3.7 and 1.0). Second, we examined the strain values in three different filling techniques. The results of the present study can be summarized as follows : 1. High C-factor groups showed higher contraction stress values than low C-factor groups at 900 sec after polymerization. 2. Hybrid resin showed higher contraction stress values than flowable resin in high C-factor cavities. But contraction stress was not revealed significant difference between hybrid resin and flowable resin in low C-factor cavities (P>0.05). 3. Bulk felling with hybrid resin(Group 1) showed high contraction stress and lining with flowable resin followed hybrid resin (Group 5) showed lower contraction stress. 4. Contraction stress were increased during 900 sec after polymerization in high C-factor groups but decreased gradually after 900 sec. 5. Low C-factor groups showed tight marginal seal between resin and cavity wall but high C-factor groups showed gaps formed between resin and cavity wall in part. On the basis above results, layering techniques in high C-factor cavity showed advantages in reducing contraction stress and gap formation between cavity wall and resin restoration.

• Korean Journal of Dental Materials
• /
• v.44 no.1
• /
• pp.61-68
• /
• 2017

This study evaluated the effects of various cleaning methods on the shear bond strength of zirconia ceramics after saliva contamination. Eighty zirconia disk specimens were divided into 8 groups. All groups were treated with one coat of MDP primer. All specimens (except the negative control) were contaminated with human saliva on the zirconia surface. The positive control went through the bonding procedure immediately after contamination without any cleaning procedure. With the exception of control groups, the remaining six groups were rinsed with water and either applied with MDP recoating (WATER+MDP) or without MDP recoating (WATER). While some were cleaned with a Ivoclean with MDP recoating (IVOCLEAN+MDP) or not applied with MDP recoating(IVOCLEAN), others were cleaned with a 1% NaOCl solution with MDP recoating (NaOCl+MDP) or without MDP recoating (NaOCl). The shear bond strength of all specimens were measured after being stored in distilled water at $37^{\circ}C$ for 24 hours. The data was analyzed statistically by an analysis of ANOVA, Tukey's post hoc test and Student's t-test was used to compare the shear bond strength according to the re-coating of MDP after the cleaning procedure. The positive control group showed the lowest shear bond strength value, and the WATER group and NaOCl group showed no significant difference when compared to the positive control group. The IVOCLEAN group showed significantly higher shear bond strength when compared to Water group and NaOCl group but not with the group of negative control. After rinsing with water or the NaOCl solution, the comparison of the single coating of MDP and re-coating of MDP showed different shear bond strengths but there was no significant difference to the negative control. After rinsing with Ivoclean, there was no significant difference to the negative control regardless of the recoating of MDP. In conclusion, the shear bond strength was affected by the cleansing procedure and Ivoclean was found to be effective regardless of the re-coating of MDP. When water or the NaOCl solution is used to remove surface contaminants, the re-coating of MDP provides a positive effect on cementation.

• Journal of dental hygiene science
• /
• v.15 no.4
• /
• pp.407-412
• /
• 2015

This study investigated flexural properties of indirect Gum-shade composite resins for esthetic improvement. The material utilized in this study was Crea.lign, Twiny flow and Twiny paste (TP). Ten specimens were fabricated with a dimension of $25{\times}2{\times}2mm$ according to the ISO 4049. After fabrications, specimens were stored in the distilled water for 24 hours at the temperature of $37^{\circ}C$. Three-point bending test was performed in universal testing machine (Instron 3344; Instron, USA) at a crosshead speed of 1 mm/min until the failure occurred. TP exhibited a higher flexural strength (FS) and flexural modulus (FM) compared to the flowable materials. There were significant differences among the three materials in FS and FM. However, there was no significant difference in work of fracture (WOF) in all tested materials (p>0.05). In Weibull analysis, TP showed the greatest Weibull modulus which means a higher reliability of the materials. Also, Gum-shade composite resins revealed a strong correlation in all flexural properties. There was a positive correlation in FS-FM ($r^2=0.99$) and a negative correlation between FS-WOF and FM-WOF ($r^2>0.97$). Therefore, this confirmed that flexural property was important for mechanical behavior evaluation and useful information. To addition, this improved among mechanical properties correlation of materials as important factor.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.17 no.5
• /
• pp.94-104
• /
• 2013

Experiments were divided into two parts; one part is to understand the basic properties of high flowable VA/VeoVa-modified cement mortar with different polymer cement ratio (P/C) and the weight ratio of fine aggregate to cement (C:F) and the other part is to investigate the effect of surface water spread on the concrete substrate on adhesion in tension. To understand the basic performance, the specimens were prepared with proportionally mixing VA/VeoVa redispersible powder, ordinary portland cement, silica sand, superplasticizer and viscosity enhancing agent. Here, P/C were 10, 20, 30, 50 and 75% and C:F were 1:1 and 1:3. As the change of P/C and C:F unit weight, flow test, crack resistance and adhesion in tension were measured. Three specimens with good adhesion properties were selected among specimens with different P/C and C:F. The effect of surface water evenly sprayed on concrete substrate on adhesive strength is investigated. The results show that surface water on concrete substrate increases the adhesion in tension of high flowable VA/VeoVa-modified cement mortar and additionally improves the flowability compared to the non-sprayed case.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.3
• /
• pp.245-253
• /
• 2019

Orthognathic surgery of skeletal Class III malocclusion improves oral function and facial appearance. The greater amount of skeletal discrepancy, the greater amount of teeth movement required for decompensation, and this often causes pathological changes in periodontal tissue especially in lower anterior dentition. We made a Top-Down treatment plan with personalized analysis using Face Hunter, Plane System and ARCUS Digma II, in order to resolve severe mobility and cross-bite of lower anterior teeth for 49-year-old female patient who had undergone orthognathic surgery 20 years ago due to skeletal Class III malocclusion and mandibular prognathism. Lower anterior teeth were extracted and alveoloplasty was done. After healing of the wound, immediate loading was conducted immediately after implant placement. Final restorations were fabricated Zirconia using CAD/CAM, and inserted intraorally screw-retained type. During 6-month follow-up, no abnormal episodes of restorations were observed, and obtained satisfactorily both of functional and esthetic outcomes.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.195-202
• /
• 2019

At the department of prosthodontics, the elderly patients with severely atrophied alveolar ridge who have been wearing complete dentures for a long period frequently visit the clinic. In general, the open-mouth impression technique for manufacturing a mandibular complete denture to secure primary support on buccal shelf area has been prevalent. In addition, for securing retention and stability of mandibular denture, we should consider diagnosis, oral function, denture border, occlusal plane, teeth arrangement, and patient training, etc.. But in edentulous patients with severe alveolar bone atrophy, it may hardly secure retention and stability of mandibular complete denture. To promote these, some of clinicians are making an attempt manufacturing the mandibular complete dentures using closed-mouth impression technique based on several reports that compare various impression techniques including open-mouth and closed-mouth impression technique. This case report suggests closed-mouth impression technique may promote retention and stability of mandibular complete denture and compares between the two impression techniques clinically.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.32 no.1
• /
• pp.164-173
• /
• 2005

Mechanical preparation has been introduced to provide the sealant retention. The objective of this study was to compare the fissure penetration and the microleakage of pit and fissure sealant using mechanical preparation(mechanical preparation + acid etching) and acid etching only. An additional objective of this study was to compare the fissure penetration and the microleakage of unfilled and filled sealant in both methods. Sixty human premolars extracted for orthodontic purpose were selected. Thirty teeth were acid etched alone and remaining thirty teeth were prepared with a $\frac{1}{4}$ round bur and then acid etched. One-half of teeth in each surface treatment method were sealed with unfilled sealant and the other half were sealed with filled sealant. All of the teeth were thermocycled for 1200 cycles at $5^{\circ}C\;and\;55^{\circ}C$ and immersed in 5% methylene blue for 24 hours. Each tooth was sectioned bucco-lingually at mesial pit and distal pit and examined under a Measurescope. In the case of mechanical preparation, fissure penetration of sealant was significantly increased compared with the case of acid etching only(P < 0.05). The filled and unfilled sealant using mechanical preparation showed significantly decreased microleakage when compared with the unfilled sealant using acid etching only(P < 0.05). No differences were found in fissure penetration and microleakage between unfilled and filled sealant in both methods. Taken together, the results of this study suggest that mechanical preparation and filled sealant are recommended when placing pit and fissure sealant. However, further clinical studies should be performed in regard to microleakage.