• Korean Journal of Materials Research
• /
• v.5 no.6
• /
• pp.723-731
• /
• 1995

P $b_2$S $r_2$( $Y_{1-x}$ C $a_{x}$)C $u_3$ $O_{8+}$$\delta$/ samples were prepared with x=0.4~0.6 and small $\delta$. To minimize the extent of oxidative decomposition reaction which occurs during the preparation of this phase, two annealing steps were adopted : First, sintered samples of P $b_2$S $r_2$( $Y_{1-x}$ C $a_{x}$)C $u_3$ $O_{8+}$$\delta$/ are oxygenated under 100% $O_2$, which leads to a large $\delta$(e.g., $\delta$=1.8). Second, the resulting samples are deoxygenated under 0.1~1.0% $O_2$in $N_2$, lowering $\delta$ to desired values. This two-step annealing procedure minimized the extent of oxidative decomposition. However, even with the two-step annealing procedure, the oxidative decomposition of P $b_2$S $r_2$( $Y_{1-x}$ C $a_{x}$)C $u_3$ $O_{8+}$$\delta$/ cannot be completely suppressed if $\delta$ is to be reduced to maximize $T_{c}$. Electrical resistivity data show that $T_{c}$(onset) is a function of hole concentration in the Cu $O_2$layer, and the optimum hole concentration for the maximum $T_{c}$ is achieved when $Ca^{2+}$is substituted for $Y^{3+}$between 0.5 and 0.6 A $T_{c}$(onset)=80K has been observed for one such sample, and this is the highest $T_{c}$(onset) yet reported for this compound.ed for this compound.nd.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.359-366
• /
• 2002

The purpose of this study is to investigate the properties of LSGM electrolyte and LSM cathode. The unit cell based on the optimum conditions and processing for high performance was fabricated and measured. The single phase of $LaGaO_3$ was obtained on sintering at $1500^{\circ}$ for 6h with composition of $(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}와 (La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ and $(La_{0.85}Sr_{0.15})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$. The grain size of the sintered body was about $10∼30{\mu}m$ and electrical conductivity was 0.13 S/cm measured at $800^{\circ}$. The single phase of $LaMnO_3$ structure in $(La1-xSrx)MnO_3$ system was obtained at x=0∼0.2 and the particle size of the synthesized powder was about 40 nm. The unit cell was prepared by firing at $1200^{\circ}$ for 1h with $(La_{0.9}Sr_{0.1})MnO_3$ cathode and 0.9NiO-0.1YSZ anode screen-printed on surfaces of $(La_{0.8}Sr_{0.2})(Ga_{0.8}Mg_{0.2})O_{3-\delta}$ electrolyte. The grain size of the electrode was close to $1{\mu}m$ and the electrode had porous structure. The maximum power density of unit cell showed $0.3W/cm^2$ at $800^{\circ}$.

• Resources Recycling
• /
• v.14 no.5 s.67
• /
• pp.13-17
• /
• 2005

As a basic study for recycling molten converter slag as an ordinary portland cement (OPC) by a conversion process, the reaction mechanism and the rate of the formation of $C_4AF$ which is one of the main components of OPC were investigated. The converter slag whose basicity was controlled by adding reagent grade $SiO_2$ was melted and hold for 30 minutes in MgO crucible at $1300^{\circ}C{\sim}1350^{\circ}C$. Then, the sintered CaO pellet heated at the same temperature was dipped into the molten slag and hold for $10{\sim}30$minutes. After the reaction, the crucible was cooled in air and the specimen was cut off to the horizontal direction of the crucible. The dissolution rate of $C_3A$ pellet was measured by the change of radius of the sintered $C_3A$ pellet, and the formed phase of $C_4AF$ was observed by SEM/EDX. As a result, the dissolution rate of $C_3A$ pellet into molten slag was increased from $0.75{\times}10^{-4}(cm/sec)$ at $1300^{\circ}C$ to $1.67{\times}10^{-4}(cm/sec)$ at $1350^{\circ}C$, and the mixed layer of $C_4AF$ and $C_{12}A_7$ was found between slag and $C_3A$ pellet.

• Korean Chemical Engineering Research
• /
• v.60 no.3
• /
• pp.459-467
• /
• 2022

Redispersion of Pt-Sn particles in Pt, PtSn catalyst which have been sintered by high temperature hydrogen reduction was investigated using oxygen treatment with various temperatures. The aim of this study was to understand the relationship between the catalytic activity for propane dehydrogenation reaction and the change in the physicochemical properties of the catalyst. X-ray diffraction analysis (XRD), CO pulse chemisorption, and H₂ temperature programmed reduction (H₂-TPR) were performed to investigate the state of active metal and interactions between particles of redispersed catalyst. It was confirmed that the dispersion and particle size of platinum, the crystal phase of the catalyst, and the reduction behavior were changed according to the oxygen treatment. As for the catalytic activity in propane dehydrogeantion, sintered PtSn catalyst treated with oxygen at 500 ℃ showed best activity and recovery of initial activity. It was confirm that catalyst after oxygen treatment at 500 ℃ showed high dispersion of Pt and decreased particle size as the results of CO pulse chemisorption and XRD of catalyst, and thus the redispersion of PtSn particles in sintered catalyst was occurred. Catalytic activity was recovered due to redispersion using oxygen treatment, and the activity recovery of the PtSn catalyst was higher than that of Pt catalyst.

• Korean Journal of Optics and Photonics
• /
• v.33 no.2
• /
• pp.74-83
• /
• 2022

The entire process, from the raw material to the final system qualification test, has been developed to fabricate a large-diameter, lightweight reflective-telescope system for a satellite observation. The telescope with 3 anastigmatic mirrors has an aperture of 700 mm and a total mass of 66 kg. We baked a silicon carbide substrate body from a carbon preform using a reaction sintering method, and tested the structural and chemical properties, surface conditions, and crystal structure of the body. We developed the polishing and coating methods considering the mechanical and chemical properties of the silicon carbide (SiC) body, and we utilized a chemical-vapor-deposition method to deposit a dense SiC thin film more than 170 ㎛ thick on the mirror's surface, to preserve a highly reflective surface with excellent optical performance. After we made the SiC mirrors, we measured the wave-front error for various optical fields by assembling and aligning three mirrors and support structures. We conducted major space-environment tests for the components and final assembly by temperature-cycling tests and vibration-shock tests, in accordance with the qualifications for the space and launch environment. We confirmed that the final telescope achieves all of the target performance criteria.

• Applied Chemistry for Engineering
• /
• v.19 no.5
• /
• pp.477-483
• /
• 2008

$La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ oxide was synthesized by a citrate method and a typical dense membrane of perovskite oxide has been prepared using as-prepared powder by pressing and sintering at $1300^{\circ}C$. Precursor of $La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ prepared by citrate method was investigated by TGA and XRD. Metal-citrate complex in precursor was decomposed into perovskite oxide in the temperature range of $260{\sim}410^{\circ}C$ but XRD results showed $SrCO_3$ existed as impurity at less than $900^{\circ}C$. Electrical conductivity of membrane increased with increasing temperature but then decreased over $700^{\circ}C$ in air atmosphere ($Po_2=0.2atm$) and $600^{\circ}C$ in He atmosphere ($Po_2=0.01atm$) respectively due to oxygen loss from the crystal lattice. The oxygen permeation flux increased with increasing temperature and maximum oxygen permeation flux of $La_{0.7}Sr_{0.3}Co_{0.2}Fe_{0.8}O_{3-{\delta}$ membrane with 1.6 mm thickness was about $0.31cm^3/cm^2{\cdot}min$ at $950^{\circ}C$. The activation energy for oxygen permeation was 88.4 kJ/mol in the temperature range of $750{\sim}950^{\circ}C$. Perovskite structure of membrane was not changed after permeation test of 40 h and the membrane was stable without secondary phase change with 0.3 mol Sr addition.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.368-370
• /
• 2013

투명 전극은 전기전도도를 갖는 동시에 가시광선을 투과하는 소재를 말하며, 구체적으로는 빛의 파장이 400~700 nm 영역대의 가시광선을 80% 이상 투과하며 전기전도도가 비저항으로 $10^{-3}{\Omega}cm$이하이거나 면저항이 $10^3{\Omega}$/${\Box}$소재를 의미한다. 투명 전극은 전기전도도에 따라 사용되는 용도가 다양하다. LCD, PDP, OLED 와 같은 평판디스플레이 및 3D 디스플레이의 투명전극으로 사용되는 핵심재료일 뿐만 아니라 터치스크린, 투명필름, 대전방지막, 열반사막, EMI 방지막, 태양전지 분야에 광범위하게 이용되고 있다. 일반적으로, 투명전극 박막에 가장 많이 사용되고 있는 소재는 ITO (indium tin oxide)이나, 주성분인 In의 사용량 증가로 상용 ITO 타겟 가격이 급등하고 있음으며, 고가의 ITO 타겟을 대체하기 위한 저가의 투명전극 소재 개발이 절대적으로 요구되며, 신규 소재 개발을 통한 기술력 우위 선점이 필수적으로 요구되는 상황이다. 본 연구에서는 기존에 디스플레이 분야에서 널리 활용되는 고가의 ITO를 대체하기 위한 다성분 금속산화물 투명전극 스퍼터링 타겟 제조기술을 개발하기 위한 연구로서, Metal이 첨가된 In-Ga-Zn-O기반의 3성분계 투명도전성 소재를 조성설계, 고밀도 균질 타겟 제조 및 투명전극 박막을 형성하는 연구를 실시하였다. 고체산화물 산화인듐(In2O3)분말, 산화갈륨(Ga2O3) 분말그리고 산화아연(ZnO)분말과 Metal을 몰비로 칭량한 후 분말을 폴리에틸렌제 포트에 넣고 에탄올을 충분히 채운 후 지르코니아(ZrO2) 볼(ball)을 이용하여 24 h 동안 볼 밀링(ball milling) 방법으로 혼합한 뒤, $120^{\circ}C$의 플레이트위에서 마그네틱 바로 stirring하면서 건조하였다. 이 분말을 건조기에서 완전히 건조한 후 알루미나 유발을 이용해서 pulverizing한 후 sieving기를 이용하여 분말의 조립화를 하였다. 이 분말을 금형에 넣고 300 kg/$cm^2$의 압력으로 press하여 성형한 뒤 대기중에서 소결하였다 소결을 위한 승온 온도는 $10^{\circ}C$/min이었고 소결은 $1,450^{\circ}C$에서 6 h 동안 하였다. IGZO target의 조성 비율은 1:1:12 (mol%)를 사용하였으며, 첨가한 Metal은 Boron (B), Germanium (Ge), Barium (Ba)을 사용하여 타겟을 제작하였다. M-IGZO 박막은RF magnetron Sputter를 이용하여 증착하였으며, 앞선 실험에서 제작한 타겟을 사용하여 M-IGZO박막을 투명전극으로 사용하기 위한 각각의 특성을 파악하였다. 모든 박막은 상온에서 증착을 하였으며, 증착된 박막두께를 측정하기 위해 ${\alpha}$-step IQ를 사용하였고, 광학적 특성을 분석하기 위해 UV-Visible spectrophotometer 로 투과율을 측정하였다. 그리고 전기적 특성을 측정하기 위해 Hall effect measurement 및 4-probe를 사용하였으며, 결정성 분석을 위하여 XRD를 이용하여 분석하였다. 표1은 M-IGZO타겟을 사용하여 증착시간에 따른 면저항 특성을 나타내었다. Ge, B, Ba이 첨가된 IGZO 박막은 증착시간이 증가할수록 면저항이 낮아짐을 알 수 있었다. 또한, Ge이 첨가된 IGZO 박막이 다른 금속이 첨가된 IGZO 박막의 면저항보다 현저히 낮음을 알 수 있었다. Fig. 1(a), (b), (c)는 각 타겟을 동일한 조건으로 증착을 하여 광학적특성을 나타내는 그래프이다. GZO 박막의 광학적 특성을 보면 가시광 영역에서 평균 투과율은 모두 80% 이상으로 우수한 광투과 특성을 보여 투명전자소자로 사용가능하다. 특히, 자외선 영역을 모두 차단하는 UV cut 능력이 우수함을 알 수 있었다. 따라서, 금속이 첨가된 IGZO 박막을 태양전지용 투명전극으로 사용할 경우, 자외선에 의하여 수명이 단축되는 현상을 줄여줄 수 있음을 기대할 수 있으며 내구성 향상에 크게 기여할 것으로 보인다. Fig. 2는 Ge=0, 0.5, 5%인 IGZO 투명전극을 총 40회 반복하여 증착을 실시한 후 각각의 면저항을 측정한 결과이다. 실험결과에 따르면 Ge가 0%, 5%인 IGZO 투명전극은 증착을 거듭할수록 면저항이 증가하는 결과를 나타내었으며, 0.5%인 IGZO 투명전극은 점차 안정화되어가는 결과를 나타내었다. 따라서 안정화 되었을 때 평균 면저항은 26ohm/sq.로 나타났으며, 광투과율은 Fig. 3과 같이 가시광영역에서 평균 80%이상의 결과를 보였으며, 550 nm에서는 86.36%의 우수한 특성을 나타내었다. 본 연구에서는 Metal이 첨가된 In-Ga-Zn-O기반의 3성분계 투명도전성 소재 target을 제작하여 RF magnetron sputter로 박막을 형성한 후 특성을 비교하였다. M-IGZO target 중 Ge (0.5%)을 첨가한 IGZO 타겟을 사용한 투명전극이 가장 우수한 특성을 보였으며, 제작된 M-target의 In 비율이 30% 정도로 기존의 ITO (90%) 대비하여 투명전극 제작 단가를 절감할 수 있다.

• Journal of Korea Water Resources Association
• /
• v.34 no.6
• /
• pp.659-672
• /
• 2001

Generally, design flood for a hydraulic structure is estimated using statistical analysis of runoff data. However, due to the lack of runoff data, it is difficult that the statistical method is applied for estimation of design flood. In this case, the synthetic unit hydrograph method is used generally and the models such as NYMO method, Snyder method, SCS method, and HYMO method have been widely used in Korea. In this study, these methods and KICT method, which is developed in year 2000, are compared and analyzed in 10 study areas. Firstly, peak flow and peak time of representative unit hydrograph and synthetic unit hydrograph in study area are compared, and secondly, the shape of unit hydrograph is compared using a root mean square error(RMSE). In Nakayasu method developed in Japan, synthetic unit hydrograph is very different from peak flow, peak time, and the shape of representative unit hydrograph, and KICT method(2000) is superior to others. Also, KICT method(2000) is superior to others in the aspects of using hydrologic and topographical data. Therefore, Nakayasu method is not a proper in hydrological practice. Moreover, it is considered that KICT model is a better method for the estimation of design flood. However, if other model, i.e. SCS method, Nakayasu method, and HYMO method, is used, parameters or regression equations must be adjusted by analysis of real data in Korea.

• Applied Chemistry for Engineering
• /
• v.16 no.5
• /
• pp.628-634
• /
• 2005

Zirconia-alumina polymer precursor was prepared from zirconium acetylacetonate (ZA). paluminium nitrate (AN), polyethylene glycol (PEG), and ethyl alcohol via an organic-inorganic solution technique. The thermal properties and viscosity of the polymer precursor were measured by differential scanning calorimetry (DSC), thermograbimetric analyzer (TGA), and dynamic viscometer. The vigorous exothermic reaction with volume expansion occurred at $140^{\circ}C$. The volume expansion was caused by abrupt decomposition of the organic group in metal compounds and the metal ions-PEG reaction. The evidences for these reactions were confirmed by FT-IR and $^{13}C$ solid NMR results. The peak intensity at N-O, O-H and C=C decreased with increasing temperature. This indicated that the decomposition of metal compounds and the metal ions-PEG reaction occurred during the vigorous exothermic reaction. At $800^{\circ}C$ for 2 h, the porous powders transformed to the crystalline $ZrO_2-Al_2O_3$ composites.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.5
• /
• pp.294-298
• /
• 2000

The $MgTiO_3\; and \;$0.9MgTiO_3-0.1SrTiO_3$ ceramics were fabricated by the conventional mixed-oxide method. The sintering temperature and time were $1300^{\circ}C~1600^{\circ}C$, 2hr., respectively. The structural and microwave dielectric properties were investigated with sintering temperature and the application for the satellite communication microwave dielectric resonator was investigated. The coexistence of cubic $SrTiO_3$ and hexagonal TEX>$MgTiO_3$ structures in $0.9MgTiO_3-0.1SrTiO_3$ ceramics were found from X-ray diffraction patterns. In the case of $MgTiO_3$ ceramics, sphere phase and needle-like phase were coexisted. The $0.9MgTiO_3-0.1SrTiO_3$ ceramics observed sphere phase. The dielectric constants and temperature coefficient of resonant $frequency(\tauf)$ were increased with addition of $SrTiO_3$ but the quality factor was decreased. The dielectric constant, quality factor and $\tau$f of the;$0.9MgTiO_3-0.1SrTiO_3$ ceramics were 22.61, 10.928(at 1GHz) and $+50.26ppm/^{\circ}C$, respectively.