• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.380-381
• /
• 2007

This paper reports on the deposition conditions and properties of ITO films used as electrode layer in a organic light emitting diodes on a PET substrate. The deposition technique employed was specially designed roll-to-roll sputtering. The oxide was deposited at room temperature in an argon and oxygen plasma on a transparent conducting ITO layer on a PET film. The influence of deposition parameters such as DC power, working pressure and oxygen partial pressure has been investigated, in order to obtain the best compromise between a high deposition rate and adequate electro-optical properties. Electrical and optical properties of ITO films were analyzed by Hall measurement examinations with van der pauw geometry at room temperature and UV/Vis spectrometer analysis, respectively. In addition, the structural properties and surface smoothness were measured by x-ray diffraction and scaning electron microscopy, respectively. From optimized ITO films grown by roll-to-roll sputter system, good electrical$(6.44{\times}10^{-4}\;{\Omega}-cm)$ and optical(above 86 % at 550 nm) properties were obtained. Also, the ITO films exhibited amorphous structure and very flat surface beacause of low deposition temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.381-382
• /
• 2007

IZO/Ag/IZO (IAI) anode films for flexible organic light emitting diodes (OLEDs) were grown on PC (polycarbonate) substrate using DC sputter (IZO) and thermal evaporator (Ag) systems as a function of Ag thickness. To investigate electrical and optical properties of IAI stacked films, 4-point probe and UV/Vis spectrometer were used, respectively. From a IAI stacked film with 12nm-thick Ag, sheet resistance of $6.9\;{\Omega}/{\square}$ and transmittance of above 82 % at a range of 500-550 nm wavelength were obtained. In addition, structural and surface properties of IAI stacked films were analyzed by XRD (X-ray diffraction) and SEM (scanning electron microscopy), respectively. Moreover, IAI stacked films showed dramatically improved mechanical properties when subjected to bending both as a function of number of cycles to a fixed radius. Finally, OLEDs fabricated on both flexible IAI stacked anode and conventional ITO/Glass were fabricated and, J-V-L characteristics of those OLEDs were compared by Keithley 2400.

• Polymer(Korea)
• /
• v.35 no.4
• /
• pp.296-301
• /
• 2011

This study focuses on the investigation of the impregnation of poly (vinyl alcohol) (PVA) crosslinked with poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA) to porous polyethylene membrane for the fuel cell application. The membranes were characterized by the measurements of the water content, contact angle, FTIR spectra, thermal gravimetric analysis, ion exchange capacity, proton conductivity, methanol permeability and elastic modulus. The existence of hydrophilic moieties in the impregnated membranes was confirmed by contact angle and FTIR measurements. The impregnated PVA/PSSAMA(90:10) membrane exhibited a higher ion exchange capacity (1.2 meq./g dry membrane) than Nafion membrane (0.91 meq./g dry membrane). Through the elastic modulus measurement, the dimensional stability of the resulting membranes was expected to increase higher than the polyethylene membranes. The methanol crossover and water content decreased even if the PSSA-MA content increased due to the reduction of the free volume.

• Journal of the Korean Vacuum Society
• /
• v.14 no.4
• /
• pp.238-244
• /
• 2005

IZO thin films are prepared on a corning 7059 glass substrate in a mixed gases of Ar +$O_2$ by rf-magnetron sputtering, using a powder target with a composition ratio of $In_{2}O_{3}$ : ZnO=90 : 10 $wt.\%$. Their electrical sheet resistance are strongly dependent on the oxygen concentration introduced during the deposition, a minimum resistivity of $3.7\times10^{-4}\Omega\cdot$ cm and an average transmittance over $85\%$ in the visible range are obtained in a film deposited in pure Ar gas which is close to near the stoichiometry. During the heat treatment from room temperature up tp $600^{\circ}C$ in various environments, the electrical resistance changes are explained by cyrstallizations or oxidizations of In metal and InO contained in the IZO film. The electrical properties due to oxygen adsorption and phase transitions occurring at temperatures over $40000^{\circ}C$ during heat treatment in air are also investigated.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.120-120
• /
• 2010

최근 투명전도성 산화물(Transparent Conductive Oxide, TCO) 박막은 액정 표시소자(LCD), 플라즈마 디스플레이 패널(PDP), 압전소자 및 태양전지의 투명소자로 사용되어지고 있다. 현재 가장 널리 사용되어지고 있는 투명전극물질인 인듐주석산화물(indium tin oxide, ITO)은 낮은 비저항과 높은 투과율을 가지고 있지만, 높은 원자재의 가격 및 수소플라즈마 처리시 In과 Sn이 환원되어 전기적, 광학적으로 불안정한 문제점들이 지적되고 있다. 이러한 문제점들을 해결하기 위해 최근 적외선 및 가시광선 영역에서 높은 투과도 및 전기 전도성과 수소플라즈마에 대한 화학적 안정성을 갖는 ZnO를 기반으로 3족 원소를 첨가한 새로운 투명 전도막에 대한 연구가 활발하다. 본 연구에서는 RF-Magnetron Sputtering법을 이용하여 $Ga_2O_3$ 혼합비에 따라 제작된 ZnO(GZO) 박막들의 전기적, 광학적, 구조적인 특성들을 분석하였다. 측정결과, $Ga_2O_3$의 첨가량이 7 wt.%인 GZO 박막이 가시광선영역에서 80%이상의 높은 투과율과 $50.5\;\Omega/\Box$의 가장 낮은 면저항을 나타내었다. 이는 Ga원소가 다른 3족 원소와 격자결합을 비교할 때, 이온의 크기가 Zn원소와 비슷하여 최적화된 혼합율을 가지는 경우 격자결합을 최소화시켜 캐리어 밀도의 증가로 인해 높은 전도성을 가지며, 고온에서도 전기적 특성 및 내구성이 향상되기 때문이다. 또한 기판온도에 따른 열처리 특성으로서 기판의 온도를 $100^{\circ}{\sim}400^{\circ}C$까지 변화를 주어 실험하였다. X-선 회절패턴 분석결과 기판온도가 증가함에 따라 ZnO (002) 방향이 감소하는 반면 ZnO(103) 방향이 증가하였으며, 기판온도가 $300^{\circ}C$ 일 때 $17.1\;\Omega/\Box$의로 가장 낮은 면저항이 나타났다. 이는 SEM 이미지를 분석한 결과, 실온에서 제작된 박막과 비교해 300 에서 증착된 GZO 박막이 결정립의 크기가 크고 밀도도 조밀해져 전하의 이동도가 향상되었기 때문이다.

• Korean Journal of Materials Research
• /
• v.18 no.1
• /
• pp.32-37
• /
• 2008

The electrical, optical, structural and surface properties of an indium tin oxide (ITO) film grown on a flexible PET substrate using a specially designed roll-to-roll (R2R) sputtering system as a function of the DC power, $Ar/O_2$ flow ratio, and rolling speed is reported. It was observed that both the electrical and optical properties of the ITO film on the PET substrate were critically dependent on the $Ar/O_2$ flow ratio. In addition, x-ray diffraction examination results showed that the structure of the ITO film on the PET substrate was an amorphous structure regardless of the DC power and the $Ar/O_2$ flow ratio due to a low substrate temperature, which was maintained constant by a main cooling drum. Under optimized conditions, ITO film with resistivity of $6.44{\times}10^{-4}{\Omega}-cm$ and transparency of 86% were obtained, even when prepared at room temperature. Furthermore, bending test results exhibited that R2R-grown ITO film had good flexibility which would be applicable to flexible displays and solar cells.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.3
• /
• pp.615-620
• /
• 2008

We fabriacted thermal evaporated $10nm-Ni_{1-x}Co_x$(x=0.2, 0.6, and 0.7) films on 70 nm-thick polysilicon substrate with $0.5{\mu}m$ line width. NiCo composite silicide layers were formed by rapid thermal annealing (RTA) at the temperatures of $700^{\circ}C$ and $1000^{\circ}C$. Then, we checked the microstructure evaluation of silicide patterns. A FIB (focused ion beam) was used to micro-mill the interconnect patterns with low energy condition (30kV-10pA-2 sec). We investigated the possibility of selective removal of silicide layers. It was possible to remove low resistance silicide layer selectively with the given FIB condition for our proposed NiCo composite silicides. However, the silicides formed from $Ni_{40}Co_{60}$ and $Ni_{30}Co_{70}$ composition showed void defects in interconnect patterns. Those void defects hinder the selective milling for the NiCo composite silicides.

• Polymer(Korea)
• /
• v.34 no.4
• /
• pp.376-380
• /
• 2010

Donor-$\pi$-acceptor (D-$\pi$-A) type chromophore-based polymers were newly synthesized. These polymers exhibited absorption peak due to intramolecular charge transfer (ICT) in a visible range as well as absorption peak due to carbonyl group in both solution and film state by measuring UV visible spectra. The addition of $Eu^{3+}$ ion into the polymers induced red-shift in absorption due to ICT and the color changes from yellow to red in the solution and film were observed by naked eyes. The contents of crosslinking agent influenced the features and solubility of the polymers. In addition, the contents of crosslinking agent and the $Eu^{3+}$ ion addition improved film-forming ability.

• Korean Journal of Materials Research
• /
• v.11 no.7
• /
• pp.556-561
• /
• 2001

We prepared a new a SOS(silicon-on-silicide) wafer pair which is consisted of Si(100)/1000$\AA$-NiSi Si (100) layers. SOS can be employed in MEMS(micro- electronic-mechanical system) application due to low resistance of the NiSi layer. A thermally evaporated $1000\AA$-thick Ni/Si wafer and a clean Si wafer were pre-mated in the class 100 clean room, then annealed at $300~900^{\circ}C$ for 15hrs to induce silicidation reaction. SOS wafer pairs were investigated by a IR camera to measure bonded area and probed by a SEM(scanning electron microscope) and TEM(transmission electron microscope) to observe cross-sectional view of Si/NiSi. IR camera observation showed that the annealed SOS wafer pairs have over 52% bonded area in all temperature region except silicidation phase transition temperature. By probing cross-sectional view with SEM of magnification of 30,000, we found that $1000\AA$-thick uniform NiSi layer was formed at the center area of bonded wafers without void defects. However we observed debonded area at the edge area of wafers. Through TEM observation, we found that $10-20\AA$ thick amourphous layer formed between Si surface and NiSix near the counter part of SOS. This layer may be an oxide layer and lead to degradation of bonding. At the edge area of wafers, that amorphous layer was formed even to thickness of $1500\AA$ during annealing. Therefore, to increase bonding area of Si NiSi ∥ Si wafer pairs, we may lessen the amorphous layers.

• Journal of the Korean Society of Radiology
• /
• v.14 no.2
• /
• pp.85-95
• /
• 2020

The filtration characteristics of H₂O-C₆H₁₂O₆ solution at cell membrane model in renal tubule which irradiated by high energy x-ray(linac 6MV) was investigated. The cell membrane model used in this experiment was a polysulfonated copolymerized membrane of m-phenylene-diamine(MPD) and trimesoyl chloride(TMC)-hexane. They were used to two cell membrane models(CM-1, CM-2). The cell membrane model composed of 0.5 wt% TMC-hexane solution(CM-2) had higher permeate flux(Jv) and rejection coefficient(R) than composed of 0.1 wt% TMC-hexane solution(CM-1). The permeate flux(Jv) and rejection coefficient(R) of H₂O-C₆H₁₂O₆ solution in two cell membrane models(CM-1, CM-2) were increased with increase of pressure drop and effective pressure difference. In this experiment range(pressure 1.5-4 MPa, temperature 36.5 ℃), permeate flux(Jv) of H₂O solvent in irradiated membrane was found to be decreased about 20-30 times than non-irradiated membrane, permeate flux(Jv) and rejection coefficient(R) of H₂O-C₆H₁₂O₆ solution in irradiated membrane was found to be decreased about 2-13 times, about 4-6 times than non-irradiated membrane, respectively. The concentration increase of H₂O-C₆H₁₂O₆ solution at cell membrane model significantly was increased at rejection coefficient(R), was decreased at permeate flux(Jv). As the filtration of H₂O-C₆H₁₂O₆ solution in cell membrane model were abnormal, cell damages were appeared at cell.