• Korean Journal of Materials Research
• /
• v.30 no.12
• /
• pp.672-677
• /
• 2020

Expensive PCBN or ceramic cutting tools are used for the processing of difficult-to-cut materials such as Ti and Ni alloy materials. These tools have a problem of breaking easily due to their high hardness but low fracture toughness. To solve this problem, cutting tools that form various coating layers are used in low-cost WC-Co hard material tools, and researches on various tool materials are being conducted. In this study, WC-5, 10, and 15 wt%Ni hard materials for difficult-to-cut cutting materials are densified using horizontal ball milled WC-Ni powders and pulsed current activated sintering method (PCAS method). Each PCASed WC-Ni hard materials are almost completely dense, with a relative density of up to 99.7 ~ 99.9 %, after the simultaneous application of pressure of 60 MPa and electric current for 2 min; process involves almost no change in the grain size. The average grain sizes of WC and Ni for WC-5, 10, and 15 wt%Ni hard materials are about 1.09 ~ 1.29 and 0.31 ~ 0.51 µm, respectively. Vickers hardness and fracture toughness of WC-5, 10, and 15 wt%Ni hard materials are about 1,923 ~ 1,788 kg/mm2 and 13.2 ~ 14.3 MPa.m1/2, respectively. Microstructure and phase analyses of PCASed WC-Ni hard materials are performed.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.1
• /
• pp.16-24
• /
• 2021

A laser-engineered net shaping (LENS) process is a representative directed energy deposition process. Deposition characteristics of the LENS process are greatly dependent on the process parameters. The present paper preliminarily investigates deposition characteristics of Inconel 718 superalloy on S45C structural steel using a LENS process. The influence of process parameters, including the laser power and powder feed rate, on the characteristics of the bead formation and the dilution in the vicinity of the deposited region is examined through repeated experiments. A processing map and feasible deposition conditions are estimated from viewpoints of the aspect ratio, defect formation, and the dilution rate of the deposited bead. Finally, an appropriate deposition condition considering side angle, deposition ratio, and buy-to-fly (BTF) is predicted.

• Textile Coloration and Finishing
• /
• v.32 no.4
• /
• pp.232-238
• /
• 2020

Duck down is a feather of waterfowl and is used as an accessory for bedding products such as evil, pillow and outdoor sleeping bags due to its soft and bulky characteristics. Down is used mainly for winter outdoor such as padding and jumpers because of its excellent thermal insulation effect. Down wear is known as a product with high added value. Down is processed and sanitized because a large amount of oil and fat, bacteria, dust, insects, and soil are mixed. In particular, if the proper amount of oil and fat is not removed, it may cause odor or bacteria, and since the fishy smell peculiar to down and harmful VOCs (toluene, benzene, etc.) are released, there is a need to suppress the occurrence of bacteria through the provision of antibacterial function. In this study, we investigated the substances that cause the fishy odor of down, and confirmed the effect on the deodorization and antibacterial properties of down according to processing agents and processing conditions in order to impart deodorant and antibacterial properties to down.

• Korean Journal of Metals and Materials
• /
• v.49 no.6
• /
• pp.440-447
• /
• 2011

To improving the mechanical properties of Mg alloys at high temperature, we investigated the mechanical properties at high temperature and the change of microstructure of Mg-6 wt%Zn-0.4 wt%Mn and Mg-6 wt%Zn-0.4 wt%Mn-1 wt%Ag alloys on age treatment that have a stable MgZn phase at high temperature and $AgMg_4$ improving yield stress. In order to predict thermodynamic data of Mg alloys, a phase diagram and precipitation phase were calculated using a thermodynamic program, and it was confirmed that the MgZn and $AgMg_4$ phase existed as main precipitation in this alloys. The experimental data examined using DSC and XRD were comparable with the calculated data for reliability. In order to analysis the microstructure and precipitate phase during aging treatment, it was measured by SEM/EDS and TEM. Lastly, mechanical properties of the MgZn and $AgMg_4$ phase were measured by a tensile test at high temperature.

• Korean Journal of Metals and Materials
• /
• v.49 no.11
• /
• pp.893-899
• /
• 2011

Fabrication of a complex aluminum alloy by the ARB process using dissimilar aluminum alloys has been carried out. Two-layer stack ARB was performed for up to six cycles at ambient temperature without a lubricant according to the conventional procedure. Dissimilar aluminum sheets of AA1050 and AA5052 with thickness of 1 mm were degreased and wire-brushed for the ARB process. The sheets were then stacked together and rolled to 50% reduction such that the thickness became 1 mm again. The sheet was then cut into two pieces of identical length and the same procedure was repeated for up to six cycles. A sound complex aluminum alloy sheet was successfully fabricated by the ARB process. The tensile strength increased as the number of ARB cycles was increased, reaching 298 MPa after 5 cycles, which is about 2.2 times that of the initial material. The average grain size was $24{\mu}m$ after 1 cycle, and became $1.8{\mu}m$ after 6 cycles.

• Design & Manufacturing
• /
• v.14 no.4
• /
• pp.25-39
• /
• 2020

In this study, an edge device that monitors the injection molding process by measuring the mold vibration(acceleration) signal and the mold surface temperature was developed and evaluated its performance. During injection molding, signals of the injection start, V/P switchover, and packing end sections were obtained through the measurement of the mold vibration and the injection time and packing time were calculated by using the difference between the times of the sections. Then, the mold closed and mold open signals were obtained using a magnetic hall sensor, and cycle time was calculated by using the time difference between the mold closed time each process. As a result of evaluating the performance by comparing the process data monitored by the edge device with the shot data recorded on the injection molding machine, the cycle time, injection time, and packing time showed very small error of 0.70±0.38%, 1.40±1.17%, and 0.69±0.82%, respectively, and the values close to the actual were monitored and the accuracy and reliability of the edge device were confirmed. In addition, it was confirmed that the mold surface temperature measured by the edge device was similar to the actual mold surface temperature.

• Journal of Surface Science and Engineering
• /
• v.53 no.6
• /
• pp.300-305
• /
• 2020

Corrosion of reinforcement steel rebar is a serious problem in a wide range of concrete application for buildings and infrastructures. Hydrophobizing surface treatments, such as self-assembled monolayer coating, edible oil-impregnation and silicone oil-impregnation were applied to solidified concrete. The hydrophobizing of concrete significantly reduces an absorption and transportation of water toward a steel rebar in concrete, so that the corrosion resistance of the steel rebar. In particular, the silicone oil-impregnation not only forms the hydrophobic monolayer on the concrete but also fills the inter-connected pores of concrete, thus the corrosion of steel rebar is significantly inhibited compared to the self-assembled monolayer coating and edible oil-impregnation. Therefore, the silicone oil-impregnation can be a promising candidate for preventing corrosion of steel rebar in concrete for durable performance and safety.

• Design & Manufacturing
• /
• v.15 no.1
• /
• pp.66-71
• /
• 2021

In this study, die turning injection(DTI) mold design for manufacturing reservoir fluid tanks used for cooling in-vehicle batteries, inverters, and motors was conducted based on multi-field CAE. Part design, performance evaluation, and mold design of the reservoir fluid tank was performed. The frequency response characteristics through modal and harmonic response analysis to satisfy the automotive performance test items for the designed part were examined. Analysis of re-melting characteristics and structural analysis of the driving part for designing the rotating die of the DTI mold were performed. Part design was possible when the natural frequency performance value of 32Hz or higher was satisfied through finite element analysis, and the temperature distribution and deformation characteristics of the part after injection molding were found through the first injection molding analysis. In addition, it can be seen that the temperature change of the primary part greatly influences the re-melting characteristics during the secondary injection. The minimum force for driving the turning die of the designed mold was calculated through structural analysis. Hydraulic system design was possible. Finally, a precise and efficient DTI mold design for the reservoir fluid tank was possible through presented multi-field CAE process.

• Journal of Powder Materials
• /
• v.28 no.6
• /
• pp.455-461
• /
• 2021

In this study, multilayered SnO nanoparticles are prepared using oleylamine as a surfactant at 165℃. The physical and chemical properties of the multilayered SnO nanoparticles are determined by transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Interestingly, when the multilayered SnO nanoparticles are heated at 400℃ under argon for 2 h, they become more efficient anode materials, maintaining their morphology. Heat treatment of the multilayered SnO nanoparticles results in enhanced discharge capacities of up to 584 mAh/g in 70 cycles and cycle stability. These materials exhibit better coulombic efficiencies. Therefore, we believe that the heat treatment of multilayered SnO nanoparticles is a suitable approach to enable their application as anode materials for lithium-ion batteries.

• Korean Journal of Materials Research
• /
• v.31 no.11
• /
• pp.642-648
• /
• 2021

The precipitation effect of Al-6%Si-0.4%Mg-0.9%Cu-(Ti) alloy (in wt.%) after various heat treatments was studied using a laser flash device (LFA) and differential scanning calorimetry (DSC). Solid solution treatment was performed at 535 ℃ for 6 h, followed by water cooling, and samples were artificially aged in air at 180 ℃ and 220 ℃ for 5 h. The titanium-free alloy Al-6%Si-0.4%Mg-0.9%Cu showed higher thermal diffusivity than did the Al-6%Si-0.4%Mg-0.9%Cu-0.2%Ti alloy over the entire temperature range. In the temperature ranges below 200 ℃ and above 300 ℃, the value of thermal diffusivity decreased with increasing temperature. As the sample temperature increased between 200 ℃ and 400 ℃, phase precipitation occurred. From the results of DSC analysis, the temperature dependence of the change in thermal diffusivity in the temperature range between 200 ℃ and 400 ℃ was strongly influenced by the precipitation of θ'-Al₂Cu, β'-Mg₂Si, and Si phases. The most important factor in the temperature dependence of thermal diffusivity was Si precipitation.