• 한국전기전자재료학회논문지
• /
• 제13권4호
• /
• pp.294-299
• /
• 2000

For practical application as a humidity sensor SnO$_2$thick films devices were fabricated on the refresh type electrode by screen printing method and their material and humidity sensing properties were investigated. As a function of Sb$_{2}$/O$_{3}$ addition rate grain size was increased while porosity and initial resistance were rapidly decreased. And the area of resistance variation according to relative humidity was decreased with increasing heat treatment temperature. SnO$_2$thick film device heat treated at 95$0^{\circ}C$ and contained 0.05mole% Sb$_{2}$/O$_{3}$ had a best humidity sensing properties. From this result it is conformed that humidity sensing properties of SnO$_2$thick film devices could be approved by very small amount of Sb$_{2}$/O$_{3}$ addition.

• 한국세라믹학회지
• /
• 제12권1호
• /
• pp.5-11
• /
• 1975

Thick film resistor paste was made utilizing oxide materials such as SnO, SnO＋Sb2O3, and SnO＋Zn. The oxide materials were mixed respectively with Q-12 glass powder and finally suspended in ethyl cellulose dissolved in ethyl cellosolve. Thick film resistor was made by screen printing the paste on the alumina substrate and firing it at a suitable temperature. Among thick films made from the resistor paste, the thick film containing 85% SnO and fired at $600^{\circ}C$ demonstrated the finest electrical properties showing 10 K ohm in sheet resistance, 110 ppm/$^{\circ}C$ in TCR. In general, TCR of the thick films made from the oxide-mixture paste is good in linearity, therefore it is suggested the oxide-mixture paste is utilized as the negative thermistor.

• 한국전기전자재료학회논문지
• /
• 제16권12S호
• /
• pp.1217-1223
• /
• 2003

Nerve gas sensor based on tin oxide was fabricated and its characteristics were examined. Target gas is dimethyl methyl phosphonate(C$_3$ $H_{9}$ $O_3$P, DMMP) that is simulant gas of nerve gas. Sensing materials were Sn $O_2$ added a-Al$_2$ $O_3$ with 0∼20wt.% and were physically mixed each material. They were deposited by screen printing method on alumina substrate. The sensor device was consisted of sensing electrode with interdigit(IDT) type in front and a heater in back side. Total size of device was 7${\times}$10${\times}$0.6㎣. Crystallite size & phase identification and morphology of fabricated Sn $O_2$ powders were analyzed by X-ray diffraction and by a scanning electron microscope, respectively. Fabricated sensor was measured as flow type and resistance change of sensing material was monitored as real time using LabVIEW program. The best sensitivity was 75% at adding 4wt.% $\alpha$-Al$_2$ $O_3$, operating temperature 30$0^{\circ}C$ to DMMP 0.5ppm. Response and recovery time were about 1 and 3min., respectively. Repetition measurement was very good with $\pm$3％ in full scale.TEX>$\pm$3％ in full scale.

• 한국군사과학기술학회지
• /
• 제7권2호
• /
• pp.81-87
• /
• 2004

Semiconductor thick film gas sensors based on tin oxide are fabricated and their gas response characteristics are examined for four simulant gases of chemical warfare agent (CWA)s. The sensing materials are prepared in three different sets. 1) The Pt or Pd $(1,\;2,\;3\;wt.\%)$ as catalyst is impregnated in the base material of $SnO_2$ by impregnation method.2) $Al_2O_3\;(0,\;4,\;12,\;20\;wt.\%),\;In_2O_3\;(1,\;2,\;3\;wt.\%),\;WO_3\;(1,\;2,\;3\;wt.\%),\;TiO_2\;(3,\;5,\;10\;wt.\%)$ or $SiO_2\;(3,\;5,\;10\;wt.\%)$ is added to $SnO_2$ by physical ball milling process. 3) ZnO $(1,\;2,\;3,\;4,\;5\;wt.\%)$ or $ZrO_2\;(1,\;3,\;5\;wt.\%)$ is added to $SnO_2$ by co-precipitation method. Surface morphology, particle size, and specific surface area of fabricated sensing films are performed by the SEM, XRD and BET respectively. Response characteristics are examined for simulant gases with temperature in the range 200 to $400^{\circ}C$, with different gas concentrations. These sensors have high sensitivities more than $50\%$ at 500ppb concentration for test gases and also have shown good repetition tests. Four sensing materials are selected with good sensitivity and stability and are fabricated as a sensor array A sensor array Identities among the four simulant gases through the principal component analysis (PCA). High sensitivity is acquired by using the semiconductor thick film gas sensors and four CWA gases are classified by using a sensor array through PCA.