• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1138-1145
• /
• 1998

The sliding wear behavior of Ni-base hardfacing alloy, Deloro 50, was investigated at the contact stresses of 15ksi and 30ksi under the various wear environments. In air at room temperature, Deloro 50 showed lower wear resistance than Stellite 6 even at 15ksi due to the occurrence of severe adhesive wear. This seems to be caused by the lower hardness and work- hardening rate of Deloro 50 than those of Stellite 6. In water at room temperature, Deloro 50 showed as good wear resistance as Stellite 6 at 15ksi. It was considered to be due to that water could effectively prevent metal to metal contact through contacting asperities. However, Deloro 50 showed severe adhesive wear at 30ksi in water at room temperature. It seems to be that the water could not suppress adhesion wear at 30ksi. At $300^{\circ}C$ in air, Deloro 50 exhibited higher wear resistance than Stellite 6 even at 30ksi. It was considered that the oxide glaze layers formed on wear surface during sliding, effectively prevented direct metal-to-metal contacts.

• Journal of the Korean Vacuum Society
• /
• v.3 no.4
• /
• pp.449-456
• /
• 1994

산업용 주요 냉간금형 소재인 STD 11 강에 질소이온주입하여 이온조입조거에 따른 질화물형성 거동, 경도 및 내마모성 변화에 관해 연구하였다. XRD분석결과 90keV 에너지로 5$\times$1017 ions/cm2 조사 량 이상에서 Fe2N형태의 질화물이 형성되었으며 3$\times$1016 ions/cm2 범위의 모든 조사량에서 경도 및 조 사량에서 경도 및 내마모성 향상효과를 얻었다. Al2O3와의 ball-on-disc 마모거동 분석결과 STD 11모재 는 응착마모와 산화마모의 혼합형태로 마모되는 반면 질소이온주입한 경우 산화마모 경향이 강하게 나 타났다.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1115-1120
• /
• 1998

The sliding wear behavior of Ni-base hardfacing alloy, Deloro 50, was investigated at the contact stresses of 15ksi and 30ksi under the various wear environments. In air at room temperature, Deloro 50 showed lower wear resistance than Stellite 6 even at 15ksi due to the occurrence of severe adhesive wear. This seems to be caused by the lower hardness and work- hardening rate of Deloro 50 than those of Stellite 6. In water at room temperature, Deloro 50 showed as good wear resistance as Stellite 6 at 15ksi. It was considered to be due to that water could effectively prevent metal to metal contact through contacting asperities. However, Deloro 50 showed severe adhesive wear at 30ksi in water at room temperature. It seems to be that the water could not suppress adhesion wear at 30ksi. At $300^{\circ}C$ in air, Deloro 50 exhibited higher wear resistance than Stellite 6 even at 30ksi. It was considered that the oxide glaze layers formed on wear surface during sliding, effectively prevented direct metal-to-metal contacts.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2008.05a
• /
• pp.187-192
• /
• 2008

A simplified model for an isolated aluminum particle burning in air is presented. Burning process consists of two stages, ignition and quasi-steady combustion (QSC). In ignition stage, aluminum which is inside of oxide film melts owing to the self heating called heterogeneous surface reaction (HSR) as well as the convective and radiative heat transfer from ambient air until the particle temperature reaches melting point of oxide film. In combustion stage, gas phase reaction occurs, and quasi-steady diffusion flame is assumed. For simplicity, 1-dimesional spherical symmetric condition and flame sheet assumption are also used. Extended conserved scalar formulations and modified Shvab-Zeldovich functions are used that account for the deposition of metal oxide on the surface of the molten aluminum. Using developed model, time variation of particle temperature, masses of molten aluminum and deposited oxide are predicted. Burning rate, flame radius and temperature are also calculated, and compared with some experimental data.