• The Journal of the Convergence on Culture Technology
• /
• v.9 no.6
• /
• pp.855-859
• /
• 2023

Copper oxide (CuO) nanoparticles were successfully synthesized using a precursor in which industrial starch was impregnated with an aqueous solution of copper (II) nitrate trihydrate. The microstructure of the precursor impregnated with an aqueous solution of copper nitrate trihydrate was confirmed with a scanning electron microscope (SEM), and the particle size and the crystal structure of the copper oxide particles produced as the temperature of the heat treatment of the precursor increased was analyzed by X-ray diffraction (XRD) and the scanning electron microscope (SEM). As a result of the analysis, it was confirmed that the temperature at which the organic matter of the precursor is completely thermally decomposed is 450-490℃, and that the size and crystallinity of the copper oxide particles increased as the heat treatment temperature increased. The size of the copper oxide particles obtained through heat treatment at 500-800℃ during 1 hour was 100nm~2㎛. It was confirmed that the copper oxide crystalline phase is formed at a heat treatment temperature of 400℃, and only the copper oxide single phase existed up to 800℃. And it was also confirmed that the size of particles produced increased as the calcination temperature increased.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.81-81
• /
• 2010

태양광 또는 자연의 힘을 이용한 에너지의 생산은 가까운 미래에 화석연료의 고갈과 이들의 소모로 인해 발행하는 이산화탄소로 인한 지구 온난화등의 문제로 인하여 그 중요성이 점증되고 있는 실정이다. 특히 태양광으로부터 전기에너지를 얻는 발전 방식은 오래전부터 연구되어 왔고 또한 상용화되어 국부적으로 보조 에너지원으로 이용되어 지고 있다. 동작 원리에 따라 이종접합에서 오는 전위차를 이용하는 방법, 동종 물질의 pn접합을 이용하여 기전력을 얻은 방법 및 연료 감응형 종류가 있다. 이 중에서 물질의 이종접합을 이용하는 방법은 아주 오래된 태양전력을 얻는 방식이나 그 동안 연구가 미비하였던 것이 사실이다. 이에 우리는 새로운 재료인 그래핀을 이용하여 산화구리와의 이종접합 태양전지의 제작및 특성을 분석 하였다. 화학기상증착법 (CVD)을 이용해 그래핀을 구리 박편 표면에 성장하였다. 적절한 온도(섭씨 약 1000도)에서 아주 적은 양의 수소 및 메탄을 흘려 주었을때 손쉽게 단일 원자층의 그래핀이 코팅된 구리박편을 얻을 수 있으며, 이 박편을 고온에서 산화 시키면 그래핀은 산화되지 않고 구리만 산화되어 손쉽게 쇼트키타입 태양전지를 얻을 수 있다. 이때 그래핀은 다른 공정 없이 투명전극의 역할을 한다. 간단한 전극을 부착하여 태양전지를 성능을 평가 하였고 그래핀 및 산화구리의 계면효과를 분석하였다. 효율면에서 III-V족 및 실리콘계의 태양전지에 비해 떨어지나 산화구리의 결정화 순도및 산화구리와 금속간의 계면개선 연구를 통해 극복가능 할 것으로 생각된다.

• Tribology and Lubricants
• /
• v.6 no.2
• /
• pp.1-15
• /
• 1990

본 해설에서는 윤활 오일에서 구리 반응 억제제와 철의 부식 억제제에 관한 내용을 검토한 것으로 자동산화 화정의 초기 생성과 연쇄적인 전파, 확산 및 종료 그리고 1차 및 2차 산화 억제제에 관해서 서술한 것이다. 구리 반응 억제제와 부식 억제 성질 및 작용이 고려되고 첨가제로써의 응용에 관해 조사하였다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.196-196
• /
• 2011

팔라듐-구리 합금 분리막은 세륨산화물로 전처리된 다공성 니켈 지지체 위에 마그네트론 스퍼터 공정과 구리리플로우 공정에 의해 제조되었다. 스퍼터 공정은 얇고 치밀한 팔라듐 합금 분리막 증착을 위해 아주 효과적이다. 본 연구에서는 고온 스퍼터 공정에 의해 증착된 팔라듐 상부에 유동성과 열적확산이 우수한 구리를 코팅한 후, 반도체 분야에서 기가 패턴 매립시 사용하는 구리리플로우 공정을 도입하였다. 구리리플로우 공정은 치밀하고 미세기공이 존재하지 않는 표면을 구현하고 무한대의 수소 투과도를 가능하게 한다. 이로써 마그네트론 스퍼터에 의해 $200^{\circ}C$에서 팔라듐과 구리를 순차적으로 코팅한 후, $700^{\circ}C$에서 2시간 구리리플로우 공정을 실시하여 $7.5{\mu}m$ 두께의 팔라듐-구리 합금 분리막이 제조되었다. 세륨산화물(CeO2)은 고온에서 장시간 운전하는 동안 다공성 니켈 지지체의 금속성분이 팔라듐 합금층으로 확산하는 금속의 확산 문제를 개선하고자 지지체와 코팅층 사이에 확산방지막으로 도입되었으며, 균일한 스퍼터 증착을 위해 평탄한 표면의 지지체를 구현하였다. 투과도 테스트는 100-400kPa 의 압력차, 673-773K 의 온도 조건에서 순수한 수소가스로 실시하였다. 표면 미세기공이 없는 치밀한 팔라듐-구리 합금 분리막은 혼합가스에서 질소의 투과 없이 수소만을 투과하는 무한대의 우수한 분리도를 나타내었으며, 상용온도 $500^{\circ}C$에서 12.6ml/$cm^2{\cdot}min{\cdot}atm$의 수소 투과 능력을 보였다. 본 연구에 의해 제조된 팔라듐-구리 합금 분리막은 표면 미세기공이 없는 치밀한 분리막 제조를 가능하게 하였으며 열팽창계수가 팔라듐과 매우 비슷한 세륨산화물($CeO_2$)로 인해 지지체층과 코팅층과의 접합력이 향상되고 수소취성에 강하고 높은 열적 안정성을 갖는다.

• Applied Chemistry for Engineering
• /
• v.34 no.5
• /
• pp.479-487
• /
• 2023

Copper is cost-effective and abundantly available as a biocidal coating agent for a wide range of material surfaces. Natural oxidation does not compromise the efficacy of copper, allowing it to maintain antimicrobial activity under prolonged exposure conditions. Furthermore, copper compounds exhibit a broad spectrum of antimicrobial activity against pathogenic yeast, both enveloped and non-enveloped types of viruses, as well as gram-negative and gram-positive bacteria. Contact killing of copper-coated surfaces causes the denaturation of proteins and damage to the cell membrane, leading to the release of essential components such as nucleotides and cytoplasm. Additionally, redox-active copper generates reactive oxygen species (ROS), which cause permanent cell damage through enzyme deactivation and DNA destruction. Owing to its robust stability, copper has been utilized in diverse forms, such as nanoparticles, ions, composites, and alloys, resulting in the creation of various coating methods. This mini-review describes representative coating processes involving copper ions and copper oxides on various material surfaces, highlighting the antibacterial and antiviral properties associated with different oxidation states of copper.

• Journal of the Korean Electrochemical Society
• /
• v.20 no.1
• /
• pp.1-6
• /
• 2017

This study investigated the effect of surface pretreatment, which removes native Cu oxides on Cu seed layer, on subsequent Cu electro-/electroless deposition in Cu interconnection. The native Cu oxides were removed by using citric acid-based solution frequently used in Cu chemical mechanical polishing process and the selective Cu oxide removal was successfully achieved by controlling the solution composition. The characterization of electro-/electrolessly deposited Cu films after the oxide removal was then performed in terms of film resistivity, surface roughness, etc. It was observed that the lowest film resistivity and surface roughness were obtained from the substrate whose native Cu oxides were selectively removed.

• Journal of the Korean Ceramic Society
• /
• v.38 no.11
• /
• pp.1000-1007
• /
• 2001

In an evacuated tube solar collector, the stable sealing of the heat pipe to the glass tube is important for the collector to use for a long period of time. The sealing of copper tube to the glass is quite difficult because of the large differences in the physical and chemical properties of the two materials. In this study, therefore, a proper copper oxide layer was induced to improve the chemical bonding of the two materials, and the oxidation state of copper and the interface between copper and glass were examined by XRD, SEM and EDS. Its bonding strength was also measured. Cu$_2$O was formed when the bare copper was heat-treated under 600$^{\circ}C$, while CuO oxide layer was formed above that temperature. The bonding state of CuO to the copper was very poor. The borate treatment of the copper, however, extend the stable forming of Cu$_2$O layer to 800$^{\circ}C$. Borosilicate glass tube was sealed to a copper tube by Housekeeper method only when the sealing part was covered with Cu$_2$O layer. The bonding strength at the interface was measured 354.4N, its thermal shock resistance was acceptable.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.5
• /
• pp.2267-2271
• /
• 2011

This study was focused on getting p-type copper-oxide thin-film semiconductors suitable for p-channel thin-film transistors. Vacuum thermal evaporation and thermal annealing were used to get copper-oxide thin-film semiconductor having properties adoptable as an active layer of thin-film transistors. n-type thin films having electron carrier density of about $10^{22}\;cm^{-3}$ before thermal annealing was converted to p-type thin films having hole carrier density of about $10^{16}\;cm^{-3}$ as the thermal annealing conditions were optimized.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.99.2-99.2
• /
• 2017

전이금속 산화물은 비교적 높은 용량 (700~1000 mAh/g)을 갖기 때문에 차세대 리튬전지용 음극으로서 많은 연구가 진행되어 왔다. 나노 코어-쉘 구조의 다공성 전이금속/전이금속 산화물 구조는 높은 비 표면적의 산화물과 높은 전기전도성을 가지는 금속 코어로 구성되어 고효율 리튬전지에 적용가능하다. 본 연구에서는 구리 소재 상에 나노코어구조의 구리/코발트 입자를 전기화학적으로 석출시킨 후 구리의 산화가 일어나지 않는 전해질/전위 조건에서 코발트만 선택적으로 산화시켜 코어-쉘 구조의 다공성 전이금속/전이금속 산화물 구조를 얻을 수 있었다. 제조된 나노 코어-쉘 구조의 다공성 전이금속/전이금속 산화물 입자를 리튬전지의 음극으로 사용하여 매우 우수한 충/방전 안정성을 나타냄을 확인할 수 있었다.

• Journal of the Korean Chemical Society
• /
• v.32 no.1
• /
• pp.22-29
• /
• 1988

The reaction of methanol-water mixture to $CO_2$ and $H_2$ on alkaline earth metal-copper-zinc oxide has been studied in the temperature range of 150 ${\sim}\;300^{\circ}C$. Generally the addition of the alkaline earth metal to Cu/ZnO resulted in an enhancement of selectivity for $CO_2$ formation and a reduction of catalytic activity. Measurable activities were found from 150$^{\circ}C$, 200$^{\circ}C$, and 250$^{\circ}C$ on Mg/Cu/ZnO, Ca/Cu/ZnO, and Ba/Cu/ZnO respectively. However, the highest selectivity for $CO_2$ formation was observed in Ba/Cu/ZnO catalyst at 250$^{\circ}C$. The effect of alkaline earth metal or ZnO on the reactivity was investigated using temperature programmed desorption of $CO_2$ or temperature programmed reduction with $H_2$ over catalysts respectively. It was found that $CO_2$ interacts more strongly in the sequence of MgO < CaO < BaO and ZnO decereases the reduction temperature of CuO. From the results, it was suggested that ZnO activates $H_2$ in the redox process of Cu component and alkaline earth metals adsorbs $CO_2$ in the catalytic process.