• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.6
• /
• pp.53-60
• /
• 2019

The purpose of this study is to evaluate the degree of improvement in strengths by mixing blast-furnace slag and fly ash in polymer cement mortar(PCM). The test specimens are prepared with EVA polymer dispersion, two types of Admixtures (blast-furnace slag and fly ash), five kinds of polymer-cement ratios (0, 5, 10, 15 and 20%), and six kinds of admixtures (0, 3, 5, 10, 15 and 20%). Plain cement mortar is also made for comparison. From the test results, the flowing of PCM is greatly improved with the mixing of the admixtures, and strengths of PCM compared to ordinary cement mortar are also improved due to a decrease in water cement ratio. In addition, the strength characteristics of PCM by admixtures are greatly improved in flexural strength with fly ash compared to other strengths. It is apparent that the optimum mix proportions with polymer-cement ratio of 10% or more, admixture contents 5 to 10% of flay ash for flexural strength improvement of EVA-cement mortar are recommended in this study.

• Journal of the Korean Institute of Gas
• /
• v.4 no.4 s.12
• /
• pp.25-33
• /
• 2000

In recent years, the subject of remaining life assessment has drawn considerable attention in power plants, where various structural components typically operate at high temperature and pressure. Thus a life prediction methodology accounting for high temperature creep fracture is increasingly needed for the components. Critical defects in such structures are generally found in the form of semi-elliptical surface crack, and the analysis of which is consequently an important problem in engineering fracture mechanics. On this background, we first develop an auto mesh generation program for detailed 3-D finite element analyses of axial and circumferential semi-elliptical surface cracks in a piping system. A high temperature creep fracture parameter $C^{\ast}$-integral is obtained from the finite element analyses of generated 3-D models. Post crack growth module is further appended here to calculate the amount of crack growth. Finally the remaining lives of surface cracked pipes for various analytical parameters are assessed using the developed life assessment program.

• Korean Chemical Engineering Research
• /
• v.48 no.6
• /
• pp.695-699
• /
• 2010

The propellant KM10, a single propellant manufactured from nitrocellulose, was known to cause natural degradation phenomena at long term storage. In this study, the self-life was estimated using high temperature acceleration aging tests and stockpile analysis test. For the life expectancy estimation, Arrhenius equation and Berthelot equation were used in the high temperature acceleration tests, and the first order regression was used in the Stockpile analysis test. The self-life of propellant KM10 using the Arrhenius equation and Berthelot equation showed significantly different results as 43.73, 16.53 years in the high temperature acceleration test, and it showed 42.94 years in the Stockpile analysis test. The value of self-life predicted by Arrhenius equation was reasonable when compared with the result of E. R. Bixon.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.35 no.9
• /
• pp.1119-1129
• /
• 2011

Shot-peening effects on the fatigue behavior of bearing steel were investigated under the high cyclic loading. Hourglass shape specimens were made of bearing steel(JIS-SUJ2) for rotary bending fatigue tests. Two kinds of treatments were performed : a heat treatment and a shot-peened surface treatment after the heat treatment. The fracture surfaces of specimens were classified into two types of fracture mode : the surface fracture mode induced by a surface defect and the internal fracture mode induced by a nonmetallic inclusion. Inclusion depth and shape affected considerably the fatigue life. Shot-peening treatment improved much the fatigue life of the bearing steel under low and high levels of cyclic loads. Probabilistic-stress-life (P-S-N) curves were suggested for the reliable fatigue life estimation of the improved bearing steel.

• Journal of the Korean Society for Railway
• /
• v.12 no.4
• /
• pp.535-541
• /
• 2009

The reliability of control system composed of electronic parts has been studied by DoD since 1960, and has been undertaken mainly by Europe for railways. Especially in Korea, a study on reliability of signalling equipment has been taken since 2000, requiring reliability test for effective maintenance of old type signalling equipment which no longer has information on its past reliability. This study evaluates the reliability test in units of parts for old type signalling equipment; for instance, failure rate in units of parts, or failure data during operation; which was utilized without its consistent reliability monitoring and analysis data for over 20 years. Also, reliability change at this point in time has been estimated by using residual life span function, and a model which can evaluate the possibility of extended operation through stress acceleration test has been developed. This model will be utilized to establish future maintenance policy for train operating company's operation on old type signalling equipment.

• Proceedings of the KIEE Conference
• /
• 2008.09a
• /
• pp.58-60
• /
• 2008

발전소에서 만들어진 전력을 소비자까지 수송하는 송변전변 및 배전설비를 주 대상으로 하는 전력계통 설비의 운영에는 전력의 수송과 이를 위해 설치되는 각종 기자재로부터 인체 및 재산의 안전을 확보하기 위해 많은 종류의 절연재를 사용하고 있다. 지금까지 전력분야에서 사용되어 온 절연재는 자기재(porcelain)가 주종을 이루어 왔으나 재료기술의 발달과 함께 폴리머 절연재료들이 속속 개발되면서 자기재에 비해 가격 및 시공성 등에서 이점이 많은 폴리머 절연재가 자기재를 대체하고 있다. 그러나 폴리머 절연재료는 기들의 재질 및 사용 환경 등에 따라 일정 수명을 가지는 것으로 나타나 수명종기에 이르면 폐기물로 배출되게 된다. 전력산업 중 배전분야에서는 2007년 구매한 기자재를 기준으로 연간 13만연 톤의 전력폐기물이 발생될것으로 예측되었으며 이들은 PE, XLPE, FRP, PVC, EPDM, Silicone 등 유기성분이 약 40%, Cu, Al, 철 등 금속과 무기성분이 약 60% 인 것으로 조사되었다. 그러나 전선 및 케이블류를 제외한 기자재를 대상으로 한 분석에서는 유기성분의 함량이 90%에 이르며 이들은 석유화학공업의 원료로부터 만들어지는 특성상 높은 에너지를 함유하는 것으로 나타난 바, 이들을 적정하게 처리하는 방안의 확보는 폐기물의 처리 외에 폐기물로부터 에너지를 회수하여 자원화하는 것이 가능한 것으로 보여진다.

• Electrical & Electronic Materials
• /
• v.27 no.10
• /
• pp.11-21
• /
• 2014

1975년 이후로 태양전지 평가 실험실과 제조업체들이 직접적으로 많은 노력을 하여 태양전지 모듈에 대한 가속 스트레스 평가를 개발하고 평가하였다. 이 노력들은 이미 알려진 불량 메커니즘을 토대로 모듈 디자인의 민감한 취약 부분을 발견하기 위한 평가를 목적으로 평가 순서/방법 표준화에 많은 기여를 하였다. 이러한 평가 순서/방법은 국가와 국제 모듈 규격 표준화에 적용되었다. 그리고, 실제 외부에서 설치되어 한 번도 문제가 발생되지 않은 평가들은 중간에 제거 되기도 하였다. 가장 대표적인 예로 twist test는 모듈 설치 후 발생되는 불량에 대한 평가이지만, 실제로 불량은 한번도 발견되지 않았다. 덧붙여서, 표준 평가들은 많은 특화된 가속평가를 사용하게 되는데, 이는 문제점들을 조사하거나 특정 모듈 디자인에 대한 잠재적인 불량을 조사하기 위함이다. 실제 수명예측을 위한 가속평가는 가속 인자의 지식이 반드시 필요하지만, 태양전지 분야에서는 문헌이 많이 부족하다. 많은 연구자들이 85/85 DH 평가시간과 습한 지역에서 수년 간 사용된 모듈과의 상관관계를 만들기 위해 시도 하였다. 그리고 이 모델은 DH 평가 표준시간인 1,000시간으로 정의하는데 많은 영향을 미치기도 했다. 하지만, 이 모델은 단지 단일 모드 불량일 경우에만 적용이 되는 것이다. 다른 불량에 대한 가속인자들은 여전히 잘 알려져 있지 않다. 따라서, 모듈이 비록 표준 규격시험을 통과했다고 하더라도 제품이 특정 기간 동안 전력을 생산할 수 있다고 말할 수 없다. 또한, 이 표준평가가 모든 불량 메커니즘에 대한 평가가 되지 않기 때문에 제품의 수명을 결정하는데 사용될 수 없다.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.181-186
• /
• 2013

We present nondestructive characterization for remanent life of advanced ferritic steels, next-gen energy facility materials by reversible permeability. The reversible permeability is based on the theory that the value of reversible permeability is the same differential of the hysteresis loop. The measurement principle is based on the foundation of harmonics voltage induced in a sensing coil using a lock-in amplifier tuned to the frequency of the exciting one. The peak interval of reversible permeability(PIRP), Vickers hardness, and tensile strength(TS) of the aged samples decreased with aging time. We could estimate the remanent life of advanced ferritic steel by using the relationship between the peak interval of reversible permeability and Larson-Miller parameter(LMP), non-destructively.

• Journal of the KSME
• /
• v.31 no.3
• /
• pp.251-260
• /
• 1991

발전 설비를 중심으로 고온 부재의 잔존 수명 진단을 위한 경년 열화도의 측정에 관련된 연구 현황에 대해 극히 좁은 범위 안에서 개략적으로 기술했다. 국내의 산업체에서도 현재 이에 관 련된 문제점을 제시하고 있고 앞으로 이러한 문제의 발생은 그 빈도와 규모면에서 증가하게 될 것이다. 이에 대비하여 기존 방법의 기술적 터득과 데이터의 축적 그리고 측정 정도를 향상시 키기 위한 새로운 측정 방법들의 개발이 시급한 실정이다. 정확한 진단과 수명이 예측을 위해선 본 글에서 설명된 각종 측정법들과, 짧은 식견으로 여기에서는 설명되지 못한 금속학적 고찰을 가미한 수많은 측정법들을 종합적으로 행하여야 할 필요가 있다는 것은 말 할 나위도 없다. 또한 실기 사용 부재의 입수, 나름대로의 정보 교환은 연구 초기 단계에서 부딪치는 수많은 문 제점들을 원활하게 해결하기 위해서는 각 전문분야의 학술적 교류와 더불어 산. 학. 연의 공동 연구가 절실하게 요구된다.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.107-108
• /
• 2011

납축전지는 전 세계 수천만 자동차부터 골프카트. 오토바이 등 동력기계에는 필수 장치로 널리 사용되고 있기 때문에 전지의 수명을 정확히 예측하고 평가하는 것이 중요하다. 본 논문에서는 납축전지의 충. 방전 특성을 고려해 동적 모델을 구현해 보았다. 회로의 구현을 위해 각기 다른 수명의 전지를 테스트하였고, 나타나는 특성 그래프의 변수들을 프로그래밍기법을 활용하여 전지의 특성을 해석할 수 있는 전기적 회로로 모델링하였다.