• Journal of the Korean Society for Nondestructive Testing
• /
• v.36 no.5
• /
• pp.377-383
• /
• 2016

The effect of long-term aging degradation on magnetic properties of ferritic 11Cr low-carbon steel was investigated. Coercivity and hysteresis loss measured from the hysteresis loops decreased with long-term aging time and showed that the relation was well fitted by a second order exponential function. Vickers hardness also decreased with aging time and resulted in mechanical softening. In addition, the microstructural evolution was observed by the scanning electron microscopy, backscattered electron image and X-ray diffraction. The $Cr_{23}C_6$ precipitates along grain boundary grew fast and Laves ($Fe_2W$) phase on martensitic lath boundaries in interior grains was developed. The solid solution atoms depleted in matrix and lath subgrains recovered owing to precipitate coarsening with long-term aging degradation. There was a close relation with softening of magnetic and mechanical properties.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.5
• /
• pp.479-484
• /
• 2009

Nondestructive evaluation(NDE) of ceramic matrix composites is essential for developing reliable ceramics for industrial applications. In the work, C-Scan image analysis has been used to characterize surface crack of SiC ceramics nondestructively. The possibility of detection of surface crack were carried out experimentally by two types of ultrasonic equipment of SDS-win and $\mu$-SDS, and three types of transducer of 25, 50 and 125 MHz. A surface micro-crack of ceramics was not detected by transducer of 25 MHz and 50 MHz. Though the focus method was detected dimly the crack by transducer of 125 MHz, the defocus method could detect the shape of diamond indenter. As a whole, the focus method and the defocus method came to the conclusion that micro crack have a good possibility for detection.

• Journal of Korean Society of Steel Construction
• /
• v.26 no.6
• /
• pp.617-626
• /
• 2014

In this paper, experiments for the evaluation of tensile strength of steel plate with bolt hole and bearing strength of bolted connection were performed, where bolt holes were punched by drilling and oxygen torch, respectively. For the tensile tests, drilled and oxygen torch punched steel plate specimens of 10mm and 15mm thickness were made from structural angles and H-shapes, respectively. For the bearing strength evaluation, test specimens were fabricated with base plates and splice plates those were also punched by drilling and oxygen torch, respectively. The Vicker's hardness were measured around the bolt hole to investigate material property change due to heat effect by oxygen torch cut. Numerical analysis was also performed to investigate the bearing strength of bolted joints due to the increase of hardness around the bolt hole by oxygen torch cut.

• Journal of the Korean Institute of Gas
• /
• v.24 no.5
• /
• pp.39-46
• /
• 2020

This paper is considered about centerline segregation of API 5L steel used in pipeline. Mn/S, Nb and C were known as segregated elements in the centerline of pipe thickness. The Mn usually was accompanied by S consisting of long viscous shape. Microstructure of the centerline was composed of MnS and Nb/Ti indusions including oxide. The segregation effect in centerline region was analyzed by OM, SEM/EDS and micro Vickers hardness. The Mn, Nb and C are retarded elements in transformation from austenite to ferrite or martensite. These elements could derive a bainitic microstructure as a kind of martensite, which is different from difference and element segregation between in matrix and centerline derived from steel melting and heat treatment.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.38 no.9
• /
• pp.1043-1048
• /
• 2014

As micro screws feature reduced screw lengths and pitches, the resulting clamping force diminishes because of the reduced length of the actual joints. The elements of the clamping force are material, geometry, and friction. We studied the shrinking size of the screw and the methods to improve the clamping force by changing the material. We developed a micro screw using SWCH18A and SUS XM7 materials, and obtained the precision and thickness of the pitch through three-dimensional measurement. We also measured the external resistance of the micro screw by applying the Vicker's hardness test and conducted a break surface analysis using a break torque test and SEM for obtaining the break characteristics.

• Journal of Biomedical Engineering Research
• /
• v.19 no.5
• /
• pp.433-441
• /
• 1998

This study was performed to evaluate the effects of surface flaw on the fracture of all-ceramic materials. A feldspathic porce lain of VMK68, a cashable ceramic of IPS-Empress, and an alumina-glass composite of In-Ceram were used. Specimens were prepared as 12$\times$3$\times$1mm in dimensions, and a Vickers-produced indentation crack was made at the center of the tensile surface. Test specimens were immersed in dlstilled water and In oil, which were broken under a crosshead speed of 0.05 mm/min by 3-point bend test at 37$^{\circ}C$. The characteristic patterns of Vickers indentation and fracture surfaces were examined by an optical microscope and a scanning electron microscope. The fracture surfaces of the VMK68 and the IPS-Empress showed a median crack pattern at the fracture origin and indicated a tendency to cleavage hackle. The fracture surface of the alumina-glass composite, In-Ceram, showed a Palmqvist crack pattern at the fracture origin and indicated a tendency of toughening by the frictional Interlocking between the microstructurally rough fracture surfaces.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.15 no.6
• /
• pp.3396-3402
• /
• 2014

The importance of shape design for strength is highly regarded when applied to thin plate products in Ceramic Injection Molding (CIM), such as cases for electronic goods. This study analyzed the characteristics of the mechanical strength of CIM product by measuring the flexural strength and elastic modulus through a 3-point bending test according to the thickness of a thin plate test piece prepared by CIM. The specimen with a thickness of 0.48mm required a 82.9~94.5N fracture load, whereas a 1.0mm thick test piece required 233.6~345.8N. The increase in thickness by 0.5mm resulted in a 3-fold increase in the fracture load, whereas the elastic modulus decreased by 20%. The thicker the specimen, the lower relative density and surface hardness of the specimen. This is because the thicker the specimen, the lower the powder fraction of the ceramic mixture, and the material properties partially change after sintering.

• Journal of the Microelectronics and Packaging Society
• /
• v.14 no.4
• /
• pp.21-25
• /
• 2007

In this study, the properties of Sn-0.7wt%Cu-Xwt%Re(X=$0.01{\sim}1.0$) older were investigated by using DSC(differential scanning calorimetry), wetting balance, victors hardness and tensile testers. The melting temperature of solder was increased with increasing the contents of rare earth element, and the melting temperature range of Sn-0.7Cu-($0.01{\sim}1.0$)Re solder was $233.9{\sim}234.7^{\circ}C$. The wettability with Sn-0.7Cu-0.1Re solder was higher than that of Sn-0.7Cu-0.01Re and Sn-0.7Cu-1.0Re solders, and the wettability of Sn-0.7Cu-0.1Re solder was higher than that of Sn-0.7wt%Cu-0.01w%P solder. Also, the hardness and tensile strength of solder were increased with increasing the contents of rare earth element.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.5
• /
• pp.229-234
• /
• 2017

In this study, TiAl alloy was fabricated by a centrifugal casting method for turbo charge of automotive. Optimum conditions for defectless morphology using various ceramic mold were investigated. The crystal structure, microstructure, and chemical composition of the TiAl prepared by centrifugal casting were studied by X-ray diffractometer (XRD), optical microscopy (OM), field emission scanning electron microscopy (FE-SEM) and energy dispersive spectroscopy (EDS), microvickers hardness analyzer (HV). Two kinds of dendrite structures were observed with 4-fold and 6-fold symmetries. The FE-SEM, EDS and HV examinations of the as-cast TiAl showed that the thickness of the oxide layer (${\alpha}$-case) was typically less than $50{\mu}m$.

• Journal of the Korean Ceramic Society
• /
• v.33 no.3
• /
• pp.339-347
• /
• 1996

Mechanical properties(flexural strength hardness fracture toughness) of alumina ceramics were evaluated. Alumina products of four companies were selected and three of those were made in Korea and one of those was made in Japan. The large differences according to manufacturing companies had resulted from flexural strength and weibull modulus which had a wide ranges of 300 to 400 MPa and 5 to 15 respectively. Critical indenstation load which could be neglected the effect of elastic recovery was about 9.8N and Vickers' hardness were about 15 GPa. Fracture toughnesses were evaluated by IF and ISB method. It was more preferable to the average at one indentation load that fracture toughness were obtained from the slope of the relationship between indentation load and crack length in IF method and between indentation load and fracture load in ISB method and fracture toughness was about 4 MPa·m1/2.