• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 춘계학술강연 및 발표대회강연 및 발표논문 초록집
• /
• pp.69-70
• /
• 2006

고주파 유도가열 연소합성법에 의해 2분 이내의 짧은 시간에 단일 공정으로 ZrC와 3Si의 혼합 분말로부터 $ZrSi_2-SiC$ 복합재료의 합성과 치밀화가 동시에 이루어졌다. 60MPa의 압력과 90%의 고주파 출력을 가하여 제조된 복합재료의 상대밀도는 약 97%였으며, $ZrSi_2$ 상과 SiC의 평균 결정립 크기는 약154nm와 78nm이었다. 비커스 경도계를 이용하여 측정된 $ZrSi_2-SiC$ 복합 재료의 경도와 파괴인성 값은 각각 $1180kg/mm^2$과 $2.5MPa{\cdot}m^{1/2}$ 이었다.

• 한국재료학회지
• /
• 제9권4호
• /
• pp.434-438
• /
• 1999

Vickers microhardness for polished Cu specimen has been measured by conventional and new methods. The conventional microhardness was measured by observing the diagonal of indentation after the load was removed. Whereas, the new method for microhardness was obtained by measuring the penetration depth of indenter into the specimen under the load. As the applied load was increased, the microhardness obtained by new method was increased. When the applied load was in the range of 5mN to 80mN, the rate of elastic to total depth of indenter was about 6% and the calculated depth of rounded indenter was 0.07$\mu\textrm{m}$. The difference in microhardness measured by two different methods such as conventional and new methods can be explained in terms of the elastic deformation of specimen, the shape of practical indenter and pile up of material.

• 한국기계가공학회지
• /
• 제3권1호
• /
• pp.45-51
• /
• 2004

In this paper, the relationship between the mechanical properties of alumina abrasives and grinding performance was investigated. Micro vickers hardness and fracture strength of all abrasives used in this study were measured. The grinding experiments were earned out with alumina grinding wheels made by various kinds of alumina abrasives including 32A, WA, ART, ALOMAX, and RA. The performance of such grinding wheel for grinding SKD11 was evaluated by specific grinding energy, grinding-ratio, and surface roughness. The grinding wheels composed by the harder abrasives and the lower fracture strength abrasives showed better grinding performance.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.797-801
• /
• 2003

The mechanical properties such as shear strength and the hardness of milli-size products that manufactured for various process parameters by forward extrusion using square dies are investigated. Shear strength test is implemented for the observation of relation between vickers hardness and shear strength in the interface of head and shaft part of a stepped pin. When the extrusion ratios of pure aluminum and pure copper billets increase, the hardness on both the surface and the center line of a pin also increase, especially the hardness on the surface is shown to be a little higher than on the center. The existence of knock-out pad in extrusion die caused hardness increase in the interface of a extruded pin. As compared shear strength with hardness of a pin, the approximated linear relations are suggested in this study.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권6호
• /
• pp.806-813
• /
• 1999

The effect of Post-Weld Heat Treatment(PWHT) of SS400 Steel was investigated with parameters such as micro vickers hardness corrosion potential polarization behaviors galvanic current Al anode generating current Al anode weight loss etc. Hardness of each parts(HAZ, BM, WM)by PWHT is lower than that of each parts by Non Post-Weld Heat Treatment(NPWHT) However hardness of WM of HAZ part was the highest among those three parts and HAZ area were also acted as cathode without any case of heat treatment. Potential difference between each three parts by PWHT was also smaller compared to NPWHT. Therefore it is suggested that Corrosion resistance property is increased by PWHT. However both Al anode generating current and anode weight loss was also decreased by PWHT compared to NPWHT when SS400 steel is cathodically protected by Al anode.

• 열처리공학회지
• /
• 제11권1호
• /
• pp.54-61
• /
• 1998

Since Cr-Mo-V steel has excellent fracture and creep properties at elevated temperature, they are extensively used as steam turbine components such as the turbine rotor. However, the turbine rotor steel used to suffer material degradation during long term service. Therefore, the assessment of the safety and residual life of the turbine rotor is periodically required during service. One of the most convenient techniques for that is the hardness method mainly due to its simplicity and nondestructive characteristics. In this research, six specimens with different aging times of turbine rotor steel were artificially prepared by an isothermal heat treatment at $630^{\circ}C$. The micro Vickers hardnesses of specimens were measured at room temperature. The relationships between the fracture properties and the hardness ratio were investigated. And also an indirect method to evaluate the residual life of degraded turbine rotor was proposed based on the micro Vickers hardness measurement.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.311-311
• /
• 2012

Boron carbide (B-C) 박막은 높은 경도, 열적 안전성, 화학적 안전성이 우수한 하드 코팅 소재로 사용되고 있다. 우수한 특성을 가지는 B-C 박막에 대한 연구는 B4C 비전도성 타겟을 이용하여 RF Sputtering 법으로 증착 공정변수에 대해서 박막의 물성에 관해 일부 연구자들이 진행하였으나, Pulsed dc margnetron sputtering 법으로 증착 공정변수에 대한 물성의 연구는 미진하였다. 반면에, DLC 박막은 우수한 특성을 가지는 하드 코팅 소재이나 400도 이상에서는 내열성이 떨어지는 단점을 가지고 있다. 연구에서는 B-C 박막의 내열성이 우수한 특성을 이용하여 DLC 박막의 내열성을 높이기 위한 목적으로 B-C 박막과 DLC 박막을 다층막으로 제조함으로서 DLC 박막을 구조적으로 안정화를 시키고자 하였다. 그리고 비전도성 B4C 타겟으로 Pulsed dc 마그네트론 스퍼터링법을 이용하여 증착기술을 개발하기 위해서 공정압력과 인가전력에 따른 B-C 박막을 제조하여 그 물성을 조사하였고, B-C/DLC 다층막을 제조하여 DLC 박막의 내열성을 증가시키고자 하였다. B-C 박막과 B-C/DLC 다층막의 경도와 탄성율은 나노인덴테이션과 마이크로 비커스를 이용하였으며, 박막의 성장구조와 박막의 구조를 조사하기 위해 SEM과 FTIR 및 XRD 을 이용하여 측정하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 추계총회 및 학술대회 논문집
• /
• pp.140-140
• /
• 2012

로듐은 열전도성 및 전기전도도가 우수할 뿐 아니라 산/알칼리에 잘 부식되지 않으며 강한 내구성을 지니고 있어서 장식 및 액세서리의 표면처리 및 각종 전기/전자산업의 부품으로 널리 이용되어지고 있다. 본 연구에서는 반도체 검사 장비인 프로브 카드에 조립되어 있는 프로브 니들의 내마모성을 향상시키기 위하여 로듐도금의 특성을 연구하였다. 로듐의 이온 공급원으로 Rhodium sulfate 를 사용하였다. 시편은 황동 시편($0.5cm{\times}2cm$)을 사용하였다. 로듐 도금 시 여러 가지 제어인자 중도금욕의 온도(상온, $40^{\circ}C$, $60^{\circ}C$)와 황산농도(10ml/l, 50ml/l, 100ml/l) 그리고 전류밀도(0.2ASD, 0.5ASD, 1.0ASD)를 변수로 하여 실험을 하였다. 각각의 변수에 따라 전류 효율 및 전착 속도를 분석하였으며, 현미경을 이용하여 표면을 관찰하였다. 그리고 비커스 경도계를 이용하여 경도를 측정하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.192-192
• /
• 2013

하이브리드 표면처리는 다른 표면처리법을 동시 또는 연속적으로 행하여 단일표면처리에 비해 더욱 우수한 특성을 부여시키기 위한 표면처리법이다. 본 연구는 붕소와 질소 원소를 이용한 하이브리드 표면처리를 오스테나이트계 스테인리스강인 STS 316L 소재에 적용하여 변화된 특성을 평가하였다. 본 실험에 사용된 하이브리드 표면처리법으로는 붕소분말을 이용한 보로나이징처리와 활성스크린을 이용한 이온질화처리법을 적용하였다. 하이브리드 표면처리된 STS 316L시편은 FE-SEM을 이용하여 표면형상 및 단면조직을 관찰하였으며 GDS와 XRD를 이용하여 깊이에 따른 원소 및 상분석을 실시하였다. 또한 마이크로비커스 경도계와 마모시험기를 이용하여 경도와 마모특성을 측정하였고, 염수분무시험을 통하여 해수환경에서 부식거동을 평가하였다.

• 한국해양공학회지
• /
• 제15권2호
• /
• pp.61-65
• /
• 2001

The fracture toughness of ceramics can be measure by such various methods as DT (double torsion), CN (chevron notch) etc. But, the application of these methods to the engineering ceramics is very difficult because of its very high hardness. So, IF (indentation fracture) method is generally used for the evaluation of fracture toughness of ceramics. The Median crack induced by the sharp Vickers indenter was compared with the detected AE (acoustic emission) signal. On the silicon nitride ceramics, the AE test results agree fairly well with the median crack occurance and growth process. But, on the alumina, very many complicated crack signals were detected besides median crack. It can be considered that the IF methods must be used in limited engineering ceramics materials.