• Journal of Dental Rehabilitation and Applied Science
• /
• v.34 no.2
• /
• pp.89-96
• /
• 2018

Purpose: The aim of this study was to evaluate the effect of delayed time, surface treatment, and repair materials on repair of bis-acryl composite resin through comparison of shear bond strength and to evaluate the utility of bis-acryl composite resin repair using polymethyl methacrylate resin. Materials and Methods: A total of 90 bis-acryl composite resin specimens were fabricated and classified into 9 test groups, each of 10 pieces according to delayed time, surface treatment and repair material. The shear bond strength of each specimen was measured using a universal testing machine immediately after fabrication and analyzed using a statistical analysis program (IBM SPSS statistics 20). After the shear bond strength measurement, the fracture surface of the specimen was observed. Results: The highest shear bond strength ($17.54{\pm}3.14MPa$) was observed in the experimental group bonded immediately with a light-curing flowable composite resin using a bonding agent. Conclusion: When repairing bis-acryl composite resin, it is necessary to consider whether to remake according to the delayed time. For effective repair, it is desirable to consider appropriate materials and surface treatment methods according to the site or purpose of use.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.30 no.2
• /
• pp.192-198
• /
• 2014

This case is a porcelain laminate veneer (PLV) and all-ceramic crown treatment case on a female patient in her thirties who visited for esthetic improvement. The patient's chief complaint was protrusive and uneven anterior teeth, and she wanted minimum tooth reduction. The patient was in skeletal class II deep bite. Considering this, check bite method was used for mounting on articulator during diagnostic wax-up. Tooth reduction was done using mock-up base on diagnostic wax-up, and the amount of deletion was checked by index. For the accordance of shade, PLVs were restored in prior to all ceramic crown. After using all-ceramic crown, satisfactory esthetic improvement was obtained.

• Korean Journal of Dental Materials
• /
• v.44 no.4
• /
• pp.311-318
• /
• 2017

The purpose of this study was to examine the effects of the curing sequence and polymerization temperature on the flexural strength and microhardness of two provisional resins (Bis-acryl resin composite and polymethyl methacrylate (PMMA)). Polymerization was carried out under various conditions, in air at $25^{\circ}C$ (control) and in hot water (40, 50, 60, 70, and $80^{\circ}C$). The flexural strength test was conducted according to ISO-4049. The Knoop hardness was measured. For the Bis-acryl resin, the temperature up to $50^{\circ}C$ did not increase the flexural strength nor the hardness of the bis-acryl resin composite (p>0.05) but higher temperatures increased the strengths. For the PMMA resin, flexural strength increased with temperatures up to $70^{\circ}C$ and then decreased slightly. Bis-acryl resin composite had higher mechanical properties than the PMMA resin. The effect of heat was more pronounced in the bis-acryl resin composite than in the PMMA resin (p<0.05).