• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.127-135
• /
• 1994

We investigated the bonding interfaces of directly-bonded Si-Si and $Si-Sio_{2}$/Si wafer pairs. By the angle lapping-delineation, anisotropic etching, and (FIR)-TEM observation methods, we studied on the interface defects and the transient region originated from the interface stress, the various types of voids, the formation and stability of interfacial oxide. We also compared the interface image of the bonded $Si-Sio_{2}$ with that of a typically grown $Si-Sio_{2}$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.2
• /
• pp.114-119
• /
• 2000

Etch characteristics of SF6/CI2 electron cyclotron resonance (ECR) plasmas have been investigated. Surface reaction of gas plasma with polysilicon was also analysed using X-ray photoelectron spectroscopy (XPS). At the same time, the relationship between surface reaction and the etched profile of polysilicon was examined using XPS. The etch rate of polysilicon and oxide increases with increasing flow rate of SF6 in the SF6/CI2 gas mixture, and tis selectivity also increase also increase. It was also found that as increasing flow rate of SF6 in the SF6/CI2 gas mixture, the atomic% of chlorine detected at surface region decrease, but F and S contents increase. At the same time, when the mixing ratio of SF6 gas increases, the anisotropy of etched polysilicon is sharply decreased in the 0%~10% range of the SF6 mixing ratio, but is rarely varied in the range over 10%, in spite of the large variations in flow rates. It can be explained that the bonding of S-Si due to SiSx(x$\leq$2) compound formed on the etched surface suppress the formation of Si-Cl and 'or Si-F bonding in the silicon etching.

• Journal of the Korean Vacuum Society
• /
• v.9 no.2
• /
• pp.99-101
• /
• 2000

The fabrication of the submicron size hole has been interesting due to the potential application of the near field optical sensor or liquid metal ion source. The 2 micron size dot array was photolithographically patterned. After formation of the V-groove shape by anisotropic KOH etching, dry oxidation at $1000^{\circ}C$ for 600 minutes was followed. In this procedure, the orientation dependent oxide growth was performed to have an etch-mask for dry etching. The reactive ion etching by the inductively coupled plasma (ICP) system was performed in order to etch ~90 nm $SiO_2$ layer at the bottom of the V-groove and to etch the Si at the bottom. The negative ion energy would enhance the anisotropic etching by the $Cl_2$ gas. After etching, the remaining thickness of the oxide on the Si(111) surface was measured to be ~130 nm by scanning electron microscopy. The etched Si aperture can be used for NSOM sensor.