• Journal of Bio-Environment Control
• /
• v.24 no.4
• /
• pp.333-340
• /
• 2015

Because soils in reclaimed lands nearby coastal areas have much higher salinity and moisture content than soils in inland area, parts of greenhouses embedded in such soils are exposed to highly corrosive environments. Owing to the accelerated corrosion of galvanized steel pipes for substrucrture and structure of greenhouses in saline environments, repair and reinforcement technologies and efficient maintenance and management for the construction materials in such facilities are required. In this study, we measured the corrosion rates of the parts used for greenhouse construction that are exposed to the saline environment to obtain a basic database for the establishment of maintenance and reinforcement standards for greenhouse construction in reclaimed lands with soils with high salinity. All the test pipes were exposed to soil and water environments with 0, 0.1, 0.3, and 0.5% salinity during the observation period of 480 days. At the end of the observation period, salinity-dependent differences of corrosion rate between black-surface corrosion and relatively regular corrosion were clearly manifested in a visual assessment. For the soils in rice paddies, the corrosion growth rate increased with salinity (0.008, 0.027, 0.036, and $0.043mm{\cdot}yr^{-1}$ at 0, 0.1, 0.3, and 0.5% salinity, respectively). The results for the soils in agricultural fields are 0.0002, 0.039, 0.040, and $0.039mm{\cdot}yr^{-1}$ at 0, 0.1, 0.3, and 0.5% salinity, respectively. The higher corrosion rate of rice-paddy soil was associated with the relatively high proportion of fine particles in it, reflecting the general tendency of soils with evenly distributed fine particles. Hence, it was concluded that thorough measures should be taken to counteract pipe corrosion, given that besides high salinity, the soils in reclaimed lands are expected to have a higher proportion of fine particles than those in inland rice paddies and agricultural fields.

• Analytical Science and Technology
• /
• v.8 no.1
• /
• pp.85-90
• /
• 1995

Corrosion characteristics of 4 kinds of the Fe-Al damping alloys has been studied in the 3.5% NaCl solution and compared with a cold rolled mild steel and pure Ti, No passivation, besides Ti, was observed in the Fe-Al damping alloys and a cold rolled mild steel. Corrosion rate was decreased with lower carbon concentration. In the case of Mn addition for improving damping capacity, corrosion rate was decreased in scrap iron but was not decreased in electrolytic iron. It has been shown that corrosion rate of Fe-Al damping alloys lays between that of the pure Ti and that of a cold rolled mild steel.

• Journal of Welding and Joining
• /
• v.4 no.1
• /
• pp.16-31
• /
• 1986

스테인레스강의 주요성능은 내식성이기 때문에 부식성의 환경에서 사용되는 일이 많다. 이 때문 에 스테인레스 강제강치에서는 부식에 관계되는 사고가 대단히 많다. 그림1(a)은 일본화학공학협 회가 1987년부터 1982년사이에 화학장치에 발생한 615건의 손상을 종류별로 분류한 것이다. 전면 부식, 공식, 동력부식균열등의 습성환경에서의 전기화학적 부식이 전체의 54%나 점하고 있 다. 이들 손상에 재료별로 보면 그림1(b)와 같이 스테인레스강이 차지하는 비율이 총 1/4에 달하 고 있다. 또한, 별도조사결과에 의하면 각종손상이 용접이음부에서 약 50% 발생하고 있어, 용접 이음부가 부식성환경에서 사용되는 경우에는 이를 부식현상과 그 방지대책을 세우지 않으면 안된다. 용접부에서 이들 부식현상이 발생하기 쉬운 것은 다음과 같은 요인으로 생각된다. (1) 용접내부는 모재와는 다른 금속조직을 가진다. (2) 용접잔류응력이 존재한다. (3) 용접결함이나 이음형식에 의한 형상불연속 놋치화하여 응력집중을 가져온다. 또한 이들이 표 면에 개구한 극간부식을 가질때에는 극간부식의 요인이 된다. 본고에서는 이들 부식현상중 가장 중요한 오-스테이나트계스테인레스강 용접부에서의 응력부식균열 현상에 대하여 설명한다.

• Proceedings of the Korean Society for Agricultural Machinery Conference
• /
• 1999.07a
• /
• pp.307-312
• /
• 1999

현재 우리나라에서 매년 생산되는 농산부산물은 볏짚, 왕겨 등이 주를 이루는데 에너지원으로서 적당한 것은 왕겨이다 하지만 왕겨는 단순히 농업의 부산물로 여겨질 정도로 농민들의 소득증대에의 기여도가 매우 낮다. 또한 왕겨는 내외피가 규소로 치밀하게 피복되어 있으므로 부식퇴기 어려움에도 불구하고 왕겨를 축사의 깔개로 이용 후 퇴비화함에 따라 농지내 왕겨 환원속도가 부식속도 보다 빨라서 토양속에 미부식 왕겨가 누적되어 농지내 토양환경을 열악하게 하고 있으며 왕겨를 축사내 깔개로 이용함에 따라 어린 가축의 생육장애 등이 제기피고 있으며 장래에는 악취로 인한 대기오염 문제와 가축의 질병 문제 등이 추가로 제기될 가능성이 많다. (중략)

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.3 no.2
• /
• pp.80-83
• /
• 2002

The effect of chloride content on the corrosion of reinforced bar in concrete was studied. The mixing ratio of the concrete was 1 : 1.78 : 5.35 : 4.73 (water : content : ballast : sand). The studied chloride content was in the range of 0∼3.5 wt%. The corrosion potentials were measured in every week for two years. The copper-copper sulfate electrode (CSE) was employed as a reference electrode. After two years, the corroded structure was examined and compared to measured corrosion potential. Any visible difference was founded in the specimen located indoor and outdoor. The chloride concentration enhanced rusting and reinforced bar, shifting the potential to active range. The results showed good argument with Van daveer criteria. In 3.5 wt% chloride, the potential shifted belong -350 mV after 58week. Specimen in 1.75 wt% chloride, showed the potential between -200 mV∼-350 mV. However those in free chloride solution maintained above -200 mV for the studied period. It can the concluded that the chloride enhanced corrosion of rebar in concrete and the electrochemical potential can be a promising corrosion monitoring technique.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.16 no.2
• /
• pp.40-48
• /
• 2012

Steel corrosion in concrete is a main cause of deterioration and early failure of concrete structures. A novel integration of electromagnetic heat induction and infrared (IR) thermography is proposed for nondestructive detection of steel corrosion in concrete, by taking advantage of the difference in thermal characteristics of corroded and non-corroded steel. This paper focuses on experimental investigation of the concept. An inductive heater is developed to remotely heat the embedded steel from concrete surface, which is integrated with an IR camera. Concrete samples with different cover depths are prepared. Each sample is embedded with a single rebar in the middle, resulting an identical cover depth from the front and the back surfaces, which enable heat induction from one surface and IR imaging from the other simultaneously. The impressed current (IC) method is adopted to induce accelerated corrosion on the rebar. IR video images are recorded during the entire heating and cooling periods. The test results demonstrate a clear difference in thermal characteristics between corroded and non-corroded samples. The corroded sample shows higher rates of heating and cooling than those of the non-corroded sample. This study demonstrates a potential for nondestructive detection of rebar corrosion in concrete.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1996.11b
• /
• pp.533-538
• /
• 1996

40$0^{\circ}C$ $H_2O$, D$_2$O 및 $O_2$ 분위기에서 Zr-2.5wt% Nb 합금의 부식거동을 비교.분석하였다. Zr-2.5wt% Nb 합금은 열처리에 따른 조직에 따라 각각의 부식매질에 대해 부식거동이 큰 차이를 보이고 있으나, 형성된 oxide는 열처리 및 부식매질에 관계없이 monoclinic ZrO$_2$ 만이 관찰되었다. 급냉조직인 martensitic $\alpha$'-Zr 상과 소둔처리 조직의 준안정상인 $\beta$-Zr 상의 경우. 부식분위기에 매우 민감하여, D$_2$O, H $_2$O, $O_2$ 순으로 큰 부식속도를 보였다. 반면, 안전성들인 $\alpha$-Zr과 $\beta$-Nb 상의 경우, 부식 분위기에 따른 별다른 부식거동 차이를 보이지 않았다. 이들 실험 결과를 바탕으로 월성형 원자로 압력관의 부식특성을 분석하였다.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.1031-1037
• /
• 1998

To investigate the effect of cooling rate and annealing temperature on the corrosion of Zircaloy-4 and Zr-2. 5Nb alloys, autoclave corrosion tests were performed at $500^{\circ}C$ for the specimens prepared by various heat treatments. The specimens were heat-treated at $1050^{\circ}C$ for 30 minutes and cooled by ice-brine quenching, water quenching, oil quenching, air cooling, and furnace cooling. To investigate the effect of annealing temperature, the specimens were annealed at $\alpha$, ($\alpha$+$\beta$)-, and $\beta$-temperatures. It was observed from the $500^{\circ}C$ corrosion test that nodular corrosion occurred on the Zircaloy-4 alloy but did not occur on the Zr-2.5Nb alloy. The corrosion resistance of Zircaloy-4 increased with increasing the cooling rate. On the other hand, the corrosion resistance of Zr-2.5Nb decreased with increasing the cooling rate and the annealing temperature. It is suggested that corrosion resistance of Zircaloy-4 would be controlled by the distribution of Fe and Cr element in the matrix and precipitates, while that of Zr-2.5Nb alloy the niobium concentration and $\beta_{-Nb}$ phase.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2004.06a
• /
• pp.223-224
• /
• 2004

고준위폐기물 혹은 사용후 핵연료의 처분용기 재질은 각 국의 처분개념과 처분공의 주위 환경에 따라 달라질 수 있다. 용기의 후보재질로는 탄소강, 스텐레스 강, 구리, 니켈, 티탄 혹은 이들의 합금이 주로 고려되고 있으나, 국내에서는 아직 선정되지 않았다. 국내 처분환경에서 이들 재질의 부식특성을 조사하고자 모의 화강암 지하수를 가해 만든 겔 상태의 경주 벤토나이트에 탄소강, 스텐레스 강, 구리 시편을 넣고, $70^{\circ}C$, 아르곤 분위기에서 530일 경과한 후 시편의 표면 변화 (그림 1) 및 무게 감소를 측정하였다. 철 부식시편은 검정색의 철 화합물 층으로 덮여 있었으며, 구리표면에는 노란색의 부식층이 형성되었는데, 이를 XRD로 분석한 결과 $Cu_2O$로 판명되었다. 그러나 $700^{\circ}C$에서 각각 0, 24, 96시간동안 예민화시킨 스텐레스 강 시편들은 모두 초기상태 그대로 광택을 유지하고 있었으며, XRD에서 다른 화합물의 형성을 발견할 수 없었다 (그림 2). 시편의 무게 감소가 균일부식에 기인한 것으로 가정하여 환산한 결과, 구리와 스텐레스 강 모두 0.3~0.4 $\mu\textrm{m}/yr$의 부식속도를 나타내었다. 그러나 구리는 부식생성물이 표면에 부착되어 있기 때문에 실제 부식두께는 이 값보다 더 클 것으로 생각된다. 용기가 초기 530일간과 같은 속도로 처분용기의 부식이 진행된다면 한국에서 기준처분 개념으로 삼고 있는 50mm 두께의 내부식성 외벽 금속용기는 적어도 만년이상 견딜 수 있을 것으로 추정된다. 한편, 검정색 부식층을 제거한 무게감소로부터 계산한 철의 부식속도는 구리의 약 30배에 해당하였다. 금속 재질의 정확한 부식 거동을 파악하기 위해서는 보다 장기간의 실험이 요구된다. 시험법 선정에 각계(규제기관, 학계, 발전소 현장 및 산업계 등) 전문가로부터 기술자문회의를 통하여 자문 의견을 받기로 하였다. 특히 현재 폐기물 인수 기술기준치가 설정된 국가의 시험법을 심층 있게 검토하기로 하였다.검토하기로 하였다. 혹은 수성주변 환경이 지배하는 산악이나 구릉지에서 흔히 나타나는 침엽수-낙엽활엽수의 혼합림 식생상태를 잘 대변해 주고 있는 것으로 판단된다. 끝으로, 의림지 호저 퇴적층 중에서 인위적인 교란흔적이 없는 암회색 유기질 니층에 대한 탄소연대측정 결과, 제1호공 12번 시료에서 950$\pm$40 years B.P을 얻었으며, 제3-1호공에서도 아래로 내려가면서 8, 10, 11번 시료에 대하여 500$\pm$30 years B.P, 650$\pm$30 years B.P, 800$\pm$40 years B.P의 연대측정 결과를 획득하였다. 이상과 같은 의림지 호저 퇴적층의 형성환경과 형성시기 연구를 통하여 의림지의 제방축조의 최초시기를 해석해 보면, 의림지의 제방은 적어도 과거 약 827년 전에서 866년 전에는 이미 축조되어 있었음을 알 수 있다. 과거 제천 일대에 살았던 옛사람들이 의림지 하류의 곡지중앙과 고기 충적선상지에 대한 관계용 용수조달의 필요성에 부응하여 상류부 곡지하천의 자연입지 환경을 최대한 이용하여 축조한 것으로 판단된다..준비하였다.전류를 구성하는 주요 입자의 에너지 영역(75~l13keV)에서 가장 높은(0.80) 상관계수를 기록했다. 넷째, 회복기 중에 일어나는 입자들의 유입은 자기폭풍의 지속시간을 연장시키는 경향을 보이며 큰 자기폭풍일수록 현저했다. 주상에서 관측된 이러한 특성은 서브스톰 확장기 활동이 자기폭풍의 발달과 밀접한 관계가 있음을 시사한다.se that were all low

• Journal of Energy Engineering
• /
• v.10 no.2
• /
• pp.132-139
• /
• 2001

석탄가스화 복합발전의 집진 공정에 사용하기 위한 금속제 safety filter의 재질 선정을 위하여 황화수소 가스 분위기에서 합금강의 부식 특성을 규명하였다. 사용 합금강은 SUS 310, SUS 316, Inconel 600과 Hastelloy X이다. 전기로 내에 설치된 지름 50mm의 qualtz 튜브 반응기에서 부식실험이 행하여졌다. 40$0^{\circ}C$부터 $700^{\circ}C$까지의 등은 조건에서 실험이 행하여졌고, 분위기 가스의 영향을 보기 위하여 H$_2$S 가스를 함유한 $N_2$(dry), $N_2$(saturation), $CO_2$(dry), 그리고 석탄가스 분위기에서 실험하였다. 부식 생성물을 파악하기 위하여 X-ray 회절기와 주사전자현미경 분석이 함께 이루어졌다. 1.7% H$_2$S, $600^{\circ}C$ 이하 온도 조건에서는 니켈계 내식강 중 Hastelloy X와 철계 내식강 중 SUS 310 등 고크롬 합금강이 IGCC 용 필터 소재 금속으로서 높은 내부식성을 나타내었다. 0.3%~4.99% 황화수소 농도 범위에서 황화수소 농도 변화에 따라서 SUS 310의 경우 3~237mg/d$m^2$.day, Inconel 600의 경우 4~660mg/d$m^2$.day로 부식속도는 크게 증가되었다. 50$0^{\circ}C$, 석탄가스 분위기에서 부식속도는 SUS 310은 45mg/d$m^2$.day, SUS 316은 110mg/d$m^2$.day, Inconel 600은 576mg/d$m^2$.day, 그리고 Hastelloy X 는 140mg/d$m^2$.day로서 합금강 시편 중 SUS 310 합금강이 가장 우수한 내식성을 나타내었다. 부식 표면에는 황화니켈, 황화철 피막이 형성되었다.