• Journal of the Korean Institute of Gas
• /
• v.12 no.4
• /
• pp.52-57
• /
• 2008

This paper studies on the wear corrosion behavior of induction hardening high strength cast iron in the acidic environments. In a variety of pH solutions, wear corrosion behavior of GC 300 with a variety of contact pressures was investigated, and corrosion wear behavior after immersion test was considered. Also, electrochemical polarization test for GC 300 was carried out in various pH solutions. The main results are as following: In the strong acidic environment, wear corrosion rate of GC 300 appears highly and in the neutral environment is stable. Also, graphitic corrosion in the strong acidic environment occurs. The corrosion current density of GC 300 becomes high in a order of pH 1 > pH 2 > pH 4 > pH 6.5.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.6
• /
• pp.1404-1411
• /
• 1993

This study was undertaken to investigate the corrosive wear charateristics upon various transformation condition of austempered low-alloy ductile cast iron in corrosive environments against mating specimen made of the hardened SM45C. The corrosive wear test was carried out by rubbing the annular surface of two test pieces in distilled water and aqueous solution at constant sliding speed of 0.5m/s. In severe wear region, the corrosive wear rate Wc increased hastily with NaCl concentration owing to intermetallic adhesion but Wc went down slowly in mild wear region due to lubricating effect of the corrosion product. The critical sliding distance decreased with increasing NaCl concentration due to increased generation rate of the corrosion product and the specific corrosive wear rate has maximum in 1% NaCl aqueous solution at mild wear region. With the variation of matrix, the corrosive wear resistance of the fine acicular bainite was higher than that of coarse upper bainite because of reducing the local cell reaction by carbides. A growth in volume fraction of retained austenite in matrix increased the Wc due to soften surface, but has a declining tendency of Wc in mild wear region.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.14 no.2
• /
• pp.399-406
• /
• 1990

This paper is studied to know corrosive wear mechanism of STS304 steel on atmospherical temperature against mating material as the same. The corrosive test was carried out by rubbing the annular surface of two test pieces in distilled water and NaCl aqueous solution. The corrosive wear mechanism was investigated by S.E.M. The experimental results show that there is one Lcr transferring from severe wear to mild wear on change of NaCl concentration and atmospherical temperature, and which is the other still remaining in server wear state. It was found that the critical sliding distance Lcr shorten with increasing NaCl concentration but it is longer with ascending atmospherical temperature and the mild wear state still continues under the condition of high generation rate and elimination rate of the corrosive product. Considering upon the result, the model of corrosive wear mechanism is proposed.