• 대한기계학회논문집
• /
• 제17권8호
• /
• pp.2033-2042
• /
• 1993

In conventional SCC susceptibility test, there are constant strain test, constant load test, slow strain rate test(SSRT) and K$_{ISCC}$ test. Among them, the SSRT method is much more aggressive in producing SCC than the other tests, so that the test time of it is considerably reduced. But this SSRT method has mostly been worked using the uniaxial tensile specimen untill now. Therefore, the SSRT method using the tensile specimen(Ten-SSRT) has much difficulty in SCC susceptibility evaluation of a localized region like weldment and the advantage material of high order. Recentely, the small punch(SP) test method using miniaturized small specimen is the very effective test method for fracture strength evaluation of a localized region like weldment and fusion reactor wall irradiated in the nuclear power plant. This paper investigated the possibility of SCC susceptibility evaluation by the SP-SSRT method using the miniaturized small specimen. Therefore, we obtained the result that the SP-SSRT had the possibility for the evaluations of SCC susceptibility for shorter time to corrosive environment compare to Ten-SSRT which was conventional method.

• Journal of Advanced Marine Engineering and Technology
• /
• 제26권1호
• /
• pp.125-131
• /
• 2002

This paper was studied on the effect of temperature on corrosion of absorption refrigeration systems using $LiBr-H_2O$ working fluids. In the fresh water and 62 % lithium bromide solution at $70^{\circ}C$, polarization test of SS 400, Cu(C1220T-OL) and Al-Ni bronze was carried out. And polarization behavior, polarization resistance characteristics, corrosion rate(mmpy) and corrosion sensitivity of materials forming absorption refrigeration systems was considered. The main results are as following: (1) As the experimental temperature increase, the change of corrosion rate of Al-Ni bronze become duller than SS 400 and Cu in 62% lithium bromide solution. (2) According as corrosion environment is changed from fresh water to 62% lithium bromide solution, potential change of Cu and Al-Ni bronze become less noble than SS 400. (3) The corrosion sensitivity of Al-Ni bronze was duller than that of Cu and SS 400 in 62% LiBr solution.

• 수산해양기술연구
• /
• 제27권2호
• /
• pp.132-140
• /
• 1991

오스테나이트계 스테인레스강 SUS316, SUS321 보다 용접성, 내식성 및 극저온인성이 양호하며 기존의 재료보다 고가 첨가 원소인 크롬과 니켈의 함유량을 절감한 새로운 강종의 개발을 목표로 연구를 수행한 결과, 다음과 같은 결론을 얻었다. 1) Trans-Varestraint 시험에 의하여 용해 제조강과 수입개의 고온 균열 감수성을 비교 평가한 결과, SUS321 수입재와 SuS321에 대응하여 개발한 강종 사이의 응고 균열 감수성이 거의 동등 내지는 용해 제조강의 고온 균열 저항력이 우수하였다. 따라서 Creq/Nieq의 값 1.43~1.48의 범위에서 합금 설계한 강종 M-1~M-9의 고온 균열 저항력은 기존의 문헌에 의한 테이타와 비교한 결과, 우수함을 알 수 있었다. 2) 샤르피(Charpy V notch) 표준 시험편에 의한 극저온 및 상온에서의 인성을 조사한 결과, 용해 제조강 M-1~M-9의 인성은 양호하였으며 특히 SUS321 수입재와 SUS321 대체재로서 개발한 M-7~M-9의 인성은 수입재의 그것보다 훨씬 높은 값을 나타내었다. 3) JIS G 0574에 의한 입계 부식 감수성을 조사한 결과, 입계 부식 감수성을 낮추기 위해서는 티타늄의 첨가가 매우 유효함을 알 수 있었다. 특히 SUS321 수입재와 SUS321 대응 강종(M-7~M-9)의 내식성은 수입재보다 개발 강종의 내식성이 훨씬 우수하였다. 4) 이상의 고온 균열 감수성과 극저온 및 상온에서의 인성, 내식성을 종합적으로 검토한 결과, 스테인리스강의 고가 첨가 원소인 크롬과 니켈의 첨가량을 절감할 수 있었다. 상기와 같은 관점에서 본 연구 수행에 의하여 새로운 합금 설계 개념에 의거, 새로운 강종의 개발과 생산 원가의 절감 그리고 제품의 품질 향상에 기여할 수 있는 기준을 확립할 수 있었다.

• 한국마린엔지니어링학회:학술대회논문집
• /
• 한국마린엔지니어링학회 2001년도 추계학술대회 논문집(Proceeding of the KOSME 2001 Autumn Annual Meeting)
• /
• pp.92-97
• /
• 2001

This paper was studied on the effect of temperature on corrosion of absorption refrigeration systems using LiBr-$H_2O$ working fluids. In the fresh water and 62 %lithium bromide solution at $70^{\circ}C$, polarization test of SS 400, Cu(Cl220T-OL) and Ni-Al bronze was carried out. And Polarization behavior, polarization resistance characteristics, corrosion rate(mmpy) and corrosion sensitivity of materials forming absorption refrigeration systems was considered. The main results are as following: As the experimental temperature increase, the change of corrosion rate of Ni-Al bronze become duller than SS 400 and Cu in 62 % lithium bromide solution. Open circuit potential of SS 400 is less noble than that of Cu and Ni-Al bronze in fresh water, but that becomes noble than Cu and Ni-Al bronze in 62 % lithium bromide solution. The corrosion sensitivity of Ni-Al bronze was controlled than that of Cu and SS 400 in 62% LiBr solution.

• 한국해양공학회지
• /
• 제2권2호
• /
• pp.122-129
• /
• 1988

Recently with the rapid development in marine and shipbuliding industries such as marine structures, ship and chemical plants, there occurs much interest in the study of corrosion fatigue characteristics which was closed up an important role in mechanical design. In this study, the 5086 Al-alloy was tested by use of rotary bending fatigue tester. The retardation effect of overload on the corrosion fatigue crack propagation in sea environment was quantitatively studied. 1) Retardation effect of corrosion fatigue crack propagation is most eminent when overload ratio is 1.52, overload magnitude corresponds to about 77% and 55% of yield strength and tensile strength respectively. 2) After overload ratio 1.52 was used, retardation of corrosion fatigue crack growth rate is largely retarded and quasi-threshold stress intensity factor range($\Delta\textrm{K}_{th}$) appears. 3) According to m of experimental constant, retardation effect of corrosion fatigue crack propagation corresponds to about 25% of constant stress amplitude when overload ratio is 1.52. 4) When overload ratio 1.52 was used, retardation parameter (RP) decreases to about 0.43 and corrosion sensitivity (S)decreses to about 2.1.

• Journal of Advanced Marine Engineering and Technology
• /
• 제25권2호
• /
• pp.409-409
• /
• 2001

해양구조물은 점점 대형화되어 가고 있는 추세에 있으며 또한 이들 구조물의 대형화에 따른 구조물의 보수, 유지관리가 매우 중요한 사안으로 등장하게 되었다. 뿐만 아니라, 이러한 구조물 등이 손상또는 파괴되었을 경우는 그에 따른 인적, 경제적 손실 또한 막대할 것으로 사료되며 이러한 구조물의 파괴사례중 상당 부분이 용접부의 부식문제 및 수소취화와 관련된 사고인것으로 보고되고 있다. 한편 용접은 급속가열, 급속냉각의 공적으로 인한 경도와 열적, 조직적 변화를 일으켜 용접부 각 미세부위별 전위차가 발생하게 되며, 이로 인해 갈바낙부실을 일으키는 것으로 보고 있다. 그리고 갈바닉 부식에 의한 용접부의 부식성을 억제하기 위해 용접후열처리(post weld heat treatment PWHT)를 시행하여 내식성을 향상시키는 경우도 있다. 본 연구에서는 고장력강인 RE36강 시험편을 전기화학적 측면에서 최적의 용접후열처리 온도를 규명하였으며, 용접방법(FCAW, SMAW), 용접후 열처리 유무에 따른 용접부위의 저변형을 인장실험을 통한 기계적 특성, 전기화학적 특성 및 수소취화 감수성을 등을 규명하였다. 따라서 본 연구 결과는 해양구조물 선박의 설계시공시에 용접부 주위의 기계적. 전기화학적 특성 평가 및 수소취화 방지대책에 좋은 참고자료가 될 것으로 기대된다.

• Journal of Advanced Marine Engineering and Technology
• /
• 제33권8호
• /
• pp.1162-1169
• /
• 2009

22APU 스테인리스강에 대해서 두가지의 용접법이 적용 되었으며, 그중 한 방법은 레이저 용접법이며 다른 하나는 TIG 용접법이다. 이 경우 상기한 두 용접을 적용할 경우 용접부의 부식특성의 차이점에 대해서 전기화학적인 방법 예를 들면 부식전위, 분극곡선 및 사이클릭볼타모그램 등의 측정에 의해서 고찰되어졌다. 레이저용접의 경우 모든 용접부(용접금속,열영향부, 모재부)의 경도가 TIG용접의 경우에 비해서 상대적으로 높은 값을 나타내었다. 더욱이 모든 용접부의 부식전류밀도 역시 TIG용접에 비해서 낮은 값이 관찰되었다. 특히 모재부의 부식전류밀도는 용접방법에 관계없이 가장 낮은 값을 나타내었다. 그리고 레이저용접의 경우 부식된 모든 용접부에서 입계부식이 관찰 되지 않았으나, TIG용접에서는 용접금속부와 열영향부에서 입계부식이 관찰되었는데 이것은 크롬카바이드의 형성에 의한 크롬결핍이 감수성온도영역에 있는 용접금속부와 열영향부에 나타났기 때문으로 사료된다. 따라서 이들 영역은 더욱 활성화된 양극으로 부식되기쉽다. 결과적으로 22APU 스테인리스강의 용접부의 내식성은 레이저용접에 의해서 확실히 개선될 수 있다는 사실을 알 수 있다.

• 한국재료학회지
• /
• 제3권4호
• /
• pp.361-371
• /
• 1993

응력부식균열(SCC) 감수성평가를 위한 여러 시험방법들중 저변형율시험방법은 비교적 \ulcorner은 시간내에 금속재료의 SCC감수성을 평가하기 위한 효과적인 시험방법이다. 그러나 저변형율 시험방법만으로 SCC과정의 미시적 파괴거동ㅇ르 분석하는 것은 매우 어렵다. 종래, 음향방출(AE)시험은 재료의 파괴과정시 미시균열의 개시 및 전파거동을 감시하는데 유효한 기법으로 잘 알려져 있다. 그러므로 본 논문에서는 저변형율시험과 음향방출시험을 이용하여 SCC의 전파과정과 AE신호 특성사이의 상호관계를 분석하였다. 실험결과, 재료의 미시파괴 과정에서 발생하는 AE신호들은 뚜렷히 시험환경에 의존하였으며, 인공해수중에서 SCC과정시 발생된 AE신호 특성은 Air상태 보다 상당히 크게 나타났다. 그리고 SCC거동은 AE신호의 진폭인자로서 명확하게 평가할 수 있다.

• 한국재료학회지
• /
• 제5권1호
• /
• pp.12-21
• /
• 1995

본 연구에서는 부식환경하에서 bulging 시험동안 음향방출거동에 미치는 변형률속도에 대한 영향을 알아보았다. 시험에 사용된 변형률속도의 범위는 $4 \times 10^{-6}S^{-1}$에서 $1 \times 10^{-4} \times S^{-1}$까지이며, AE신호 특성을 평가하기 위해 사용된 인자는 AE hit수와 진폭으로 하였다. 시험결과, 변형률속도가 감소함에 따라 등가파괴변형률과 원주방향의 균열 길이는 감소하였으나, 파괴과정동안 총 누적 AE hit수와 평균진폭은 크게 증가하였다. 그리고 AE신호 특성치의 최대점은 시험전분부에 접근하였으며, 단위 등가파괴변형률당 평균진폭이 20dB 이상에서는 뚜렷하게 응력부식륜열 현상을 관찰할 수 있었다. 또한 음향방출시험법은 변형률속도에 따른 재료의 응력부식균열 감수성 정도를 평가하는데 있어 그 적용 가능성이 있음을 알 수 있었다.

• Journal of Welding and Joining
• /
• 제11권3호
• /
• pp.61-74
• /
• 1993

The cause of corrosion failure found in structures or various components operating in severe corrosive environment has been attributed to stress corrosion cracking(SCC) which is resulting from the combined effects of corrosive environments and static tensile stress. Cathodic protection is an electrochemical method of corrosion control that is widely used in marine environment and primarily on carbon steel. A number of criteria are used to determine whether or not a structure is cathodically protected. In practice, -0.8V versus Ag/AgCl is the most commonly used for marine structures. This paper showed the combined effects of cathodic potential and slow, monotonic straining on the tensile ductility and fracture morphology of parents and friction welded joints for SM45C, SCM440 and SM20C steels in syntheic sea water(S.S.W.,pH:8.2). For the parent materials in cathodic potentials, the higher tensile strength is, the more susceptible SCC is. And the welded HAZ is more susceptible than the parent materials.