• Journal of the Korean Society for Nondestructive Testing
• /
• v.22 no.2
• /
• pp.155-169
• /
• 2002

The objective of this study was to investigate the effect of crack opening and closure in the AE activities during fatigue test. Laboratory experiment using various materials and test conditions were carried out to identify AE characteristics of fatigue crack propagation. Compact tension specimens of 2024-T4 and 6061-T6 aluminum alloy were prepared for fatigue test. AE activities were analyzed based on the phase of the loading cycle. Generally, most of AE were generated when the crack begins' opening and the crack closes fully, whereas a few in the pull opening of the crack. Also AE activity in the peak loading of cycle was different with each specimen. However, in the same material, AE activity was not affected by the change of cyclic frequency (0.1, 0.2, 1.0Hz). It was found that AE activities during crack opening and closure depend on material properties such as micro-structure, tensile strength and yield strength.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.6 no.2
• /
• pp.26-33
• /
• 1997

In this study effect of residual stress and its redistribution in weldment on the fatigue crack propagation was investigated. Fatigue tests were conducted by the center notched specimens machined with welded plate. The residual stress and its redistribution after the crack growth were measured by the magnetizing stress indicator and hole-drilling method. Fatigue crack propagation was estimated by the specimens having residual stress redistributed after the cracks growth and having the effects of crack closure. Crack growth rates were predicted and compared with experimental results. It had been found that the predicted crack propagation rates have a good agreement with experimental results when the redistribution of residual stress was considered.