The fabrication process of particulate metal matrix composites(PMMCs) with homogeneous distribution of reinforcement and reheating for thixoforming has been studied. Both of eletro-magnetic stirring and mechanical stirring were used to fabricate particulate metal matrix composites(PMMCs) for variation of particle size. The electrical and mechanical processing conditions for fabricating PMMCs are also suggested. For thixoforming of PMMCs, fabricated bi1lets are reheated by using the designed optimal coil with as function of length between PMMC billet and coil surface, and coil diameter and billet. The effect of reinforcement distribution according to variation of billet temperature were investigated with solid fraction theory with a function of matrix alloy and volume fraction of reinforcement.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2000.04a
• /
• pp.16-16
• /
• 2000

분무주조법으로 제조된 Al-25Si-(Fe,V) 합금빌렛의 미세조직을 광학현미경, 주사전자현미경, 투과전자현미경으로 분석하였으며, 빌렛내에서 관찰되는 2차상의 형성거동을 정확히 분석하기 위해 over-sprayed 분말의 미세조직을 분무주조 빌렛과 함께 관찰하였다. 먼저 분무주조 빌렛을 표면으로부터 중심부까지 관찰한 결과, 분무주조 빌렛의 미세조직은 표면부 10mm 가량을 제외하고는 매우 균일한 미세조직을 보여주었다. 이에 본 연구에서는 분무주조 빌렛의 표면부와 중심부, 그리고 over-sprayed 분말조직으로 구분하여 각각에서 관찰되는 2차상을 관찰하였으며, 이를 바탕으로 분무주조 빌렛내에 형성된 2차상의 형성기구를 규명하고자 하였다. Over-sprayed 분말의 미세조직은 기지조직내에 균일하게 분포된 침상의 $\delta$-AlFeSi 상과 각형의 Si 입자로 구성되어 있었다. 반면, 분무주조 빌렛의 경우, 그 중심부에서는 기자조직내에 균일하게 분포된 막대형의 $\beta$-AlFeSi과 부정형의 조대한 Si입자가 관찰되었으며, 표면부에서는 부정형의 Si 입자와 함께 막대형의 $\beta$-AlFeSi/$\delta$-AlFeSi 복합상이 관찰되었다. 특히, 빌렛 표면부의 $\beta$-AlFeSi 상과 $\delta$-AlFeSi 상간에는 일정한 방위관계가 존재하였으며, 이러한 결과는 분무주조 빌렛내에 분포된 $\beta$-AlFeSi상들이 분무액적내에 형성된 준안정 $\delta$-AlFeSi 상으로부터 상분해되어 형성되었음을 제시한다. 이상의 분무주조 조직과 over-sprayed 분말의 미세조직으로부터 분무주조 빌렛의 최종 주조조직은 반응고상태의 분무액적 조직에 의해 지배됨을 알 수 있다.r plate)의 단면 미세조직 사진으로써 모재부와 오버레이충을 함께 보여주고 있다. 모재와 오버레이 충간의 경계면은 모재 일부가 용융된 후 웅고하면서 형성됨으로 인해서 도금이나 용사층과는 달리 매우 견고하게 결합되어 있다. 따라서 계면부의 탈락이라는 문 제점은 거의 없어 심한 응력을 받는 기계구조물 및 부품에도 본 기술은 널리 적용되고 있다. 그리고 사진 1에서 알 수 있는 바와 같이 모재와는 전혀 상이한 재료를 자유로이 선택하여 표면 유효층 일부만 오버레이시키며I 주조 및 단조가 불가능한 재료까지도 표면부에 오버레이 시킴으로 서 부품 및 설비의 제조에 있어 재료비의 절감과 제품의 수명이 획기적으로 개선될 수 있다. 그리고 최근에는 도금 빛 용사 둥과 같은 표면처리를 할 경우임의 소재 표면에 도금 및 용 사에 용이한 재료를 오버레이용접시킨 후 표면처리를 함으로써 보다 고품질의 표면층을 얻기위한 시도가 이루어지고 있다. 따라서 국내, 외의 오버레이 용접기술의 적용현황 및 대표적인 적용사례, 오버레이 용접기술 및 용접재료의 개발현황 둥을 중심으로 살펴봄으로서 아직 국내에서는 널리 알려지지 않은 본 기 술의 활용을 넓이고자 한다. within minimum time from beginning of the shutdown.및 12.36%, $101{\sim}200$일의 경우 12.78% 및 12.44%, 201일 이상의 경우 13.17% 및 11.30%로 201일 이상의 유기의 경우에만 대조구와 삭제 구간에 유의적인(p<0.05) 차이를 나타내었다.는 담수(淡水)에서 10%o의 해수(海水)로 이주된지 14일(日) 이후에 신장(腎臟)에서 수축된 것으로 나타났다. 30%o의 해수(海水)에 적응(適應)된 틸라피아의 평균 신사구체(腎絲球體)의 면적은 담수(淡水)에 적응된 개체의 면적보다 유의성있게 나타났다. 해수(海水)에 적응(適應)된 틸라피아의 신단위(腎單位)의 사

• Korean Journal of Materials Research
• /
• v.4 no.8
• /
• pp.945-951
• /
• 1994

In order to elucidate the extrusion characteristics of $SiC_{p}$/6061 Al composite, defomation resistance, $K_{w}$ was determined using the empirical formula suggested by Watanabe et al, and also extrusion pressure was measured using the extrusion press with a capacity of 350 ton. The $K_{w}$ which are propotional to extrudability, was increased with increasing volume fraction of reinforcement, $SiC_{p}$, but decreased with increasing the particle size. The peaks of maximum extrusion pressure in curves of extrusion force vs ram stroke were changed sharply with decreasing the particle size. The elevated extrustion temperature resulted in the decreased $K_{w}$ and extrusion pressure, but caused the surface tearing of extrusion composite bars. The results showed that extrudability of the composite billets is depend on the extrusion conditions as well as the characteristics of reinforcement, $SiC_{p}$.

• Journal of the Korean Society for Precision Engineering
• /
• v.18 no.6
• /
• pp.166-173
• /
• 2001

Composite materials consists of two or more different material layers. The usefulness of clad metal rods forms the possibilities of combination of properties of different metals. Copper clad aluminum composite materials are being used for economic and structural purpose. In this study, composite billet consists of commercially pure copper and aluminum(A6061) and experimental conditions consist of the combinations of clad thickness, extrusion ratio, and semi-cone angle of die. In order to investigate the influence of these parameters on the hot direct extrudability of the copper clad aluminum composite material rods, the experimental study have been performed with various extrusion temperatures, extrusion ratios, semi-cone angles of die, and composition rate of Cu:Al.

• Korean Journal of Materials Research
• /
• v.5 no.8
• /
• pp.953-959
• /
• 1995

It was investigated that reinforced species, billet condition and extrusion variation in Al 6061 composite material effected on extrusion process of particulate reinforced composite material. The strength of composite material with reinforcement species revealed SiC$\sub$w/> A1$_2$O$\sub$3f/ > A1$_2$O$\sub$3f/ > A1$_2$O$\sub$3f/ orderly. K$\sub$w/ increased as volute fraction increased in all composite material. The composite materials reinforced by A1$_2$ $O_3$required the larger pressure in hot extrusion process than those by SiC$\sub$p/ at all condition. Extrusion process tended to decrease as the semi-angle of extrusion dies increased because larger contact area caused larger shear friction. Extrusion temperature went up about 50$^{\circ}C$ in low elevated deformation temperature. In extrusion temperature above 500$^{\circ}C$, severe tearing occurred on extrusion surface. More reinforcement in volume fraction, more hot tearing.