• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.10
• /
• pp.688-695
• /
• 2017

Compared to metal, CFRP has excellent mechanical characteristics in terms of intensity, hardness, and heat resistance as well as its light weight that it is used widely in various fields. Therefore, this material has been used recently in the aerospace field. On the other hand, the material has shortcomings in terms of its extreme vulnerability to damage occurring internally from an external impact. This study examined the intensity up to its destruction from repeated use with the internal impact of a CFRP laminated plate that had also been exposed to external impact obtain design data for the external plate of aircraft used in the aerospace field. For the experimental method, regarding the quasi-isotopic type CFRP specimen and orthotropic CFRP specimen that are produced with a different layer structure, steel spheres with a diameter of 5 mm were collided to observe the resulting impact damage. Through a 3-point flexural fatigue experiment, the progress of internal layer separation and impact damage was observed. Measurements of the flexural fatigue strength after the flexural fatigue experiment until internal damage occurs and the surface impacted by the steel spheres revealed the quasi-isotopic layer structure to have a higher intensity for both cases.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.34 no.2
• /
• pp.155-164
• /
• 2014

Carbon-fiber-reinforced plastic (CFRP) composites are increasingly being used in a variety of industry applications, such as aircraft, automobiles, and ships because of their high specific stiffness and high specific strength. Aircraft are exposed to high temperatures and high humidity for a long duration during flights. CFRP materials of the aircraft can absorb water, which could decrease the adhesion strength of these materials and cause their volumes to change with variation in internal stress. Therefore, it is necessary to estimate the characteristics of CFRP composites under actual conditions from the viewpoint of aircraft safety. In this study air-coupled ultrasonic testing (ACUT) was applied to the evaluation of water absorption properties of CFRP composites. CFRP specimens were fabricated and immersed in distilled water at $75^{\circ}C$ for 30, 60, and 120 days, after which their ultrasonic images were obtained by ACUT. The water absorption properties were determined by quantitatively analyzing the changes in ultrasonic signals. Further, shear strength was applied to the specimens to verify the changes in their mechanical properties for water absorption.

• Transactions of the Korean Society of Machine Tool Engineers
• /
• v.16 no.3
• /
• pp.125-132
• /
• 2007

The purpose of present paper is to investigate a fracture characteristics of the finite-width single-edge-notch(SEN) carbon fiber/epoxy reinforced plastics(CFRP) plates by using an acoustic emission(AE). Uni-directionally oriented 10 plies CFRPs specimen which had different notch length were prepared for monotonic tensile test. Matrix cracking appeared over whole testing process and fiber breaking appeared later on mainly Load distribution factor of the matrix confirmed that increased according as increases of plate width ratio. The amplitude distribution of AE signal from a specimens is an aid to the determination of the different fracture mechanism such as matrix cracking, disbonding, interfacial delamination, fiber pull-out, fiber breaking, and etc. In the result of AE amplitude distribution analysis, matrix cracking, fiber disbonding or interfacial delamination, and fiber pull-out or fiber breaking signal correspond to <65dB, <75dB, and <90dB respectively, Also, changes of the slope of cumulative AE energy represented crazing phenomena or degradation of materials.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.3
• /
• pp.258-265
• /
• 2014

By replacing the previous metal connector on the joints of timber structure, the GFRP reinforced laminated wooden pin was produced using a wooden material and Glass fiber reinforced plastic(GFRP) composite laminate. In addition, using the reinforced wooden pin, the tensile type shear strength test was conducted. Based on the result of the bending strength test of the reinforced laminated wooden pin according to the GFRP arrangement, a specimen(Type-A) with a single insertion of GFRP for each layer have shown the most favorable performance. Also, it was verified that densified specimen hot pressed for an hour at the temperature of $150^{\circ}C$ and with the oppression pressure $1.96N/mm^2$ have shown the improved performance of 1.57 times than the specimen without the densification. And in the bending strength test considering the load direction, edgewise have shown a higher performance of 3.51 times than the flatwise. A shear strength test was conducted using the Type-A reinforced laminated wooden pin which have shown a moderate performance on the test. Based on the test conducted by differentiating the type of the joint plate and the connector, compared to the specimen(Type-DS) applied with the drift pin and steel plate, the specimen( Type-WL) applied with the GFRP reinforced laminated wooden pin and GFRP reinforced wooden laminated plate have shown 1.12 times higher shear strength and also have shown an excellent toughness even after the maximum load.

• Composites Research
• /
• v.22 no.2
• /
• pp.7-13
• /
• 2009

With the wide application of fiber-reinforced composite material in aero-structures and mechanical parts, the design of composite joint have become a very important research area because they are often the weakest areas in composite structures. In this paper, the failure strengths of the hybrid composite joints which were composed of a combination of an adhesive joint and a mechanical joint were evaluated and predicted. The 10 hybrid joint specimens which have different w/d, e/d and adherend thickness were manufactured and tested. The damage zone theory and the failure area index method were used for the failure prediction of the adhesive joint and the mechanical joint, respectively and the hybrid joints were assumed to be failures if either of the two failure criteria was satisfied. From the results of experiments and analyses, the failure strengths of the hybrid joints could be predicted to within 25.5%.

• Journal of the Society of Naval Architects of Korea
• /
• v.29 no.4
• /
• pp.214-226
• /
• 1992

In this paper, the characteristics of fatigue crack growth in the spot welded joint of the same kinds of specimens($HS{\times}HS,\;GA{\times}GAB$) and different kinds of specimens($HS{\times}GA,\;HS{\times}GAB$) which consist of dual phase high strength steel(HS) and monogalvanized steel(GA) were examined with static tension tests and axial tension fatigue tests. Some of the important results are as follows : 1. The divergence of tensile strengths among the same and different kinds of spot welds under the same conditions is comparatively low regardless of the difference of stiffness. 2. At the low load bevel and long life legion, the fatigue crack is initiated near the nugget. However, in the high load level and short life region, it occurs a tittle far from the nugget. 3. It has shown a linear relation between maximum stress Intensity factor, Kmax and fatigue life, $N_f$ among each of the spot welds and has gathered in a narrow band on the log-log graph paper. $Kmax=H{\cdot}{N_f}^{P}$ where H and P are a material constant.

• Composites Research
• /
• v.31 no.3
• /
• pp.88-93
• /
• 2018

In this study, damaged composite laminates were repaired by a stepped patch repair method using halloysite nanotube(HNT) and milled carbon(MC) reinforced composite materials with different amount of the particles. And the mechanical and structural effects of the particles on the interface between the damaged and repair surfaces were analyzed. At this time, after exposing them to a harsh environment of high temperature and humidity for a long time, the recovery rate of the material properties relative to the material forming the damaged plate was compared. As a result, at $70^{\circ}C$ high temperature distilled water, the hygroscopicity of the HNT/GFRP composites was significantly different from that of the MC/GFRP composites. Especially, 0.5, 1 wt. % HNT was added, the moisture absorption rate was the lowest and this was the factor that contributed to the mechanical strength increase. On the other hand, MC showed a high hygroscopic resistance only with a small amount, and the strength was different according to the action direction of the load, and the addition amount was also different.

• Journal of the Korean Society of Safety
• /
• v.25 no.3
• /
• pp.34-39
• /
• 2010

Unidirectional Carbon Fiber Reinforced Plastics (CFRP) are advanced materials which combine the characteristics of the light weight, high stiffness and strength. For those reasons, the use of the unidirectional CFRP has increased in jet fighters, aerospace structures. However, unidirectional CFRP composites have a lot of problems, especially delamination, compared with traditional materials such as steels and aluminums, and so forth. Therefore, the interlaminar fracture toughness for a laminate CFRP composite is very important. In this study, The mode II interlaminar fracture toughness was measured by using center notched flexure(CNF) test specimen. The CNF specimens using unidirectional carbon prepreg were fabricated by a hot-press with the gage pressure and temperature controller. And three kinds of a/L ratio was applied to these specimens. Here, we discuss the relations of the crack growth and the mode II interlaminar fracture under the four point bending CNF test. From the results, we shows that mode II interlaminar was occurred when the more $a_0$/L ratio, the less load. And $G_{IIC}$ also were obtained as 5.33, 2.9 and $0.58kJ/m^2$ according to $a_0$/L ratio=0.2, 0.3 and 0.4.

• Composites Research
• /
• v.22 no.5
• /
• pp.15-23
• /
• 2009

The lubricant tribological characteristics of $Al_2O_3$ fiber and SiC particle hybrid metal matrix composites (MMCs) fabricated by squeeze casting method was investigated using a pin-on-disk wear tester. The wear tests of the MMCs were performed according to fiber/particle hybrid ratio in the planar-random (PR) and normal (N) orientations sliding against a counter steel disk at a fixed speed and $25\;kg_f$ loading under different sliding distances and temperatures. The test results showed that the wear behavior of MMCs varied with fiber orientation and hybrid ratio. At room temperature, the lubricant wear behavior of F20P0 unhybrid PR-MMCs was superior to that of N-MMCs while the hybrid composites exhibited the reverse lubricant wear behavior. It was also revealed that the wear resistance of PR-MMCs was superior to that of the N-MMCs due to the joint action of reinforcements and lubricant film between the friction surfaces at an elevated temperature of $100^{\circ}C$ for both fiber only and hybrid cases. In case of $150^{\circ}C$, although the trend of weight loss was similar to that of others, the wear resistance of PR-MMCs was better than that of N-MMCs for hybrid MMCs.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.3
• /
• pp.234-246
• /
• 2013

It was found that test piece heated rapidly by 3 kW microwave for 5 minutes satisfies the targeted temperature and the percentage of moisture content, and the highest rate of weight increase is obtained in case of 120 minute immersion in the mixture of phosphates and heterocyclic compounds, from the result of such analysis as: kiln drying schedule, flame retardent by flammability test, insect resistance by termites, and permeability of combined penetrant for the wood after assigning multifunctional finish by immersing conifer structural frame, which is used for the frame work of wooden house and indoor/outdoor finishing in flame retardant and insect repellent materials mixture with the remaining heat of microwave. In addition, after a test of flame retardent treated item, it was identified that every mixture of phosphates corresponds with the standards of flame retardent, and upon investigation of moritality of 7 days after putting termites, it was showed that test piece immersed in the mixture of phosphates and heterocyclic compounds has the best characteristics, showing over 96% of high moritality. From the analysis of inward permeability of combined penetrant for the wood, it was decided that excellent performance in the flame retardent and insect resistance of the wood revealed due to full penetration of combined penetrant as it was found that combined penetrant penetrated through the whole inner cells of the wood.