• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.313-320
• /
• 2010

Objectives: The aim of this study was to examine changes in the dentinal fluid flow (DFF) during desensitizing agent application and to compare permeability after application among the agents. Materials and Methods: A Class 5 cavity was prepared to exposure cervical dentin on an extracted human premolar which was connected to a sub-nanoliter fluid flow measuring device (NFMD) under 20 cm water pressure. DFF was measured from before application of desensitizing agent (Seal&Protect, SP; SuperSeal, SS; BisBlock, BB; Gluma desensitizer, GL; Bi-Fluoride 12, BF) through application procedure to 5 min after application. Results: DFF rate after each desensitizing agent application was significantly reduced when compared to initial DFF rate before application (p < 0.05). SP showed a greater reduction in DFF rate than GL and BF did (p < 0.05). SS and BB showed a greater reduction in DFF rate than BF did (p < 0.05). Conclusions: Characteristic DFF aspect of each desensitizing agent was shown in NFMD during the application procedure.

• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.321-334
• /
• 2010

Objectives: The purpose of this study is to evaluate bonding efficacy by means of measuring the effect of remained solvent on Degree of conversion(DC) and ${\mu}TBS$ and FE-SEM examination. Materials and Methods: Two 2-step total etching adhesives and two single-step self etching adhesives were used in this study. First, volume weight loss of 4 dentin adhesives were measured using weighting machine in process of time in normal conditions and calculate degree of evaporation (DE). Reaction/reference intensity ratio were measured using micro-Raman spectroscopy and calculate DC according to DE. Then 2 experimental groups were prepared according to air-drying methods (under, over) and control group was prepared to manufacturer's instruction. Total 12 groups were evaluated by means of micro tensile bond strength and FE-SEM examination. Results: Degree of evaporation (DE) was increased as time elapsed but different features were observed according to the kind of solvents. Acetone based adhesive showed higher DE than ethanol and butanol based adhesive. Degree of conversion (DC) was increased according to DE except for $S^3$ bond. In ${\mu}TBS$ evaluation, bond strength was increased by additional air-drying. Large gaps and droplets were observed in acetone based adhesives by FE-SEM pictures. Conclusions: Additional air-drying is recommended for single-step self etching adhesive but careful consideration is required for 2-step total etching adhesive because of oxygen inhibition layer. Evaporation method is carefully chose and applied according to the solvent type.

• Restorative Dentistry and Endodontics
• /
• v.35 no.5
• /
• pp.374-379
• /
• 2010

Objectives: Nickel-titanium (Ni-Ti) rotary instruments have some unexpected disadvantages including the tendency to screw-in to the canal. The purpose of this study was to evaluate the influence of root canal curvatures on the screw-in effect of Ni-Ti rotary files. Materials and Methods: A total of 80 simulated root canals in clear resin blocks were used in the study. Canals with curvature of 0, 10, 20 and 30 degrees were instrumented with ProTaper instruments SX, S1, S2 and a ProFile of #25/0.06 to 1.0-2.0 mm beyond the initial point of root curvature. The screw-in force was measured with a specially designed device while canal was instrumented with a ProFile of #30/0.06 at a constant speed of 300 rpm. The data were subjected to one-way ANOVA and Scheffe multiple range test for post-hoc test. Results: Larger degree of canal curvature generated significantly lesser screw-in forces in all groups (p < 0.001). Conclusions: More attention needs to be paid when using rotary instruments in canals with less curvature than canals with more curvatures to prevent or reduce any accidental overinstrumentation.

• Restorative Dentistry and Endodontics
• /
• v.34 no.5
• /
• pp.415-423
• /
• 2009

The purpose of this study is to investigate the response of human pulp cell on Portland cement mixed with $\beta$-glycerophosphate. To investigate the effect of $\beta$-glycerophosphate and/or dexamethasone on human pulp cell, ALP activity on various concentration of $\beta$-glycerophosphate and dexamethasone was measured and mineral nodule of human pulp cell was stained with Alizarin red S. MTS assay and ALP activity of human pulp cell on Portland cement mixed with various concentration of $\beta$-glycerophosphate (10 mM, 100mM, 1M) was measured and the specimens were examined under SEM. Addition of $\beta$-glycerophosphate or dexamethasone alone had no effect however, the addition of 5 mM $\beta$-glycerophosphate and 100 nM dexamethasone had the largest increasement in ALP activity. There was no toxicity in all samples and the data showed that Portland cement mixed with 10 mM $\beta$-glycerophosphate had more increase in ALP activity compared with control. In conclusion, Portland cement mixed with $\beta$-glycerophosphate has no toxicity and promotes differentiation and mineralization of pulp cell compared with additive-free Portland cement. This implicated that application of Portland cement mixed with $\beta$-glycerophosphate might form more reparative dentin and in turn it would bring direct pulp capping to success.

• Restorative Dentistry and Endodontics
• /
• v.34 no.3
• /
• pp.199-207
• /
• 2009

The objective of this study was to evaluate the effect of color measuring instrument by measuring the color of dental composite resins. Nine shade light cured composite resin disks were prepared (diameter : 15 mm, thickness : 4 mm). CIE $L^*a^*b^*$ color scale of each disk was measured with 3 different types of spectrophotometer [MiniScan XE plus (Model 4000S, Hunter Lab, USA), CM-3500d (Minolta, Japan) and Specbos 2100 Miniature VIS Reflection spectrometer (Serial No: 319416, JETI Technishe VIS Instrumentic GmbH. Germany)]. Miniscan XE Plus and CM-3500d using identical measuring geometry with different size of viewing aperture. But Specbos 2100 using different measuring geometry. Within the limitation of this study, there were color difference (${\Delta}E^*$) from 2.4 to 7.8 between Miniscan XE Plus and CM-3500d, but $L^*$, $a^*$, $b^*$ values showed the high correlation. However, there were great color difference (${\Delta}E^*$) in the extent of about 20 between instruments with the different measuring geometry. Therefore, color scale measured by color measuring instrument should be used as a relative value rather than an absolute value in the field of dentistry.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.125-131
• /
• 2011

Objectives: The purpose of this study was to evaluate the effect of surface treatment of FRC-Post on bonding strength to resin cements. Materials and Methods: Pre-surface treated LuxaPost (DMG), Rely-X Fiber Post (3M ESPE) and self adhesive resin cement Rely-X Unicem (3M ESPE), conventional resin cement Rely-X ARC (3M ESPE), and Rely-X Ceramic Primer (3M ESPE) were used. After completing the surface treatments of the posts, posts and resin cement were placed in clear molds and photo-activation was performed. The specimens were sectioned perpendicular to the FRC-Post into 2 mm-thick segments, and push-out strength were measured. The results of bond strength value were statistically analyzed using independent samples t-test and oneway ANOVA with multiple comparisons using Scheffe's test. Results: Silanization of posts affect to the bond strength in LuxaPost, and did not affect in Rely-X Fiber Post. Rely-X ARC showed higher value than Rely-X Unicem. Conclusions: Silanization is needed to enhance the bond strength between LuxaPost and resin cements.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.108-113
• /
• 2011

Objectives: To determine the effect of the spectral output of single and dual-peak light emitting diode (LED) curing lights on the microhardness and color stability of commercial resin composites formulated with camphorquinone and alternative photoinitiators in combination. Materials and Methods: Three light-polymerized resin composites (Z100 (3M ESPE), Tetric Ceram (Ivoclar Vivadent) and Aelite LS Posterior (Bisco)) with different photoinitiator systems were used. The resin composites were packed into a Teflon mold (8 mm diameter and 2 mm thickness) on a cover glass. After packing the composites, they were light cured with single-peak and dual-peak LEDs. The Knoop microhardness (KHN) and color difference (${\Delta}E$) for 30 days were measured. The data was analyzed statistically using a student's t-test (p < 0.05). Results: All resin composites showed improved microhardness when a third-generation dual-peak LED light was used. The color stability was also higher for all resin composites with dual-peak LEDs. However, there was a significant difference only for Aelite LS Posterior. Conclusions: The dual-peak LEDs have a beneficial effect on the microhardness and color stability of resin composites formulated with a combination of camphorquinone and alternative photoinitiators.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.139-148
• /
• 2011

Objectives: This study investigated the effect of the strength and wetting characteristics of adhesives on the bond strength to dentin. The experimental adhesives containing various ratios of hydrophobic, low-viscosity Bis-M-GMA, with Bis-GMA and TEGDMA, were made and evaluated on the mechanical properties and bond strength to dentin. Materials and Methods: Five experimental adhesives formulated with various Bis-GMA/Bis-MGMA/TEGDMA ratios were evaluated on their viscosity, degree of conversion (DC), flexural strength (FS), and microtensile bond strength (MTBS). The bonded interfaces were evaluated with SEM and the solubility parameter was calculated to understand the wetting characteristics of the adhesives. Results: Although there were no significant differences in the DC between the experimental adhesives at 48 hr after curing (p > 0.05), the experimental adhesives that did not contain Bis-GMA exhibited a lower FS than did those containing Bis-GMA (p < 0.05). The experimental adhesives that had very little to no TEGDMA showed significantly lower MTBS than did those containing a higher content of TEGDMA (p < 0.05). The formers exhibited gaps at the interface between the adhesive layer and the hybrid layer. The solubility parameter of TEGDMA approximated those of the components of the primed dentin, rather than Bis-GMA and Bis-M-GMA. Conclusions: To achieve a good dentin bond, a strong base monomer, such as Bis-GMA, cannot be completely replaced by Bis-M-GMA for maintaining mechanical strength. For compatible copolymerization between the adhesive and the primed dentin as well as dense cross-linking of the adhesive layer, at least 30% fraction of TEGDMA is also needed.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.119-124
• /
• 2011

Objectives: The purpose of this experiment was to evaluate four different polishing systems of their polishability and polishing time. Materials and Methods: 4 mm diameter and 2 mm thickness Teflon mold was made. Z-250 (3M ESPE) hybrid composite resin was slightly overfilled and pressed with slide glass and cured with Optilux 501 for 40 sec each side. Then the surface roughness (glass pressed: control group) was measured with profilometer. One surface of the specimen was roughened by #320 grit sand paper and polished with one of the following polishing systems; Sof-Lex (3M ESPE), Jiffy (Ultradent), Enhance (Dentsply/Caulk), or Pogo (Dentsply/Caulk). The surface roughness and the total polishing time were measured. The results were analyzed with one-way ANOVA and Duncan's multiple range test. Results: The surface roughness was lowest in Pogo, and highest in Sof-Lex. Polishing times were shortest with Pogo, and followed by the Sof-Lex, Enhance and Jiffy. Conclusions: One-step polishing system (Pogo) is very effective to get the smooth surface in a short time, therefore it can be recommended for final polishing system of the restoration.

• Restorative Dentistry and Endodontics
• /
• v.36 no.2
• /
• pp.132-138
• /
• 2011

Objectives: The purpose of this study was to evaluate curing degree of three dual-cure resin cements with the elapsed time in self-cure and dual-cure mode by means of the repeated measure of micro-hardness. Materials and Methods: Two dual-cure self-adhesive resin cements studied were Maxcem Elite (Kerr), Rely-X Unicem (3M ESPE) and one conventional dual-cure resin cement was Rely-X ARC resin cement (3M ESPE). Twenty specimens for each cements were made in Teflon mould and divided equally by self-cure and dual-cure mode and left in dark, $36^{\circ}C$, 100% relative humidity conditional-micro-hardness was measured at 10 min, 30 min, 1 hr, 3 hr, 6 hr, 12 hr and 24 hr after baseline. The results of micro-hardness value were statistically analyzed using independent samples t-test and one-way ANOVA with multiple comparisons using Scheffe's test. Results: The micro-hardness values were increased with time in every test groups. Dual-cure mode obtained higher micro-hardness value than self-cure mode except after one hour of Maxcem. Self-cured Rely-X Unicem showed lowest value and dual-cured Rely-X Unicem showed highest value in every measuring time. Conclusions: Sufficient light curing to dual-cure resin cements should provided for achieve maximum curing.