• Korean Journal of Materials Research
• /
• v.6 no.8
• /
• pp.841-851
• /
• 1996

In a recent investigation, the formation of bainite phase in direct-quenched low carbon non heat-treated steel was reported. In this study the effects of bainite phase on the mechanical properties of direct-quenched microalloying steels were investigated. By isothermal transformation at $480^{\circ}C$ for 7 sec., volume fraction of bainite lath was 15~20%, and the UTS and impact energy were increased. In this case $B_{ll}$ and $B_{lll}$ type bainite was observed and the fractography of impact test specimen showed a ductile fracture tendency. Isothermal transformation for 100sec., yielded 30% volume fraction of granular bainite and the mechanical properties were decreased. The f ractography of impact test specimen showed a brittle fracture tendency. The addition of Mo was more effective than B for improving impact energy because amounts of boron aditions were restricted to considerably lower levels, typically 10~ 30ppm. From this study, it is predicted that 15~20% volume fraction of lath bainite on the direct quenching process is procduced by addition of Mo up to 1.2wt. % and controlling the finish forging proc¬ess at $1000^{\circ}C$ and using oil as direct quenching media. This will improve mechanical properties of the direct- quenched steel.

• Proceedings of the KWS Conference
• /
• 2010.05a
• /
• pp.19-19
• /
• 2010

Mo 변화에 따른 Cr-Mo 강의 미세조직 및 물성병화를 알아보기 위해 새로 디자인된 용접봉을 사용하여 Flux cored arc welding(FCAW) 공정으로 용접하였다. 또한 고온에서의 용접부 물성을 알아보기 위하여 각각의 시편을 $400^{\circ}C$, $500^{\circ}C$, $600^{\circ}C$, $700^{\circ}C$에서 24시간 동안 열처리 하였다. 용접부의 미세조직은 미세한 베이나이트 및 침상 페라이트로 구성되었으며 Mo의 함량이 높아질수록 베이나이트 조직이 증가하여 경도 및 강도가 증가하였다. 높은 항복강도와 인장강도를 가지며 연신율이 매우 낮음을 관찰하였다. 열처리후의 미세조직은 $400^{\circ}C$, $500^{\circ}C$는 템퍼드 베이나이트 조직이 나왔으나 $600^{\circ}C$에서 베이나이트 조직이 성장하였다. $700^{\circ}C$ 로 갈수록 베이나이트가 감소하고 페라이트로 미세조직이 변태 하였으며 탄화물의 석출 및 성장이 관찰되었다. 이로 인하여 경도값이 $400^{\circ}C$, $;500^{\circ}C$ 에서 증가하였고 $600^{\circ}C$는 소폭 감소하였으며 $700^{\circ}C$의 경우 완전 페라이트 조직의 형성으로 경도가 크게 감소하고 Mo 함량에 따른 경도 차이 또한 보이지 않았다.

• Korean Journal of Materials Research
• /
• v.1 no.3
• /
• pp.115-124
• /
• 1991

In this study, the relationship between mechanical properties and the effects of second phase in tri-phase steel which was composed of ferrite-martensite-bainite was investigated. In order to obtain different microstructure of ferrite+martensite(DP), ferrite+bainite(F+B), and ferrite+martensite+bainite(TP, different heat treatment has been accomplished. The effects of volume fraction and microstructure of each specimen were studied on tensile property, Charpy impact energy and stretch-flangeability. As the bainite content in triphase steels increased, the tensile strength, and yield strength decreased as well as the reduction of area and strength-uniform elongation increased. However, ferrite-bainite steel had high yield ratio and yield point elongation. The Charpy impact energy of TP and F+B steel was higher than that of DP steel. In addition, the characteristics of hole expanding limit($\lambda$) of TP steel and F+B steel were higher than that of DP steel. These mechanical properties of tri-phase steel have been improved, because bainite could be deformed easily within ferrite matrix. The effect of bainite on ductility in tri-phase steel has been found to be favorable. In this experiment, tri-phase steel contained within 27% bainite volume fraction had good nechanical properties and superior stretch-flangeability.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1996.05c
• /
• pp.182-187
• /
• 1996

원자로 압력용기강의 품질 열처리인 ？칭과 템퍼링 중간에 페라이트와 오스테나이트가 공존하는 2상영역에서 열처리를 행함으로써 인성을 향상시키는 제조공정을 개발하였다. 710~74$0^{\circ}C$에서 4~8시간 동안 2상영역 열처리를 추가하면 기존 열처리 과정에 비하여 상온 충격인성이 크게 증가하였다. 상온 충격인성과 두께를 고려하여 결정한 최적 조건안 7$25^{\circ}C$에서 6시간 동안 2상영역 열처리를 하면 최대 흡수 에너지가 30~50% 증가하고, 천이 온도가 약 l$0^{\circ}C$ 감소하였다. 2상영역에서 형성된 침상 오스테나이트는 냉각 중에 하부 베이나이트 또는 마르텐사이트로 변태하여 템퍼드 베이나이트와 복합조직을 이루므로 균열진전을 억제하여 충격인성이 향상되었다. 2상영역 열처리 온도가 높거나 시간이 길면 오스테나이트의 체적 분율이 증가하거나 조대화가 일어나 균열진전억제 효과는 저하되었다.

• Korean Journal of Materials Research
• /
• v.9 no.12
• /
• pp.1252-1262
• /
• 1999

The effect of microstructures on the strength-flangeability of Nb bearing hot-rolled high strength steel was investigated in order to improve the strength-flangeability of conventional TS 580MPa grades HSLA steel for the automotive wheel disc. The low temperature coiling method using 3-step controlled cooling pattern after hot rolling was effective to produce the Nb-bearing high strength steel with the polygonal ferrite and bainite duplex microstructures. It was suggested that the suppressed precipitation of grain boundary cementites and the decreased hardness difference between ferrite matrix and bainite cause the excellent stretch-flangeability of ferrite-bainite duplex microstructure steel. Therefore, the formation and propagation of microcracks were suppressed relative to the conventional HSLA steel with ferrite and pearlite microstructure. In addition, the elongation was improved as compared with that of hot-rolled steel sheets using conventional early cooling pattern because the volume fraction of polygonal ferrite was increased.

• Journal of Welding and Joining
• /
• v.10 no.1
• /
• pp.12-19
• /
• 1992

용접능률의 향상을 위한 대입열용접법의 적용은 과도한 입열량으로 인하여 용접부의 인성이 저 하한다는 점에서 그 적용에 주의를 요한다. 본 보에서는 대입열용접시 열영향부의 인성 저하의 원인과 그 대책을 강재의 측면에서 검토하였다. 고장력강을 용접하면 입열량이 증가함에 따라 오스테나이트 결정립이 조대화되고 상부 베이나이트와 도상 마르텐사이트가 생성되어 인성이 저하한다. 그 대책으로서는 용접 열싸이클과정중 안정한 질화물, 산화물등을 모재에 미세분산시켜 오스테나이트 결정립 성장을 억제하고, 페라이트, 펄라이트 변태를 촉진시킨다. 이러한 석출물의 형성을 위해서는 주로 Ti, Ca, REM, B등의 합금원소가 이용된다. 소입성이 높은 주질고장력 강에서는 석출물의 분산에 의한 페라이트의 변태 촉진 보다는 Mn, Ni, Cr, Mo, V등의 합금원 소를 첨가하여 소입성을 높여 인성이 우수한 하부 베이나이트 조직을 형성하든가, 탄소량을 저 감시켜 도상 마르텐사이트의 생성을 억제하므로서 인성을 확보한다. 현재 국내에서 제조되고 있는 대입열용접용강중 인장강도 50kgf/mm$^{2}$급강은 기본적으로 용접부 인성이 우수한 TMCP법으로 제조되며, Ti등을 첨가하여 석출물의 효과를 이용하고 N을 억제하여 기지의 인 성을 향상시키는 등의 방법을 병용하고 있다. 인장강도 60kgf/mm$^{2}$ 급강은 조질처리에 의하여 제조되며, 50kgf/mm$^{2}$급강과 같이 Ti, B등의 첨가에 의한 석출물의 효과를 이용 하고 있다.

• Journal of Korea Foundry Society
• /
• v.26 no.4
• /
• pp.180-183
• /
• 2006

The effects of adding Ni on microstructure and mechanical properties of Nodular Indefinite Chilled Iron (NICI) were studied. Thermal fatigue, hardness, tensile properties, wear resistance, are very important factors for NICI used for hot working roll and wire rod mill. The results show that addition 4% nickel has changed pearlite to bainite. Bainite matrix is superior to pearlite matrix on wear resistance, hardness and strength and will increase performance lifetime of NICI conventional roll material. Based in the bainitic microstructure, hardness and tensile property increase up to 48 HRc and $72\;kg/mm^2$, respectively.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.5
• /
• pp.252-261
• /
• 2017

This study examined the effect of heat treatment on the microstructure and mechanical properties of J55 line pipe steel. The experiments were carried out at under the following various conditions: austenization temperature($880^{\circ}C$, $910^{\circ}C$, $940^{\circ}C$), cooling methods(water quenching, oil quenching) and tempering temperature(none, $550^{\circ}C$, $650^{\circ}C$). The phase diagram and CCT curve were simulated based on the chemical composition of J55 steel to predict the microstructures. In the results, A1, A3 temperature decreased. As the austenization temperature increased, existing austenite grains grew exponentially which seriously degraded their mechanical properties. Various microstructures, including martensite, bainite, ferrite, and pearlite, developed in accordance with the heat treatments and were closely correlated with hardness, tensile strength and toughness. Martensite was formed after water quenching, but bainite and ferrite appeared after oil quenching. FeC precipitation formed and coarsened during tempering, which improved their toughness.

• Proceedings of the KWS Conference
• /
• 2004.05a
• /
• pp.194-196
• /
• 2004

최근 구조용 강재의 제조 및 적용에 있어 기계적 성질 제어의 필요성이 증가하고 있으며, 이는 공정 중의 미세조직 변화의 예측을 필요로 한다. 이에 상변태 현상에 대한 다양한 모델이 제안되고 있으며, 특히 등온 변태 모델과 비 등온 과정을 미소의 등온구간의 합으로 가정한 가산법칙의 적용을 기본으로 하고 있다. (중략)

• Transactions of the Korean Society of Automotive Engineers
• /
• v.8 no.4
• /
• pp.141-148
• /
• 2000

As the steel plates used for automobile safety the TRIP-assisted multiphase steels are being introduced to automobile industry with respect to their remarkable mechanical properties for the combination of high strength and large elongation. This multiphase structure is generated by two stage heat treatment (intercritical annealing & isothermal treatment) The metastable retained austenite can be transformed to martensite when plastically deformed which results in TRIP effect. Actually the microstructure of TRIP-assisted steels consist of a fine dispersite. There present discussion deals with bainite reaction kinetics of austenite in the process o f two stage heat treatment. In relation to bainite transformation the characteristics of bainite reaction is found to be influenced by the bainite tempering temperature and also by the relative rate in which carbides precipitate within residual austenite.