• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.8-14
• /
• 2016

A bulk-type Ta material is fabricated using the kinetic spray process and its microstructure and physical properties are investigated. Ta powder with an angular size in the range $9-37{\mu}m$ (purity 99.95%) is sprayed on a Cu plate to form a coating layer. As a result, ~7 mm-sized bulk-type high-density material capable of being used as a sputter material is fabricated. In order to assess the physical properties of the thick coating layer at different locations, the coating material is observed at three different locations (surface, center, and interface). Furthermore, a vacuum heat treatment is applied to the coating material to reduce the variation of physical properties at different locations of the coating material and improve the density. OM, Vickers hardness test, SEM, XRD, and EBSD are implemented for analyzing the microstructure and physical properties. The fabricated Ta coating material produces porosity of 0.11~0.12%, hardness of 311~327 Hv, and minor variations at different locations. In addition, a decrease in the porosity and hardness is observed at different locations upon heat treatment.

• Journal of the Korean institute of surface engineering
• /
• v.41 no.6
• /
• pp.301-307
• /
• 2008

In this paper, nanocrystallization of CuNiTiZr bulk metallic glass (BMG) subjecting to a kinetic spraying, dependent on impact velocity, was investigated by numerical and experimental approaches. The crystallization fraction and nucleation activation energy of initial feedstock and as-deposited coating were estimated by DSC and Kissinger method, respectively. The results of numerical modeling and experiment showed that the crystalline fraction and nucleation activation energy in BMG coatings were depended on kinetic energy of incident particle. Upon impact, the conversion of particle kinetic energy leads to not only decreasing free energy barrier but also increasing the driving force for an amorphous to crystalline phase transformation. The nanocrystallization of BMGs is associated with the strain energy delivered by a plastic deformation with a high strain rate.

• Korean Journal of Materials Research
• /
• v.33 no.7
• /
• pp.273-278
• /
• 2023

In this study, based on the saturation magnetic flux density experimental values (B_s) of 622 Fe-based bulk metallic glasses (BMGs), regression models were applied to predict B_s using artificial neural networks (ANN), and prediction performance was evaluated. Model performance evaluation was investigated by using the F1 score together with the coefficient of determination (R² score), which is mainly used in regression models. The coefficient of determination can be used as a performance indicator, since it shows the predicted results of the saturation magnetic flux density of full material datasets in a balanced way. However, the BMG alloy contains iron and requires a high saturation magnetic flux density to have excellent applicability as a soft magnetic material, and in this study F1 score was used as a performance indicator to better predict B_s above the threshold value of B_s (1.4 T). After obtaining two ANN models optimized for the R² and F1 score conditions, respectively, their prediction performance was compared for the test data. As a case study to evaluate the prediction performance, new Fe-based BMG datasets that were not included in the training and test datasets were predicted using the two ANN models. The results showed that the model with an excellent F1 score achieved a more accurate prediction for a material with a high saturation magnetic flux density.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.190-190
• /
• 2008

자연적으로 발생되는 파도, 비, 우박 등과 철도, 차량 및 엘리베이터 등과 같은 인위적인 설치, 이동에 의해 발생되는 진동에너지는 우리 일상생활에서 가장 흔하게 발생할 수 있는 에너지원인데, 이러한 진동에너지는 압전 소재를 이용하여 재생 가능하여 최근에는 이에 대한 연구가 활발히 진행되어 왔다. 예를 들면, 미국의 MIT에서는 인간이 걸을 때 신발에 가해지는 압력을 이용하여 전력을 발생시키는 연구를 진행하여 2.9 mW의 전력을 얻었다. 특히 이러한 기술은 인간의 걷기 운동 등과 같은 일상적인 동작으로 필요한 전력을 얻을 수 있고, 세라믹 소자를 이용하기 때문에 전자노이즈가 발생되지 않을 뿐 아니라 반영구적으로 사용할 수가 있어서, 소형 전자기기 등에 서 기존 이차전지를 대체 또는 보완 할 수 있는 기술로 검토되고 있다. PZT계 세라믹스는 높은 유전상수와 우수한 압전특성으로 이러한 압전발전 분야에서 가장 널리 사용되어지고 있다. 하지만 에너지 효율을 높이기 위하여 적층 구조의 제작 시 구조적 특성상 내부전극이 도포된 상태에서 동시 소결이 필요한데, $1000^{\circ}C$ 이상의 높은 소결온도 때문에 소재 원가가 낮은 Ag전극 대신 값비싼 Pd나 pt가 다량 함유된 Ag/Pd, Ag/Pt 전극이 사용되고 있어 경제성이 떨어지는 단점을 갖게 된다. 순수 Ag 전극을 사용하거나 Ag의 비율이 높은 내부전극을 사용하기 위해서는 $900^{\circ}C$ 이하에서 소결되고 우수한 전기적 특성을 보이는 압전 세라믹스 소재를 개발 하는 것이 필요하다. 따라서 본 연구에서는 압전특성이 우수한 $(Pb_{1-x}Cd_x)(Ni_{1/3}Nb_{2/3})_{0.25}(Zr_{0.35}/Ti_{0.4})O_3$ 계의 조성을 설계하고, 소결온도를 낮추기 위해서 2 단계 하소법을 이용하였다. 또한 $MnCO_3$, $SiO_2$, $Pb_3O_4$ 등을 소랑 첨가하여 액상 소걸 특성을 부여하여 소결 온도를 감소시키려는 시도도 하였다. 소결체의 전체적인 제조 공정은 일반적인 벌크 세라믹의 소걸 공정을 따랐다. 최종 소결된 시편을 XRD분석을 통하여 상을 확인하였고 SEM을 이용하여 미세조직을 관찰 하였다. 전기적 특성을 평가하기 위하여 두께를 1mm로 연마한 시편에 Ag 전극을 도포하여 $650^{\circ}C$ 에서 열처리한 후, 분극처리 하였다. Impedance analyzer를 이용하여 압전 특성 (전기기계결합계수 및 기계적품질계수)을 측정 하였고, 압전전하상수는 $d_{33}$-meter로 측정하였다. 본 연구에서는 압전체에 가해지는 하중의 크기, 시편의 크기, 하중을 가하는 방법, 에너지 저장회로의 최적화 등을 다양하게 시도하면서 에너지 변환 및 저장 효율을 평가하였다.

• New Physics: Sae Mulli
• /
• v.68 no.11
• /
• pp.1183-1191
• /
• 2018

The plasmon behaviors in a superlattice of $GaAs/Al_xGa_{1-x}As$ multiple quantum wells with a half-parabolic confining potential due to different dielectric interfaces are studied under magnetic and electric fields perpendicular and parallel to the superlattice axis by using a previously published theoretical framework. From the density-density correlation functions by considering the intrasubband and the inter-subband transitions under the random phase approximation, we calculate the dispersion energies of the surface and the bulk states as functions of the composition of the multiple quantum well structure and of the magnetic field strength and the average electric field strength over the quantum well. The Raman intensities for various magnetic field strengths and average electric field strengths over the quantum well are also obtained as a function of the energy of the incoming light for these states.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.34 no.1
• /
• pp.36-39
• /
• 2024

As interest in power semiconductors is growing recently, research on device design and application using light energy gap materials such as SiC and GaN is being actively conducted. Because AlN single crystals have a larger energy gap than the above mentioned materials, research on high-power devices is also in progress, but commercialized wafers have not yet been reported, so research is needed. In this study, we applied the HVPE (Hydride vapor phase epitaxy) method to produce AlN single crystals and attempted to obtain bulk single crystals using our own manufacturing equipment. To this end, we would like to report the results of securing the growth conditions for single crystals. we would like to report on the change in the shape of the grown crystal according to the change in temperature.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.03a
• /
• pp.94-94
• /
• 2003

최근, 새로운 전자재료로서 GaN 분말의 합성과 응용에 관한 연구가 많이 이루어지고 있다. CaN 분말은 열처리 과정 중 분해를 방지하기 위한 표면 보호용 소재, CaN 박막 또는 벌크 결정을 성장하기 위한 precursor 및 대면적 평판표시소자 제작을 위한 전기발광소자용 소재 등에 적용되고 있다. 일반적으로 100$0^{\circ}C$ 이상의 온도에서Ga과 NH$_3$를 반응시키거나, Ga이 포함된 화합물반도체 또는 산화물 및 질산염 등을 NH$_3$ 분위기에서 가열시켜 GaN 분말을 합성시키고 있다. 본 논문에서는 출발물질로서 GaOOH를 채택하고, 이를 NH$_3$ 가스를 흘리면서 가열 반응시켜 GaN 분말을 합성하고 X선 회절분석 방법을 사용하여 GaN의 합성에 대한 반응기구를 조사하였다. GaN 분말을 합성하기 위하여 GaOOH 분말 1g을 석영 용기에 담아 석영 반응관 내에 위치시키고, 반응관 내부를 $10^{-3}$ torr의 진공으로 배기한 후 $N_2$를 주입하면서 전기로의 온도를 1$0^{\circ}C$/min으로 승온시켰다. 반응온도는 300~l17$0^{\circ}C$의 범위에서 변화시켰고, 반응시간은 10분부터 24시간까지 변화시켰으며, NH$_3$의 유량은 300~700 sccm의 범위에서 변화시켰다. GaN의 반응역학을 조사하기 위하여 X선 회절도에서 특정 성분의 회절강도는 시료 내에 포함된 특정 성분의 량에 직접 비례한다고 가정하고, 2$\theta$=37$^{\circ}$부근에서 관찰되는 GaN의 (101)면에 의한 회절강도를 측정하고, 이를 GaN의 생성량으로 고려하였다.}C$로 소결 하였다. coating 결과 박리현상은 없었으나, 표면과 단면의 SEM분석결과 다소 porous한 박막층이 형성되었으며, Ca이온이 지지체로 permeation되는 현상이 발생하였다. 이와 같은 결과로부터 보다 치밀한 박막생성을 위해, slurry 제조조건을 변화시켰으며, Ca이온의 migration을 막기 위해 barrier layer를 이용하였다 완전 소결된 지지체는 가스투과도와 전기전도도측정을 통하여 특성을 평가하였다.였다.다.m이하의 NH$_3$ 가스를 검출할 수 있었다.기 화강암 관입 이전에 좌수향 전단 운동에 의해 부분적으로 재활성 되었으며, 후기 화강암의 관입 이후에 재차 우수향 전단운동으로 활성화 되었음을 알 수 있다. 이상의 결과를 종합하면 호남전단대는 쥬라기 중기에 발생한 광역적인 우수향의 연성전단운동이나, 운동 특성은 연속적이기 보다는 단속적으로 일어난 것으로 생각된다.리 폐 관류는 정맥주입 방법에 비해 고농도의 cisplatin 투여로 인한 다른 장기에서의 농도 증가 없이 폐 조직에 약 50배 정도의 고농도 cisplatin을 투여할 수 있었으며, 또한 분리 폐 관류 시 cisplatin에 의한 직접적 폐 독성은 발견되지 않았다이 낮았으나 통계학적 의의는 없었다[10.0%(4/40) : 8.2%(20/244), p>0.05]. 결론: 비디오흉강경술에서 재발을 낮추기 위해 수술시 폐야 전체를 관찰하여 존재하는 폐기포를 놓치지 않는 것이 중요하며, 폐기포를 확인하지 못한 경우와 이차성 자연기흉에 대해서는 흉막유착술에 더 세심한 주의가 필요하다는 것을 확인하였다. 비디오흉강경수술은 통증이 적고, 입원기간이 짧고, 사회로의 복귀가 빠르며, 고위험군에 적용할 수 있고, 무엇보다도 미용상의 이점이 크다는 면에서 자연기흉에 대해 유용한 치료방법임에는 틀림이 없으나 개흉술에 비

• Korean Chemical Engineering Research
• /
• v.48 no.3
• /
• pp.283-291
• /
• 2010

In this review, the studies on the electrochemical properties of $TiO_2$ nanotube as an anode material of lithium-ion battery, which was prepared by an alkaline hydrothermal reaction and anneling process, were investigated andanalyzed in terms of charge-dischage characteristics. Up to date, a maximum discharge capacity of $338mAh\;g^{-1}$(x=1.01) was achieved by the nanotube with $TiO_2(B)$ phase, whereas the theoretical capacity of $TiO_2$ anode was $335mAh\;g^{-1}$(x=1) in the basis of $Li_xTiO_2$ as a product of electrochemical reaction between $TiO_2$ and lithium. This was due to fast lithium transport by a shortened diffusion path provided by controlling the nanostructure of $TiO_2$, because the self-diffusion of lithium was slow in a basis of its activation energy as 0.48 eV. Due to an excellent ion storage capabilities in both the surface and the bulk phase, the $TiO_2$ nanotube could be a promising active material as both an anode of lithium-ion battery and an electrode of capacitor with high-rate performances.