• Journal of Sensor Science and Technology
• /
• v.11 no.5
• /
• pp.309-318
• /
• 2002

A stoichiometric mixture of evaporating materials for $CdIn_2S_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $CdIn_2S_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $630^{\circ}C$ and $420^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of $CdIn_2S_4$ single crystal thin films measured with Hall effect by van der Pauw method are $9.01{\times}10^{16}\;cm^{-3}$ and $219\;cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $CdIn_2S_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=2.7116\;eV-(7.74{\times}10^{-4}\;eV)T^2/(T+434)$. The crystal field and the spin-orbit splitting energies for the valence band of the $CdIn_2S_4$ have been estimated to be 0.1291 eV and 0.0248 eV, respectively, by means of the photocurrent spectra and the Hopfield quasi cubic model. These results indicate that the splitting of the ${\Delta}so$ definitely exists in the ${\Gamma}5$ states of the valence band of the $AgInS_2$/GaAs epilayer. The three photocurrent peaks observed at 10K areascribed to the $A_1$-, $B_1$-, and C1-exciton peaks for n = 1.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.4
• /
• pp.138-147
• /
• 2001

The stochiometric mixtures mixture of evaporating materials for the $ZnIn_{2}S_{4}$ single crystal thin film was prepared from horizontal furnace. To obtain the $ZnIn_{2}S_{4}$ single crystal thin film, $ZnIn_{2}S_{4}$ mixed crystal was deposited on throughly etched semi-insulting GaAs(100) in the Hot Wall Epitaxy(HWE) system. The sourceand substrate temperature were $610^{\circ}C$ and $450^{\circ}C$, respectively and the growth rate of the $ZnIn_{2}S_{4}$ single crystal thin film was about 0.5$\mu\textrm{m}$/hr. The crystalline structure of $ZnIn_{2}S_{4}$ single crystal thin film was investigated by photoluminescence and double crystal X-ray diffraction (DCXD) measurement. The carrier density and mobility of $ZnIn_{2}S_{4}$ single crystal thin film measured from Hal effect by van der Pauw method are $8.51{\times}10^{17}{\textrm}{cm}^{-3}$, 291$\textrm{cm}^2$/V.s at $293^{\circ}$K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $ZnIn_{2}S_{4}$ single crystal thin film, we have found that the values of spin orbit splitting $\Delta$So and the crystal filed splitting DCr were 0.0148eV and 0.1678 eV at $10^{\circ}$K, respectively. From the photoluminescence measurement of $ZnIn_{2}S_{4}$ single crystal thin film, we observed free excition($E_{X}$) typically observed only in high quality crystal and neutral donor bound exicton ($D^{\circ}$, X) having very strong peak intensity. The full width at half maximum and binding energy of neutral donor bound excition were 9meV and 26meV, respectively. The activation energy of impurity measured by Haynes rule was 130meV.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.6
• /
• pp.229-236
• /
• 2014

A stoichiometric mixture of evaporating materials for $MnAl_2S_4$ single crystal thin films was prepared from horizontal electric furnace. To obtain the single crystal thin films, $MnAl_2S_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperatures were $630^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The temperature dependence of the energy band gap of the $MnAl_2S_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=3.7920eV-5.2729{\times}10^{-4}eV/K)T^2/(T+786 K)$. In order to explore the applicability as a photoconductive cell, we measured the sensitivity (${\gamma}$), the ratio of photocurrent to dark current (pc/dc), maximum allowable power dissipation (MAPD) and response time. The results indicated that the photoconductive characteristic were the best for the samples annealed in S vapour compare with in Mn, Al, air and vacuum vapour. Then we obtained the sensitivity of 0.93, the value of pc/dc of $1.10{\times}10^7$, the MAPD of 316 mW, and the rise and decay time of 14.8 ms and 12.1 ms, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.3
• /
• pp.122-126
• /
• 2003

In this study, $Zn_{0.86}Mn_{0.14}$Te epilayer of 0.7 $\mu\textrm{m}$-thickness was grown on GaAs(100) substrate by using hot wallepitaxy. GaAs(100) substrate was removed from $Zn_{0.86}Mn_{0.14}$Teepilayer by the selective etching solution. The crystal structure and the lattice constant of only Z $n_{0.86}$ M $n_{0.14}$Te epilayer were investigated to be zincblende and 6.140 $\AA$ from X-ray diffraction pattern, respectively. Mn composition x of $Zn_{1-x}Mn_x$Te epilayer was found to be 0.14 using this lattice constant and Vegard's law. The crystal quality of the epilayer was confirmed to be very good due to 256 arcsec-full-width at half-maximum of the double crystal rocking curve. The absorption spectra from the transmission ones were obtained to measure the band gap energy of $Zn_{0.86}Mn_{0.14}$Te epilayer from 300 K to 10 K. With the decreasing temperature,. strong absorption regions in the absorption spectra were shifted to higher energy side and the absorption peak meaning the free exciton formation appeared near the absorption edge. The band gap energy values of $Zn_{0.86}Mn_{0.14}$Te epilayer at 0 K and 300 K were found to be almost 2.4947 eV and 2.330 eV from the temperature dependence of the free exciton peak position energy of $Zn_{0.86}Mn_{0.14}$Te epilayer, respectively. The free exciton peak position energy of $Zn_{0.86}Mn_{0.14}$Te epilayer without GaAs substrate was larger 15.4 meV than photoluminescence peak position energy at 10 K. This energy difference between two peaks was analysed to be Stokes shift.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.3
• /
• pp.189-198
• /
• 2000

The stochiometric mixture of evaporating materials for the $CuGaSe_2$single crystal thin films were prepared from horizontal furnace. Using extrapolation method of X-ray diffraction patterns for the polycrystal $CuGaSe_2$, it was found tetragonal structure whose lattice constant $a_0}$ and $c_0$ were 5.615 $\AA$ and 11.025 $\AA$, respectively. To obtains the single crystal thin films, $CuGaSe_2$mixed crystal was deposited on throughly etched GaAs(100) by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $610^{\circ}C$ and $450^{\circ}C$ respectively, and the growth rate of the single crystal thin films was about 0.5$\mu\textrm{m}$/h. The crystalline structure of single crystal thin films was investigated by the double crystal X-ray diffraction (DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility depending on temperature. From Hall data, the mobility was likely to be decreased by pizoelectric scattering in the temperature range 30 K to 150 K and by polar optical scattering in the temperature range 150 K to 293 K. The optical energy gaps were found to be 1.68 eV for CuGaSe$_2$sing1e crystal thin films at room temperature. The temperature dependence of the photocurrent peak energy is well explained by the Varshni equation then the constants in the Varshni equation are given by $\alpha$ = $9.615{\times}10^{-4}$eV/K, and $\beta$ = 335 K. From the photocurrent spectra by illumination of polarized light of the $CuGaSe_2$single crystal thin films. We have found that values of spin orbit coupling $\Delta$So and crystal field splitting $\Delta$Cr was 0.0900 eV and 0.2498 eV, respectively. From the PL spectra at 20 K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be 0.0626 eV and the dissipation energy of the acceptor-bound exciton and donor-bound exciton to be 0.0352 eV, 0.0932 eV, respectively.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.6
• /
• pp.425-433
• /
• 2000

The stochiometric mix of evaporating materials for the $CuGaTe_2$single crystal thin films was prepared from horizontal furnance. Using extrapolation method of X-ray diffraction patterns for the $CuGaTe_2$polycrystal, it was found tetragonal structure whose lattice constant $a_0 and c_0$ were 6.025 $\AA$ and 11.931 $\AA$, respectively. To obtain the single crystal thin films, $CuGaTe_2$mixed crystal was deposited on throughly etched semi-insulator GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were $670^{\circ}C$ and $410^{\circ}C$ respectively, and the thickness of the single crystal thin films is 2.1$\mu\textrm{m}$. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). Hall effect on this sample was measured by the method of van der Pauw and studied on carrier density and mobility dependence on temperature. The carrier density and mobility of $CuGaTe_2$single crystal thin films deduced from Hall data are $8.72{\times}10{23}$개 $\textrm m^3$, $3.42{\times}10^{-2}$ $\textrm m^2$/V.s at 293K, respectively. From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the $CuGaTe_2$single crystal thin film, we have found that the values of spin orbit coupling $\Delta$s.o and the crystal field splitting $\Delta$cr were 0.0791 eV and 0.2463 eV at 10 K, respectively. From the PL spectra at 10 K, the peaks corresponding to free bound excitons and D-A pair and a broad emission band due to SA is identified. The binding energy of the free excitons are determined to be 0.0470 eV and the dissipation energy of the donor-bound exciton and acceptor-bound exciton to be 0.0490 eV, 0.0558 eV, respectively.

• Journal of Sensor Science and Technology
• /
• v.6 no.4
• /
• pp.328-336
• /
• 1997

The CdSe thin films were grown on the Si(100) wafers by a hot wall epitaxy method (HWE). The source and substrate temperature are $600^{\circ}C$ and $430^{\circ}C$ respectively. The crystalline structure of epilayers was investigated by double crystal X-ray diffraction(DCXD). Hall effect on the sample was measured by the van der Pauw method and studied on the carrier density and mobility dependence on temperature. From Hall data, the mobility was increased in the temperature range 30K to 150K by impurity scattering and decreased in the temperature range 150k to 293k by the lattice scattering. In order to explore the applicability as a photoconductive cell, we measured the sensitivity(${\gamma}$), the ratio of photocurrent to darkcurrent(pc/dc), maximum allowable power dissipation(MAPD), spectral response and response time. The results indicated that the photoconductive characteristic were the best for the samples annealed in Cu vapor compare with in Cd, Se, air and vacuum vapour. Then we obtained the sensitivity of 0.99, the value of pc/dc of $1.39{\times}10^{7}$, the MAPD of 335mW, and the rise and decay time of 10ms and 9.5ms, respectively.