• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.20 no.1
• /
• pp.49-59
• /
• 1984

Optimizing investigation of characteristics of underwater welding by a gravity type arc welding process was experimentally carried out by using six types of domestic coated welding electrodes for welding of domestic marine structural steel plates (KR Grade A-1, SWS41A, SWS41B,) in order to develop the underwater welding techniques in practical use. Main results obtained are summarized as follows: 1. The absorption speed of the coating of domestic coated lime titania type welding-electrode became constant at about 60 minutes in water and it was about 0.18%/min during initial 8 minutes of absorption time. 2. Thus, the immediate welding electrode could be used in underwater welding for such a short time in comparison with the joint strength of in-atmosphere-and on-water-welding by dry-, wet-or immediate-welding-electrode. 3. By bead appearance and X-ray inspection, ilmenite, limetitania and high titanium oxide types of electrodes were found better for underwater-welding of 10 mm KR Grade A-1 steel plates, while proper welding angle, current and electrode diameter were 6$0^{\circ}C$, above 160A and 4mm respectively under 28cm/min of welding speed. 4. The weld metal tensile strength or proof stress of underwater-welded-joints has a quadratic relationship with the heat input, and the optimal heat input zone is about 13 to 15KJ/cm for 10mm SWS41A steel plates, resulting from consideration upon both joint efficiency of above-100% and recovery of impact strength and strain. Meanwhile, the optimal heat input zone resulting from tension-tension fatigue limit above the base metal's of SWS41A plates is 16 to 19KJ/cm. Reliability of all the empirical equations reveals 95% confidence level. 6. The microstructure of the underwater welds of SES41A welded in such a zone has no weld defects such as hydrogen brittleness with supreme high hardness, since the HAZ-bond boundary area adjacent to both surface and base metal has only Hv400 max with the microstructure of fine martensite, bainite, pearlite and small amount of ferrite.

• The Journal of Engineering Geology
• /
• v.14 no.4 s.41
• /
• pp.461-468
• /
• 2004

In order to characterize hydraulic property dependant on join roughness in rock mass, this study computed permeability coefficients on each range of joint roughness coefficient (JRC) suggested by Barton(1976). For a quantitative analysis of roughness components spectral analysis using the fast fourier transform was performed to select effective frequencies on each PC range. The results of spectral analyses show that low ranges of the JRC are mainly composed of low frequency domain, while high ranges of the JRC have dominant components at high frequency domain. The inverse Fourier transform made it possible to generate joint models of each JRC range using the effective frequencies of roughness spectrum. The homogenization analysis was applied to calculate permeability coefficient at homogeneous microscale, and then, computes a homogenized permeability coefficient (C-permeability coefficient) at macro scale. Therefore, it is possible to analyze accurate characteristics of permeability reflected with local effect of facture geometry. According to the calculation results, permeability coefficients were distributed between $10^{-3}m/sec\;and\;10^{-4}/sec$. In cases of sheared joint models permeability coefficients were plotted between $10^{-4}m/sec\;and\;10^{-5}/sec$, showing irregular distribution of permeability coefficients on each IRC range. The differences of permeability coefficients for the same aperture models or for the sheared joint models indicate that changes of roughness pattern influence on permeability coefficients. Therefore, the effect of joint roughness should be considered to characterize hydraulic properties in rock joints.